CNx thin films grown by PLD at different temperatures

Carbon Nitride (CNx) thin films were grown by pulsed laser deposition using a Nd:YAG laser (1064 nm, 500mJ), in a graphite target (99.999%) on Si(100) substrate for three different temperatures 21, 50 and 200 °C, in a nitrogen atmosphere at constant pressure of 2,66 Pa. The FTIR’s analysis made to t...

Full description

Autores:
Jorge Luis Gallego Cano; Universidad Tecnológica de Pereira, Colombia
Deisy Ramírez Vinasco; Universidad Tecnológica de Pereira, Colombia
Henry Riascos Landázuri; Universidad Tecnológica de Pereira, Colombia
Leonid Ipaz; Universidad del Valle, Colombia
Juan Muñoz Saldaña; Instituto Politécnico Nacional, México
Tipo de recurso:
Fecha de publicación:
2011
Institución:
Universidad del Norte
Repositorio:
Repositorio Uninorte
Idioma:
spa
OAI Identifier:
oai:manglar.uninorte.edu.co:10584/4145
Acceso en línea:
http://rcientificas.uninorte.edu.co/index.php/ingenieria/article/view/2882
http://hdl.handle.net/10584/4145
Palabra clave:
Rights
License
http://purl.org/coar/access_right/c_abf2
id REPOUNORT2_18a61601f9d4712d3728c3ea0bf34d78
oai_identifier_str oai:manglar.uninorte.edu.co:10584/4145
network_acronym_str REPOUNORT2
network_name_str Repositorio Uninorte
repository_id_str
spelling Jorge Luis Gallego Cano; Universidad Tecnológica de Pereira, ColombiaDeisy Ramírez Vinasco; Universidad Tecnológica de Pereira, ColombiaHenry Riascos Landázuri; Universidad Tecnológica de Pereira, ColombiaLeonid Ipaz; Universidad del Valle, ColombiaJuan Muñoz Saldaña; Instituto Politécnico Nacional, MéxicoColombia2013-08-31T23:11:00Z2013-08-31T23:11:00Z2011-08-09http://rcientificas.uninorte.edu.co/index.php/ingenieria/article/view/2882http://hdl.handle.net/10584/4145Carbon Nitride (CNx) thin films were grown by pulsed laser deposition using a Nd:YAG laser (1064 nm, 500mJ), in a graphite target (99.999%) on Si(100) substrate for three different temperatures 21, 50 and 200 °C, in a nitrogen atmosphere at constant pressure of 2,66 Pa. The FTIR’s analysis made to the films, revealed the presence of active modes around 1108 cm-1, 1465 cm-1, 2270 cm-1, associated with the simple, double and triple bonding of CN, respectively. Chemical composition was studied by EDX analysis, low nitrogen contents were found between 3 and 6 at%. And the mechanical properties of the films were evaluated using nanoindentation technique. The highest hardness was 14 GPa at 200 ºC substrate temperature.Películas delgadas de nitruro de carbono (CNx) fueron formadas por la técnica de depósito por láser pulsado (PLD, siglas en inglés). Para la ablación incidió sobre la superficie del blanco de grafito pirolítico (99.999% de pureza) un láser Nd:YAG (1064 nm, 500 mJ), cuya fluencia del haz se mantuvo a un valor de 10 J∙cm-2. Las películas se formaron sobre sustratos de Si (100) y en una atmósfera de nitrógeno, y a tres valores diferentes de temperatura del sustrato (21, 50 y 200° C). Durante el crecimiento de estas películas se mantuvo la presión del gas ambiente constante (2,66 Pa). También se analizaron las propiedades mecánicas y químicas de las películas mediante microscopia de fuerza atómica (AFM, por sus siglas en inglés), espectroscopia infrarroja (FTIR), energía dispersiva de rayos X (EDX) y nanoindentación. El análisis de FTIR revela la presencia de modos activos alrededor de 1108 cm-1, 1465 cm-1, 2270 cm-1, asociados a enlaces simples, dobles y triples de CN, respectivamente. Por medio de EDX, se estudió la composición química de las muestras, encontrándose bajos contenidos de nitrógeno, con una variación entre el 3 y 6 %at. Las propiedades mecánicas fueron evaluadas mediante la técnica de nanoindentación. La mayor dureza de las muestras fue de 14 GPa, obtenida para la muestra formada a una temperatura del sustrato de 200º C.application/pdfspaUniversidad del NorteRevista Científica Ingeniería y Desarrollo; Vol 29, No 1 (2011): Enero - Junio; 50-60instname:Universidad del Nortereponame:Repositorio Digital de la Universidad del NorteCNx thin films grown by PLD at different temperaturesPelículas delgadas de CNx formadas por PLD a diferentes temperaturasarticlepublishedVersionhttp://purl.org/coar/version/c_970fb48d4fbd8a85http://purl.org/coar/resource_type/c_6501http://purl.org/coar/access_right/c_abf210584/4145oai:172.16.14.36:10584/41452015-10-07 01:47:19.844Repositorio Digital de la Universidad del Nortemauribe@uninorte.edu.co
dc.title.none.fl_str_mv CNx thin films grown by PLD at different temperatures
Películas delgadas de CNx formadas por PLD a diferentes temperaturas
title CNx thin films grown by PLD at different temperatures
spellingShingle CNx thin films grown by PLD at different temperatures
title_short CNx thin films grown by PLD at different temperatures
title_full CNx thin films grown by PLD at different temperatures
title_fullStr CNx thin films grown by PLD at different temperatures
title_full_unstemmed CNx thin films grown by PLD at different temperatures
title_sort CNx thin films grown by PLD at different temperatures
dc.creator.fl_str_mv Jorge Luis Gallego Cano; Universidad Tecnológica de Pereira, Colombia
Deisy Ramírez Vinasco; Universidad Tecnológica de Pereira, Colombia
Henry Riascos Landázuri; Universidad Tecnológica de Pereira, Colombia
Leonid Ipaz; Universidad del Valle, Colombia
Juan Muñoz Saldaña; Instituto Politécnico Nacional, México
dc.contributor.author.none.fl_str_mv Jorge Luis Gallego Cano; Universidad Tecnológica de Pereira, Colombia
Deisy Ramírez Vinasco; Universidad Tecnológica de Pereira, Colombia
Henry Riascos Landázuri; Universidad Tecnológica de Pereira, Colombia
Leonid Ipaz; Universidad del Valle, Colombia
Juan Muñoz Saldaña; Instituto Politécnico Nacional, México
description Carbon Nitride (CNx) thin films were grown by pulsed laser deposition using a Nd:YAG laser (1064 nm, 500mJ), in a graphite target (99.999%) on Si(100) substrate for three different temperatures 21, 50 and 200 °C, in a nitrogen atmosphere at constant pressure of 2,66 Pa. The FTIR’s analysis made to the films, revealed the presence of active modes around 1108 cm-1, 1465 cm-1, 2270 cm-1, associated with the simple, double and triple bonding of CN, respectively. Chemical composition was studied by EDX analysis, low nitrogen contents were found between 3 and 6 at%. And the mechanical properties of the films were evaluated using nanoindentation technique. The highest hardness was 14 GPa at 200 ºC substrate temperature.
publishDate 2011
dc.date.issued.none.fl_str_mv 2011-08-09
dc.date.accessioned.none.fl_str_mv 2013-08-31T23:11:00Z
dc.date.available.none.fl_str_mv 2013-08-31T23:11:00Z
dc.type.none.fl_str_mv article
dc.type.coarversion.fl_str_mv http://purl.org/coar/version/c_970fb48d4fbd8a85
dc.type.coar.fl_str_mv http://purl.org/coar/resource_type/c_6501
dc.type.hasVersion.none.fl_str_mv publishedVersion
dc.identifier.other.none.fl_str_mv http://rcientificas.uninorte.edu.co/index.php/ingenieria/article/view/2882
dc.identifier.uri.none.fl_str_mv http://hdl.handle.net/10584/4145
url http://rcientificas.uninorte.edu.co/index.php/ingenieria/article/view/2882
http://hdl.handle.net/10584/4145
dc.language.iso.none.fl_str_mv spa
language spa
dc.relation.ispartof.none.fl_str_mv Revista Científica Ingeniería y Desarrollo; Vol 29, No 1 (2011): Enero - Junio; 50-60
dc.rights.coar.fl_str_mv http://purl.org/coar/access_right/c_abf2
rights_invalid_str_mv http://purl.org/coar/access_right/c_abf2
dc.format.none.fl_str_mv application/pdf
dc.coverage.spatial.none.fl_str_mv Colombia
dc.publisher.none.fl_str_mv Universidad del Norte
publisher.none.fl_str_mv Universidad del Norte
dc.source.none.fl_str_mv instname:Universidad del Norte
reponame:Repositorio Digital de la Universidad del Norte
instname_str Universidad del Norte
institution Universidad del Norte
reponame_str Repositorio Digital de la Universidad del Norte
collection Repositorio Digital de la Universidad del Norte
repository.name.fl_str_mv Repositorio Digital de la Universidad del Norte
repository.mail.fl_str_mv mauribe@uninorte.edu.co
_version_ 1812183120768663552

Publicaciones similares