Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering

ilustraciones, diagramas

Autores:
Prieto Rivera, Lina Fernanda
Tipo de recurso:
Fecha de publicación:
2024
Institución:
Universidad Nacional de Colombia
Repositorio:
Universidad Nacional de Colombia
Idioma:
spa
OAI Identifier:
oai:repositorio.unal.edu.co:unal/86922
Acceso en línea:
https://repositorio.unal.edu.co/handle/unal/86922
https://repositorio.unal.edu.co/
Palabra clave:
530 - Física
620 - Ingeniería y operaciones afines::621 - Física aplicada
SEMICONDUCTORES
PROPIEDADES OPTICAS
MICROSCOPIA DE FUERZA ATOMICA
DIFRACCION DE RAYOS X
ESPECTROSCOPIA DE RAMAN
ESPECTROS MOLECULARES
Semiconductors
Optical properties
Atomic force microscopy
X-rays - diffraction
Raman Spectroscopy
Molecular spectra
DC Magnetron Sputtering
Manganeso (Mn)
Cobalto (Co)
Oxido de Zinc (ZnO)
Espintrónica
Diluted Magnetic Semiconductor
Manganese (Mn)
Cobalt (Co)
Zinc oxide (ZnO)
Spintronics
Rights
openAccess
License
Atribución-NoComercial 4.0 Internacional
id UNACIONAL2_b80ae73d0387e2e3a3ed24f23d243432
oai_identifier_str oai:repositorio.unal.edu.co:unal/86922
network_acronym_str UNACIONAL2
network_name_str Universidad Nacional de Colombia
repository_id_str
dc.title.spa.fl_str_mv Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
dc.title.translated.eng.fl_str_mv Influence of Co/Mn on the Optical and Morphological Properties of ZnO Nanostructures Fabricated by Co-Sputtering
title Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
spellingShingle Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
530 - Física
620 - Ingeniería y operaciones afines::621 - Física aplicada
SEMICONDUCTORES
PROPIEDADES OPTICAS
MICROSCOPIA DE FUERZA ATOMICA
DIFRACCION DE RAYOS X
ESPECTROSCOPIA DE RAMAN
ESPECTROS MOLECULARES
Semiconductors
Optical properties
Atomic force microscopy
X-rays - diffraction
Raman Spectroscopy
Molecular spectra
DC Magnetron Sputtering
Manganeso (Mn)
Cobalto (Co)
Oxido de Zinc (ZnO)
Espintrónica
Diluted Magnetic Semiconductor
Manganese (Mn)
Cobalt (Co)
Zinc oxide (ZnO)
Spintronics
title_short Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
title_full Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
title_fullStr Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
title_full_unstemmed Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
title_sort Influencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-Sputtering
dc.creator.fl_str_mv Prieto Rivera, Lina Fernanda
dc.contributor.advisor.spa.fl_str_mv Dussán Cuenca, Anderson
dc.contributor.author.spa.fl_str_mv Prieto Rivera, Lina Fernanda
dc.contributor.researchgroup.spa.fl_str_mv Materiales Nanoestructurados y Sus Aplicaciones
dc.contributor.cvlac.spa.fl_str_mv https://scienti.minciencias.gov.co/cvlac/visualizador/generarCurriculoCv.do?cod_rh=0000088907
dc.subject.ddc.spa.fl_str_mv 530 - Física
620 - Ingeniería y operaciones afines::621 - Física aplicada
topic 530 - Física
620 - Ingeniería y operaciones afines::621 - Física aplicada
SEMICONDUCTORES
PROPIEDADES OPTICAS
MICROSCOPIA DE FUERZA ATOMICA
DIFRACCION DE RAYOS X
ESPECTROSCOPIA DE RAMAN
ESPECTROS MOLECULARES
Semiconductors
Optical properties
Atomic force microscopy
X-rays - diffraction
Raman Spectroscopy
Molecular spectra
DC Magnetron Sputtering
Manganeso (Mn)
Cobalto (Co)
Oxido de Zinc (ZnO)
Espintrónica
Diluted Magnetic Semiconductor
Manganese (Mn)
Cobalt (Co)
Zinc oxide (ZnO)
Spintronics
dc.subject.lemb.spa.fl_str_mv SEMICONDUCTORES
PROPIEDADES OPTICAS
MICROSCOPIA DE FUERZA ATOMICA
DIFRACCION DE RAYOS X
ESPECTROSCOPIA DE RAMAN
ESPECTROS MOLECULARES
dc.subject.lemb.eng.fl_str_mv Semiconductors
Optical properties
Atomic force microscopy
X-rays - diffraction
Raman Spectroscopy
Molecular spectra
dc.subject.proposal.spa.fl_str_mv DC Magnetron Sputtering
Manganeso (Mn)
Cobalto (Co)
Oxido de Zinc (ZnO)
Espintrónica
dc.subject.proposal.eng.fl_str_mv Diluted Magnetic Semiconductor
Manganese (Mn)
Cobalt (Co)
Zinc oxide (ZnO)
Spintronics
description ilustraciones, diagramas
publishDate 2024
dc.date.accessioned.none.fl_str_mv 2024-10-09T16:48:36Z
dc.date.available.none.fl_str_mv 2024-10-09T16:48:36Z
dc.date.issued.none.fl_str_mv 2024
dc.type.spa.fl_str_mv Trabajo de grado - Maestría
dc.type.driver.spa.fl_str_mv info:eu-repo/semantics/masterThesis
dc.type.version.spa.fl_str_mv info:eu-repo/semantics/acceptedVersion
dc.type.content.spa.fl_str_mv Text
dc.type.redcol.spa.fl_str_mv http://purl.org/redcol/resource_type/TM
status_str acceptedVersion
dc.identifier.uri.none.fl_str_mv https://repositorio.unal.edu.co/handle/unal/86922
dc.identifier.instname.spa.fl_str_mv Universidad Nacional de Colombia
dc.identifier.reponame.spa.fl_str_mv Repositorio Institucional Universidad Nacional de Colombia
dc.identifier.repourl.spa.fl_str_mv https://repositorio.unal.edu.co/
url https://repositorio.unal.edu.co/handle/unal/86922
https://repositorio.unal.edu.co/
identifier_str_mv Universidad Nacional de Colombia
Repositorio Institucional Universidad Nacional de Colombia
dc.language.iso.spa.fl_str_mv spa
language spa
dc.relation.references.spa.fl_str_mv Dussán Cuenca Anderson, Quiroz Gaitán Heiddy Paola, y Calderón Cómbita Jorge Arturo, “Nanomateriales que revolucionan la tecnología.”, Bogotá, D.C. Colombia, jun. 2020.
C. L. Terán Ramírez, “Caracterización y estudio de dispositivos basados en nanoestructuras de ZnO:Co para su aplicación en memorias no volátiles usando una configuración tipo transistor”, 2022, Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: https://repositorio.unal.edu.co/handle/unal/82126
T. Dietl, H. Ohno, F. Matsukura, J. Cibert, y D. Ferrand, “Zener Model Description of Ferromagnetism in Zinc-Blende Magnetic Semiconductors”, Science (1979), vol. 287, no 5455, pp. 1019–1022, feb. 2000, doi: 10.1126/SCIENCE.287.5455.1019.
P. Shukla et al., “Investigation on structural, morphological and optical properties of Co-doped ZnO thin films”, Physica B Condens Matter, vol. 550, pp. 303–310, dic. 2018, doi: 10.1016/J.PHYSB.2018.08.046.
A. Kolodziejczak-Radzimska y T. Jesionowski, “Zinc Oxide—From Synthesis to Application: A Review”, Materials, vol. 7, no 4, p. 2833, 2014, doi: 10.3390/MA7042833.
A. Ashar et al., “Integrated hydrothermal assisted green synthesis of ZnO nano discs and their water purification efficiency together with antimicrobial activity”, Journal of Materials Research and Technology, vol. 15, pp. 6901–6917, nov. 2021, doi: 10.1016/J.JMRT.2021.11.009.
S. Fernández, A. Bollero, F. B. Naranjo, O. de Abril, y J. J. Gandía, “Optimization of ZnO:Al based back reflectors for applications in thin film flexible solar cells”, Vacuum, vol. 99, pp. 56–61, ene. 2014, doi: 10.1016/J.VACUUM.2013.04.013.
S. A. al Rifai y E. P. Domashevskaya, “The synthesis and optical properties of different zinc oxide nanostructures”, Russian Journal of Physical Chemistry A, vol. 87, no 13, pp. 2246–2252, dic. 2013, doi: 10.1134/S0036024413130037.
Y. Kumari, L. K. Jangir, y A. Kumar, “ZnO in solar cell and ultraviolet detectors”, Nanostructured Zinc Oxide, pp. 319–350, ene. 2021, doi: 10.1016/B978-0-12-818900-9.00019-X.
Flores Moreno Armando, “Estudio de nanoestructuras de ZnO estabilizadas con polímeros.”, 2019. Accedido: 29 de enero de 2022. [En línea]. Disponible en: http://dgsa.uaeh.edu.mx:8080/bibliotecadigital/bitstream/handle/231104/2677/Estudio%20de%20nanoestructuras%20de%20ZnO%20estabilizadas%20con%20pol%c3%admeros.pdf?sequence=1&isAllowed=y
M. M. F. F. F. F. A. G. M. (LA) Alejandro Mercado Mercado, “Historia Y Evolución De La Industria De Semiconductores Y La Integración De México En El Sector”, European Scientific Journal, ESJ, 12(18), 65.
W. González, V. Héctor, y L. Mancini, “Ciencia de los Materiales”. [En línea]. Disponible en: http://fisica.unav.es/
Eggleston Dennis L., “Basic Electronics for Scientists and Engineers”, Los Ángeles. [En línea]. Disponible en: www.cambridge.org/Eggleston.
Dr. Guido Tarrach, “Los Semiconductores y sus Aplicaciones”, 2001, Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: https://www.academia.edu/11494235/Los_Semiconductores_y_sus_Aplicaciones
J. S. Meena, S. M. Sze, U. Chand, y T. Y. Tseng, “Overview of emerging nonvolatile memory technologies”, Nanoscale Res Lett, vol. 9, no 1, p. 526, 2014, doi: 10.1186/1556-276X-9-526.
N. Y. Bautista Sapuyes, “Preparación y caracterización del semiconductor ZnO con impurezas magnéticas”, 2019, Accedido: 22 de enero de 2022. [En línea]. Disponible en: https://repositorio.unal.edu.co/handle/unal/76534
J. Antonio, J. Miramontes, y V. H. Collins Martínez, “ESTUDIO DE LAS FASES CRISTALOGRAFICAS DE LA FERRITA DE ESTRONCIO COMO FOTOCATALIZADORES EN LA PRODUCCIÓN DE HIDRÓGENO”, 2018. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: http://cimav.repositorioinstitucional.mx/jspui/handle/1004/1926
Y. • Freedman, “Física universitaria CON FÍSICA MODERNA”.
G. S. Grinblat, “Nanoestructuras semiconductoras de ZnO: fabricación, estudio y optimización de propiedades ópticas lineales y no lineales”, 2015. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: https://repositorio.ecci.edu.co/handle/001/4000
A. Quesada, M. A. García, J. L. Costa-Krämer, J. F. Fernández, M. Martín-González, y A. Hernando, “Semiconductores magnéticos diluidos: Materiales para la espintrónica”, REF Enero-Marzo 2007 , 2007. [En línea]. Disponible en: http://www.rsef.org
A. Carrero, V. Sagredo, C. Pernechele, y J. Larionova, “Propiedades estructurales, ópticas y magnéticas del ZnO: Co preparado por el método sol gel autocombustión”. 2014
D. Olga Sánchez Garrido Ramón Escobar Galindo, M. Yuste Yuste, y J. de, “Dopaje y nanoestructuración de láminas delgadas de ZnO mediante sputtering magnetrón reactivo”, 2013. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: http://hdl.handle.net/10486/660453
Z. bin Gu et al., “Optical properties of (Mn, Co) co-doped ZnO films prepared by dual-radio frequency magnetron sputtering”, Thin Solid Films, vol. 515, no 4, pp. 2361–2365, dic. 2006, doi: 10.1016/j.tsf.2006.04.030.
G. F. Neumark, I. L. Kuskovksy, y H. X. Jiang, Zinc Oxide Fundamentals, Materials and Device Technology by Hadis Morkoç, 220mit Özgür (z-lib.org).
Y. M. Hu et al., “The morphology and optical properties of Cr-doped ZnO films grown using the magnetron co-sputtering method”, Appl Surf Sci, vol. 254, no 13, pp. 3873–3878, abr. 2008, doi: 10.1016/J.APSUSC.2007.12.014.
A. Janotti y C. G. van de Walle, “Fundamentals of zinc oxide as a semiconductor”, Reports on Progress in Physics, vol. 72, no 12, p. 126501, oct. 2009, doi: 10.1088/0034-4885/72/12/126501.
Tosi Ezequiel, “Estudios de Superficies de Nanoestructuras Semiconductoras”, 2019. Accedido: 29 de enero de 2022. [En línea]. Disponible en: https://notablesdelaciencia.conicet.gov.ar/bitstream/handle/11336/102479/CONICET_Digital_Nro.88ecbdd0-9820-4539-a5c1-64131be3e9fd_A.pdf?sequence=2&isAllowed=y
Ü. Özgür et al., “A comprehensive review of ZnO materials and devices”, J Appl Phys, vol. 98, no 4, p. 041301, ago. 2005, doi: 10.1063/1.1992666.
V. Balaprakash, M. Mohan, P. Gowrisankar, K. Thangavel, y S. Sudha, “Structural, morphological and optical properties of nano structured cobalt doped ZnO thin films”, Mater Today Proc, vol. 33, pp. 2251–2254, ene. 2020, doi: 10.1016/J.MATPR.2020.04.061.
Javier Pereyra, “Propiedades Ópticas de Materiales Nanoestructurados: Transmitancia y Fotoluminiscencia.”, Montevideo, Uruguay., 2013. Accedido: 22 de enero de 2022. [En línea]. Disponible en: https://www.colibri.udelar.edu.uy/jspui/bitstream/20.500.12008/4040/1/uy24-63816.pdf
J. Cui, “Zinc oxide nanowires”, Mater Charact, vol. Complete, no 64, pp. 43–52, 2012, doi: 10.1016/J.MATCHAR.2011.11.017.
A. Moezzi, A. M. McDonagh, y M. B. Cortie, “Zinc oxide particles: Synthesis, properties and applications”, Chemical Engineering Journal, vol. 185–186, pp. 1–22, mar. 2012, doi: 10.1016/J.CEJ.2012.01.076.
F.-H. Wang, M.-S. Chen, Y.-L. Jiang, H.-W. Liu, y T.-K. Kang, “Fabrication and characterization of sputtered Mg and F co-doped ZnO thin films with different substrate temperature for silicon thin-film solar cell applications”, J Alloys Compd, vol. 897, p. 163174, mar. 2022, doi: 10.1016/J.JALLCOM.2021.163174.
F. García-Salinas, A. Vázquez-Durán, y J. M. Yáñez-Limón, “Comparative study of Al-doped ZnO films deposited by sol–gel and by sputtering using a sintered target from ZnO nanoparticles synthesized by sol–gel”, Boletín de la Sociedad Española de Cerámica y Vidrio, nov. 2021, doi: 10.1016/J.BSECV.2021.11.004.
Temístocles Mendivil Reynoso, “Fabricación de transistores FET a base de una película delgada de ZnO”, 2010. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: http://hdl.handle.net/20.500.12984/7572
R. Amari, B. Deghfel, A. Mahroug, A. A. Mohamad, A. Boukhari, y N. Selmi, “Effects of Mn doping on the structural, morphological, electronic and optical properties of ZnO thin films by sol-gel spin coating method: An experimental and DFT+U study”, Physica B Condens Matter, vol. 577, p. 411766, ene. 2020, doi: 10.1016/J.PHYSB.2019.411766.
P. Shukla et al., “Investigation on structural, morphological and optical properties of Co-doped ZnO thin films”, Physica B Condens Matter, vol. 550, pp. 303–310, dic. 2018, doi: 10.1016/J.PHYSB.2018.08.046.
F. Lekoui et al., “Investigation of the effects of thermal annealing on the structural, morphological and optical properties of nanostructured Mn doped ZnO thin films”, Opt Mater (Amst), vol. 118, ago. 2021, doi: 10.1016/J.OPTMAT.2021.111236.
D. Sharma y R. Jha, “Transition metal (Co, Mn) co-doped ZnO nanoparticles: Effect on structural and optical properties”, J Alloys Compd, vol. 698, pp. 532–538, 2017, doi: 10.1016/j.jallcom.2016.12.227.
M. Nirmala, P. Smitha, y A. Anukaliani, “Optical and electrical properties of undoped and (Mn, Co) co-doped ZnO nanoparticles synthesized by DC thermal plasma method”, Superlattices Microstruct, vol. 50, no 5, pp. 563–571, nov. 2011, doi: 10.1016/j.spmi.2011.09.002.
V. K. Sharma, M. Najim, A. K. Srivastava, y G. D. Varma, “Structural and magnetic studies on transition metal (Mn, Co) doped ZnO nanoparticles”, J Magn Magn Mater, vol. 324, no 5, pp. 683–689, mar. 2012, doi: 10.1016/j.jmmm.2011.08.061.
ELEAZAR GÁNDARA MARTÍNEZ, “SÍNTESIS Y CARACTERIZACIÓN DE HETEROESTRUCTURAS DE PELÍCULAS DELGADAS DE ZNO: AL/ZNS”, dic. 2015, Accedido: 22 de enero de 2022. [En línea]. Disponible en: http://eprints.uanl.mx/id/eprint/11783
N. Kamarulzaman, M. F. Kasim, y R. Rusdi, “Band Gap Narrowing and Widening of ZnO Nanostructures and Doped Materials”, Nanoscale Res Lett, vol. 10, no 1, pp. 1–12, dic. 2015, doi: 10.1186/S11671-015-1034-9/TABLES/4.
De atocha Martín Enrique A., “Propiedades estructurales, morfologicas y optoelectronicas de peliculas delgadas de oxido de zinc preparadas por rf-sputtering”. Accedido: 15 de enero de 2022. [En línea]. Disponible en: https://www.researchgate.net/publication/317452869_Propiedades_estructurales_morfologicas_y_optoelectronicas_de_peliculas_delgadas_de_oxido_de_zinc_preparadas_por_rf-sputtering#pf11
A. M. Luis Angelats Silva, A. López Milla, J. Rodríguez Rodríguez, O. Perales-Pérez, y S. Rojas Flores, “CRECIMIENTO Y MORFOLOGÍA DE NANOESTRUCTURAS DE ZnO OBTENIDAS POR ROCIADO PIROLÍTICO GROWTH AND MORPHOLOGY OF ZnO NANOESTRUCTURES OBTAINED BY SPRAYED PYROLITIC”, Pueblo Cont, vol. 24, pp. 105–112, 2013.
HINESTROZA SAMIR AGÁMEZ, “Determinación de la Longitud del Enlace Zn − O en el Semiconductor ZnO Dopado con Ce Mediante Espectroscopía Infrarroja con Transformada de Fourier y Difracción de Rayos X”, 2021.
R. Yakimova, “Developments in the growth of wide bandgap semiconductors*”, Phys Scr, vol. 2006, no T126, p. 121, ago. 2006, doi: 10.1088/0031-8949/2006/T126/027.
M. López Ponce, “PROPIEDADES ÓPTICAS Y ESTRUCTURALES DE NANOESTRUCTURAS DE Zn(Cd)(Mg)O”, 2015.
E. , P. R. , & R. L. . Villegas, “Métodos de medición de espesores de películas delgadas basadas en óxidos semiconductores”, Revista mexicana de física, 64(4), 364-367., 2018.
E. Adrián, D. E. Atocha, y M. Tovar, “‘PROPIEDADES ESTRUCTURALES, MORFOLÓGICAS Y OPTOELECTRÓNICAS DE PELÍCULAS DELGADAS DE ÓXIDO DE ZINC PREPARADAS POR RF-SPUTTERING’ TESIS PRESENTADA POR”, 2010.
L. M.-A. a, A. G. H.-Z. Alondra S. Mendoza-Villeda, “Caracterización morfológica de nanotubos de ZnO”, TEPEXI Boletín Científico de la Escuela Superior Tepeji del Río, 2020.
N. Yanira y B. Sapuyes, “Preparación y caracterización del semiconductor ZnO con impurezas magnéticas”, 2019.
L. A. Florez Galvan, “CORRELACIÓN ENTRE LAS PROPIEDADES ESTRUCTURALES Y ÓPTICAS DEL ÓXIDO DE ZINC NANOESTRUCTURADO DOPADO CON COBALTO”, 2020.
J. J. Beltrán, C. A. Barrero, y A. Punnoose, “Identifying the sources of ferromagnetism in sol-gel synthesized Zn1−xCoxO (0≤x≤0.10) nanoparticles”, J Solid State Chem, vol. 240, pp. 30–42, ago. 2016, doi: 10.1016/J.JSSC.2016.05.013.
Y. Kumar, A. Sahai, S. F. Olive-Méndez, N. Goswami, y V. Agarwal, “Morphological transformations in cobalt doped zinc oxide nanostructures: Effect of doping concentration”, Ceram Int, vol. 42, no 4, pp. 5184–5194, mar. 2016, doi: 10.1016/J.CERAMINT.2015.12.041.
V. Gandhi, R. Ganesan, H. Hameed, A. Syedahamed, y M. Thaiyan, “Effect of Cobalt Doping on Structural, Optical, and Magnetic Properties of ZnO Nanoparticles Synthesized by Coprecipitation Method”, 2016.
N. M. Basith, J. J. Vijaya, L. J. Kennedy, M. Bououdina, S. Jenefar, y V. Kaviyarasan, “Co-Doped ZnO Nanoparticles: Structural, Morphological, Optical, Magnetic and Antibacterial Studies”, J Mater Sci Technol, vol. 30, no 11, pp. 1108–1117, nov. 2014, doi: 10.1016/J.JMST.2014.07.013.
DEISY RAMÍREZ VINASCO y LILIANA PATRICIA VERA L, “PELÍCULAS DELGADAS DE Zn 1-x Mn x O”, 2009.
H. fu Zhang, R. jin Liu, H. fa Liu, C. xin Lei, D. tai Feng, y C. K. Yuan, “Mn-doped ZnO transparent conducting films deposited by DC magnetron sputtering”, Mater Lett, vol. 64, no 5, pp. 605–607, mar. 2010, doi: 10.1016/j.matlet.2009.12.015.
M. A. Borysiewicz, “ZnO as a Functional Material, a Review”, Crystals, vol. 9, no. 10, p. 505, 2019., 2019, doi: 10.3390/cryst9100505.
Dmitry Bokov, Abduladheem Turki Jalil, Supat Chupradit, y Wanich Suksatan, “Nanomaterial by Sol-Gel Method: Synthesis and Application”, Advances in Materials Science and Engineering, 2021.
Jesús Herranz Zamorano, “Crecimiento por Epitaxia de Haces Moleculares de puntos cuánticos de InAs sobre GaAs(001) con control en su lugar de formación para su integración en microcavidades ópticas”, Instituto de Microelectrónica de Madrid, 2015.
L. Guillermo, A. Gutiérrez, D. C. Constanza, y P. Espinosa, “SÍNTESIS DE PELÍCULAS DELGADAS POR LA TÉCNICA DE MAGNETRÓN SPUTTERING A PARTIR DE BLANCOS DE RENIO Y BORO”, 2017.
J. A. Juhasz y S. M. Best, “Surface modification of biomaterials by calcium phosphate deposition”, Surface Modification of Biomaterials: Methods Analysis and Applications, pp. 143–169, ene. 2011, doi: 10.1533/9780857090768.1.143.
M. Camino, “Electrodeposición de películas delgadass de ZnO para aplicaciones fotovoltaicas”, 2020. [En línea]. Disponible en: http://rinfi.fi.mdp.edu.arhttp://rinfi.fi.mdp.edu.ar/xmlui/handle/123456789/424
C. C. Jorge Arturo, “ESTUDIO DE LAS PROPIEDADES ÓPTICAS Y ELÉCTRICAS DEL COMPUESTO Ga 1-x Mn x Sb USADO PARA APLICACIONES EN ESPINTRÓNICA”, 2016.
Recursos para el espectrofotómetro UV-Vis, “Recursos para el espectrofotómetro UV-Vis”, Thermo Fisher Scientific Inc. Accedido: 21 de noviembre de 2023. [En línea]. Disponible en: https://www.thermofisher.com/co/en/home/industrial/spectroscopy-elemental-isotope-analysis
J. Sánchez-González, A. Díaz-Parralejo, A. L. Ortiz, y F. Guiberteau, “Determination of optical properties in nanostructured thin films using the Swanepoel method”, Appl Surf Sci, vol. 252, no 17, pp. 6013–6017, jun. 2006, doi: 10.1016/J.APSUSC.2005.11.009.
F. Mesa, V. Ballesteros, y A. Dussan, “Cálculo de constantes ópticas de películas delgadas de Cu3BiS3 a través del método de Wolfe”, Univ Sci (Bogota), vol. 19, no 2, mar. 2014, doi: 10.11144/Javeriana.SC19-2.ccop.
S. R. Bhattacharyya, R. N. Gayen, R. Paul, y A. K. Pal, “Determination of optical constants of thin films from transmittance trace”, Thin Solid Films, vol. 517, no 18, pp. 5530–5536, jul. 2009, doi: 10.1016/j.tsf.2009.03.168.
M. Nowak, “Thin Solid Films”, 254 (1995) 200.
D. Poelman y P. F. Smet, “Methods for the determination of the optical constants of thin films from single transmission measurements: a critical review”, J Phys D Appl Phys, vol. 36, no 15, pp. 1850–1857, ago. 2003, doi: 10.1088/0022-3727/36/15/316.
I. O. D. Franta, “Optical characterization of inhomogeneous thin films of ZrO2 by spectroscopic ellipsometry and spectroscopic reflectometry”, Wiley Analytical Science, 2000.
Ana Iris Peña Maldonado., “LINAN LABORATORIO NACIONAL DE INVESTIGACIONES EN NANOCIENCIAS Y NANOTECNOLOGÍA IPICYT”.
J. Ernesto y V. Cadre, “Microscopía de Fuerza Atómica”, 2020, doi: 10.13140/RG.2.2.17860.24963.
E. N. La, C. De Materiales, M. Ipohorski, y P. B. Bozzano, “MICROSCOPÍA ELECTRÓNICA DE BARRIDO”.
“Microscópio electrónico escaneando HistoriayPrincipios y Capacidades”, Microscópio electrónico escaneando HistoriayPrincipios y capacidades, https://hmong.es/wiki/Scanning_electron_microscope (accessed 10 December 2023).
A. Patricia y L. Díaz, “SÍNTESIS Y ESTUDIO DEL EFECTO DEL Mn SOBRE LAS PROPIEDADES ESTRUCTURALES Y ELÉCTRICAS DE NANOESTRUCTURAS DE ZnO”, 2023.
“Microscopía electrónica de barrido de emisión de campo : Servicio de Microscopía Electrónica : UPV”. Accedido: 12 de enero de 2024. [En línea]. Disponible en: https://www.upv.es/entidades/SME/info/859071normalc.html#
C. Á. Romero, M. Teresa, y D. Carbó, “APLICACIÓN DE LA TÉCNICA DE MICROSCOPIA ELECTRÓNICA DE BARRIDO DE EMISIÓN DE CAMPO CON HAZ DE IONES FOCALIZADO-MICROANÁLISIS DE RAYOS X A COLECCIONES NUMISMÁTICAS”.
B. D. (Bernard D. Cullity, Elements of x-ray diffraction. Addison-Wesley Publishing Company, Inc, 1978.
G. F. Harrington y J. Santiso, “Back-to-Basics tutorial: X-ray diffraction of thin films”, J Electroceram, vol. 47, no 4, pp. 141–163, dic. 2021, doi: 10.1007/s10832-021-00263-6.
Y. Waseda, E. Matsubara, y K. Shinoda, “X-Ray Diffraction Crystallography”, X-Ray Diffraction Crystallography, 2011, doi: 10.1007/978-3-642-16635-8.
U. Nacional, A. De México, M. Luisa, y R. García, “Centro de Investigación en Energía Introducción al Método Rietveld Septiembre de 2007”.
V. Esteve, “El método de Rietveld”, 2006, Accedido: 12 de enero de 2024. [En línea]. Disponible en: https://latam.casadellibro.com/libro-el-metodo-rietveld/9788480215756/1133058
J. Otero, “Espectroscopía Raman: Fundamento y aplicaciones”, 2015, doi: 10.13140/RG.2.1.5015.5362.
A. Carrero, V. Sagredo, C. Pernechele, y J. Larionova, “Propiedades estructurales, ópticas y magnéticas del ZnO: Co preparado por el método sol gel autocombustión”, 2014.
José M. Albella, Capas delgadas y modificación superficial de materiales. 2018.
T. MARIA FERNANDEZ NAVARRO Doctor en Ciencias Químicas, “Nucleación y cristalización en vidrios”.
“Shalimova_K_V_Fisica_De_Los_Semiconducto”, Editorial MIR MOSCU, 1975.
P. Makuła, M. Pacia, y W. Macyk, “How To Correctly Determine the Band Gap Energy of Modified Semiconductor Photocatalysts Based on UV-Vis Spectra”, 6 de diciembre de 2018, American Chemical Society. doi: 10.1021/acs.jpclett.8b02892.
Gerardo García Naumis, “Nuevas tecnologías que surgen del desorden: LOS MATERIALES AMORFOS”, 2003.
I. C. R. H. P. P. Oslen Dilayder Jaimes, “Correlation Method in a ZnO Crystal”, Ciencia en Desarrollo, Vol. 9 No. 2, 2018.
Marcel Schumm, “ZnO-based semiconductors studied by Raman spectroscopy: semimagnetic alloying, doping, and nanostructures”, 2008.
“Nanopartículas de Óxido de Zinc Dopadas con Co, Cr, Fe, Mn y Ni. Propiedades Y Aplicación En La Degradación Fotocatalítica De Compuestos Orgánicos Contaminantes”. Accedido: 27 de enero de 2024. [En línea]. Disponible en: https://repositorio.unal.edu.co/handle/unal/83694
M. I. Medina-Montes et al., “Physical properties of photoconductive Ag-Sb-S thin films prepared by thermal evaporation”, Mater Sci Semicond Process, vol. 137, p. 106167, ene. 2022, doi: 10.1016/J.MSSP.2021.106167.
E. M. García Martínez, “Aplicación de la ley de Lambert-Beer en espectroscopía UV-visible”, jun. 2012, Accedido: 22 de julio de 2024. [En línea]. Disponible en: https://riunet.upv.es:443/handle/10251/16360
“Microscopio de Fuerza Atómica (ATM)”. Accedido: 3 de enero de 2024. [En línea]. Disponible en: http://www.linan-ipicyt.mx/Microscopio_de_Fuerza_Atomica.html
B. J. Inkson, “Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) for materials characterization”, Materials Characterization Using Nondestructive Evaluation (NDE) Methods, pp. 17–43, ene. 2016, doi: 10.1016/B978-0-08-100040-3.00002-X.
“The Raman Spectrophotometer”. Accedido: 12 de enero de 2024. [En línea]. Disponible en: https://www.sas.upenn.edu/~crulli/TheRamanSpectrophotometer.html
dc.rights.coar.fl_str_mv http://purl.org/coar/access_right/c_abf2
dc.rights.license.spa.fl_str_mv Atribución-NoComercial 4.0 Internacional
dc.rights.uri.spa.fl_str_mv http://creativecommons.org/licenses/by-nc/4.0/
dc.rights.accessrights.spa.fl_str_mv info:eu-repo/semantics/openAccess
rights_invalid_str_mv Atribución-NoComercial 4.0 Internacional
http://creativecommons.org/licenses/by-nc/4.0/
http://purl.org/coar/access_right/c_abf2
eu_rights_str_mv openAccess
dc.format.extent.spa.fl_str_mv 87 páginas
dc.format.mimetype.spa.fl_str_mv application/pdf
dc.publisher.spa.fl_str_mv Universidad Nacional de Colombia
dc.publisher.program.spa.fl_str_mv Bogotá - Ciencias - Maestría en Ciencias - Física
dc.publisher.faculty.spa.fl_str_mv Facultad de Ciencias
dc.publisher.place.spa.fl_str_mv Bogotá, Colombia
dc.publisher.branch.spa.fl_str_mv Universidad Nacional de Colombia - Sede Bogotá
institution Universidad Nacional de Colombia
bitstream.url.fl_str_mv https://repositorio.unal.edu.co/bitstream/unal/86922/1/license.txt
https://repositorio.unal.edu.co/bitstream/unal/86922/2/1016054985.2024.pdf
https://repositorio.unal.edu.co/bitstream/unal/86922/3/1016054985.2024.pdf.jpg
bitstream.checksum.fl_str_mv eb34b1cf90b7e1103fc9dfd26be24b4a
c865b7cc5c00fd13214377a95c48f922
b0432bbbead1054b2769f66448d17ba2
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
repository.name.fl_str_mv Repositorio Institucional Universidad Nacional de Colombia
repository.mail.fl_str_mv repositorio_nal@unal.edu.co
_version_ 1814089247948275712
spelling Atribución-NoComercial 4.0 Internacionalhttp://creativecommons.org/licenses/by-nc/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Dussán Cuenca, Anderson393dbd423635d474564f566b8ee5f549Prieto Rivera, Lina Fernanda020cf6b79c623607c2dd24a62a3b3971Materiales Nanoestructurados y Sus Aplicacioneshttps://scienti.minciencias.gov.co/cvlac/visualizador/generarCurriculoCv.do?cod_rh=00000889072024-10-09T16:48:36Z2024-10-09T16:48:36Z2024https://repositorio.unal.edu.co/handle/unal/86922Universidad Nacional de ColombiaRepositorio Institucional Universidad Nacional de Colombiahttps://repositorio.unal.edu.co/ilustraciones, diagramasEn este trabajo se estudiaron los efectos de Mn y Co sobre las propiedades morfológicas, ópticas y estructurales de películas delgadas de ZnO fabricadas por el método DC Magnetron Co-Sputtering, modificando algunos parámetros de síntesis sobre cada muestra, algunos como; concentración de Mn o de Co, temperatura del sustrato, uso de sustrato de distinta naturaleza a la del vidrio; tal como el Titanio y la variación en el tiempo de depósito. Es así que a partir de la caracterización a través de microscopia SEM, FESEM y AFM mostraron formación granular, la topografía de las muestras ZnO:Co constituida por pequeños gránulos, en donde a mayor concentración del material depositado las nanoestructuras granulares tienen mayor tamaño y se definen al aumentar la resolución de la micrografía. Por otra parte, para las muestras ZnO:Mn el aumento en la potencia del Mn genera la formación de “clusters” en la superficie de la película delgada. La caracterización óptica se realizó a través del uso de un espectrofotómetro Cary 5000 del UV-VIS-NIR de alto rendimiento fotométrico en el rango de 250 a 2500 nm a presión atmosférica y temperatura ambiente, este estudio mostró que la brecha de energía “gap” del material ZnO:Co toma valores entre 3,00 eV y 3,58 eV de acuerdo a los parámetros de síntesis y la concentración de Co, a su vez para las muestras ZnO:Mn el valor del gap toma valores entre 3,48 eV y 3,64 eV. También, se establecieron los comportamientos del coeficiente de absorción (α), el coeficiente de extinción (k), gap y una estimación del espesor (d) de las muestras. A partir de la caracterización por difracción de rayos X (XRD, por sus siglas en inglés) y espectroscopia RAMAN revelan la característica amorfa de la muestra, lo que implica que la película delgada no presenta fases cristalinas. Así mismo, se identificaron bandas asociadas a los modos de vibración que son atribuidas a los modos E2 (alto) y E1 (LO) permiten afirmar la presencia de la fase de ZnO (Texto tomado de la fuente).In this work the effects of Mn and Co on the morphological, optical and structural properties of ZnO thin films fabricated by the DC Magnetron Co-Sputtering method were studied, modifying some synthesis parameters on each sample, such as; concentration of Mn or Co, substrate temperature, use of substrate of different nature to that of glass; such as Titanium and the variation in the deposition time. Thus, from the characterization through SEM microscopy, FESEM and AFM showed granular formation, the topography of the ZnO:Co samples constituted by small granules, where the higher the concentration of the deposited material, the larger the granular nanostructures are and they are defined by increasing the resolution of the micrograph. On the other hand, for the ZnO:Mn samples the increase in Mn power generates the formation of “clusters” on the surface of the thin film. The optical characterization was performed through the use of a Cary 5000 UV-VIS-NIR spectrophotometer of high photometric performance in the range of 250 to 2500 nm at atmospheric pressure and room temperature, this study showed that the energy gap of the ZnO:Co material takes values between 3.00 eV and 3.58 eV according to the synthesis parameters and the concentration of Co, in turn for the ZnO:Mn samples the value of the gap takes values between 3.48 eV and 3.64 eV. Also, the behaviors of the absorption coefficient (α), extinction coefficient (k), gap and an estimation of the thickness (d) of the samples were established. Characterization by X-ray diffraction (XRD) and RAMAN spectroscopy revealed the amorphous characteristic of the sample, which implies that the thin film does not present crystalline phases. Likewise, bands associated to the vibrational modes were identified, which are attributed to the E2 (high) and E1 (LO) modes and allow affirming the presence of the ZnO phase.MaestríaMagister en Ciencias - Física87 páginasapplication/pdfspaUniversidad Nacional de ColombiaBogotá - Ciencias - Maestría en Ciencias - FísicaFacultad de CienciasBogotá, ColombiaUniversidad Nacional de Colombia - Sede Bogotá530 - Física620 - Ingeniería y operaciones afines::621 - Física aplicadaSEMICONDUCTORESPROPIEDADES OPTICASMICROSCOPIA DE FUERZA ATOMICADIFRACCION DE RAYOS XESPECTROSCOPIA DE RAMANESPECTROS MOLECULARESSemiconductorsOptical propertiesAtomic force microscopyX-rays - diffractionRaman SpectroscopyMolecular spectraDC Magnetron SputteringManganeso (Mn)Cobalto (Co)Oxido de Zinc (ZnO)EspintrónicaDiluted Magnetic SemiconductorManganese (Mn)Cobalt (Co)Zinc oxide (ZnO)SpintronicsInfluencia del Co/Mn sobre las propiedades ópticas y morfológicas de nano estructuras de ZnO fabricadas por Co-SputteringInfluence of Co/Mn on the Optical and Morphological Properties of ZnO Nanostructures Fabricated by Co-SputteringTrabajo de grado - Maestríainfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/acceptedVersionTexthttp://purl.org/redcol/resource_type/TMDussán Cuenca Anderson, Quiroz Gaitán Heiddy Paola, y Calderón Cómbita Jorge Arturo, “Nanomateriales que revolucionan la tecnología.”, Bogotá, D.C. Colombia, jun. 2020.C. L. Terán Ramírez, “Caracterización y estudio de dispositivos basados en nanoestructuras de ZnO:Co para su aplicación en memorias no volátiles usando una configuración tipo transistor”, 2022, Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: https://repositorio.unal.edu.co/handle/unal/82126T. Dietl, H. Ohno, F. Matsukura, J. Cibert, y D. Ferrand, “Zener Model Description of Ferromagnetism in Zinc-Blende Magnetic Semiconductors”, Science (1979), vol. 287, no 5455, pp. 1019–1022, feb. 2000, doi: 10.1126/SCIENCE.287.5455.1019.P. Shukla et al., “Investigation on structural, morphological and optical properties of Co-doped ZnO thin films”, Physica B Condens Matter, vol. 550, pp. 303–310, dic. 2018, doi: 10.1016/J.PHYSB.2018.08.046.A. Kolodziejczak-Radzimska y T. Jesionowski, “Zinc Oxide—From Synthesis to Application: A Review”, Materials, vol. 7, no 4, p. 2833, 2014, doi: 10.3390/MA7042833.A. Ashar et al., “Integrated hydrothermal assisted green synthesis of ZnO nano discs and their water purification efficiency together with antimicrobial activity”, Journal of Materials Research and Technology, vol. 15, pp. 6901–6917, nov. 2021, doi: 10.1016/J.JMRT.2021.11.009.S. Fernández, A. Bollero, F. B. Naranjo, O. de Abril, y J. J. Gandía, “Optimization of ZnO:Al based back reflectors for applications in thin film flexible solar cells”, Vacuum, vol. 99, pp. 56–61, ene. 2014, doi: 10.1016/J.VACUUM.2013.04.013.S. A. al Rifai y E. P. Domashevskaya, “The synthesis and optical properties of different zinc oxide nanostructures”, Russian Journal of Physical Chemistry A, vol. 87, no 13, pp. 2246–2252, dic. 2013, doi: 10.1134/S0036024413130037.Y. Kumari, L. K. Jangir, y A. Kumar, “ZnO in solar cell and ultraviolet detectors”, Nanostructured Zinc Oxide, pp. 319–350, ene. 2021, doi: 10.1016/B978-0-12-818900-9.00019-X.Flores Moreno Armando, “Estudio de nanoestructuras de ZnO estabilizadas con polímeros.”, 2019. Accedido: 29 de enero de 2022. [En línea]. Disponible en: http://dgsa.uaeh.edu.mx:8080/bibliotecadigital/bitstream/handle/231104/2677/Estudio%20de%20nanoestructuras%20de%20ZnO%20estabilizadas%20con%20pol%c3%admeros.pdf?sequence=1&isAllowed=yM. M. F. F. F. F. A. G. M. (LA) Alejandro Mercado Mercado, “Historia Y Evolución De La Industria De Semiconductores Y La Integración De México En El Sector”, European Scientific Journal, ESJ, 12(18), 65.W. González, V. Héctor, y L. Mancini, “Ciencia de los Materiales”. [En línea]. Disponible en: http://fisica.unav.es/Eggleston Dennis L., “Basic Electronics for Scientists and Engineers”, Los Ángeles. [En línea]. Disponible en: www.cambridge.org/Eggleston.Dr. Guido Tarrach, “Los Semiconductores y sus Aplicaciones”, 2001, Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: https://www.academia.edu/11494235/Los_Semiconductores_y_sus_AplicacionesJ. S. Meena, S. M. Sze, U. Chand, y T. Y. Tseng, “Overview of emerging nonvolatile memory technologies”, Nanoscale Res Lett, vol. 9, no 1, p. 526, 2014, doi: 10.1186/1556-276X-9-526.N. Y. Bautista Sapuyes, “Preparación y caracterización del semiconductor ZnO con impurezas magnéticas”, 2019, Accedido: 22 de enero de 2022. [En línea]. Disponible en: https://repositorio.unal.edu.co/handle/unal/76534J. Antonio, J. Miramontes, y V. H. Collins Martínez, “ESTUDIO DE LAS FASES CRISTALOGRAFICAS DE LA FERRITA DE ESTRONCIO COMO FOTOCATALIZADORES EN LA PRODUCCIÓN DE HIDRÓGENO”, 2018. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: http://cimav.repositorioinstitucional.mx/jspui/handle/1004/1926Y. • Freedman, “Física universitaria CON FÍSICA MODERNA”.G. S. Grinblat, “Nanoestructuras semiconductoras de ZnO: fabricación, estudio y optimización de propiedades ópticas lineales y no lineales”, 2015. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: https://repositorio.ecci.edu.co/handle/001/4000A. Quesada, M. A. García, J. L. Costa-Krämer, J. F. Fernández, M. Martín-González, y A. Hernando, “Semiconductores magnéticos diluidos: Materiales para la espintrónica”, REF Enero-Marzo 2007 , 2007. [En línea]. Disponible en: http://www.rsef.orgA. Carrero, V. Sagredo, C. Pernechele, y J. Larionova, “Propiedades estructurales, ópticas y magnéticas del ZnO: Co preparado por el método sol gel autocombustión”. 2014D. Olga Sánchez Garrido Ramón Escobar Galindo, M. Yuste Yuste, y J. de, “Dopaje y nanoestructuración de láminas delgadas de ZnO mediante sputtering magnetrón reactivo”, 2013. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: http://hdl.handle.net/10486/660453Z. bin Gu et al., “Optical properties of (Mn, Co) co-doped ZnO films prepared by dual-radio frequency magnetron sputtering”, Thin Solid Films, vol. 515, no 4, pp. 2361–2365, dic. 2006, doi: 10.1016/j.tsf.2006.04.030.G. F. Neumark, I. L. Kuskovksy, y H. X. Jiang, Zinc Oxide Fundamentals, Materials and Device Technology by Hadis Morkoç, 220mit Özgür (z-lib.org).Y. M. Hu et al., “The morphology and optical properties of Cr-doped ZnO films grown using the magnetron co-sputtering method”, Appl Surf Sci, vol. 254, no 13, pp. 3873–3878, abr. 2008, doi: 10.1016/J.APSUSC.2007.12.014.A. Janotti y C. G. van de Walle, “Fundamentals of zinc oxide as a semiconductor”, Reports on Progress in Physics, vol. 72, no 12, p. 126501, oct. 2009, doi: 10.1088/0034-4885/72/12/126501.Tosi Ezequiel, “Estudios de Superficies de Nanoestructuras Semiconductoras”, 2019. Accedido: 29 de enero de 2022. [En línea]. Disponible en: https://notablesdelaciencia.conicet.gov.ar/bitstream/handle/11336/102479/CONICET_Digital_Nro.88ecbdd0-9820-4539-a5c1-64131be3e9fd_A.pdf?sequence=2&isAllowed=yÜ. Özgür et al., “A comprehensive review of ZnO materials and devices”, J Appl Phys, vol. 98, no 4, p. 041301, ago. 2005, doi: 10.1063/1.1992666.V. Balaprakash, M. Mohan, P. Gowrisankar, K. Thangavel, y S. Sudha, “Structural, morphological and optical properties of nano structured cobalt doped ZnO thin films”, Mater Today Proc, vol. 33, pp. 2251–2254, ene. 2020, doi: 10.1016/J.MATPR.2020.04.061.Javier Pereyra, “Propiedades Ópticas de Materiales Nanoestructurados: Transmitancia y Fotoluminiscencia.”, Montevideo, Uruguay., 2013. Accedido: 22 de enero de 2022. [En línea]. Disponible en: https://www.colibri.udelar.edu.uy/jspui/bitstream/20.500.12008/4040/1/uy24-63816.pdfJ. Cui, “Zinc oxide nanowires”, Mater Charact, vol. Complete, no 64, pp. 43–52, 2012, doi: 10.1016/J.MATCHAR.2011.11.017.A. Moezzi, A. M. McDonagh, y M. B. Cortie, “Zinc oxide particles: Synthesis, properties and applications”, Chemical Engineering Journal, vol. 185–186, pp. 1–22, mar. 2012, doi: 10.1016/J.CEJ.2012.01.076.F.-H. Wang, M.-S. Chen, Y.-L. Jiang, H.-W. Liu, y T.-K. Kang, “Fabrication and characterization of sputtered Mg and F co-doped ZnO thin films with different substrate temperature for silicon thin-film solar cell applications”, J Alloys Compd, vol. 897, p. 163174, mar. 2022, doi: 10.1016/J.JALLCOM.2021.163174.F. García-Salinas, A. Vázquez-Durán, y J. M. Yáñez-Limón, “Comparative study of Al-doped ZnO films deposited by sol–gel and by sputtering using a sintered target from ZnO nanoparticles synthesized by sol–gel”, Boletín de la Sociedad Española de Cerámica y Vidrio, nov. 2021, doi: 10.1016/J.BSECV.2021.11.004.Temístocles Mendivil Reynoso, “Fabricación de transistores FET a base de una película delgada de ZnO”, 2010. Accedido: 27 de septiembre de 2024. [En línea]. Disponible en: http://hdl.handle.net/20.500.12984/7572R. Amari, B. Deghfel, A. Mahroug, A. A. Mohamad, A. Boukhari, y N. Selmi, “Effects of Mn doping on the structural, morphological, electronic and optical properties of ZnO thin films by sol-gel spin coating method: An experimental and DFT+U study”, Physica B Condens Matter, vol. 577, p. 411766, ene. 2020, doi: 10.1016/J.PHYSB.2019.411766.P. Shukla et al., “Investigation on structural, morphological and optical properties of Co-doped ZnO thin films”, Physica B Condens Matter, vol. 550, pp. 303–310, dic. 2018, doi: 10.1016/J.PHYSB.2018.08.046.F. Lekoui et al., “Investigation of the effects of thermal annealing on the structural, morphological and optical properties of nanostructured Mn doped ZnO thin films”, Opt Mater (Amst), vol. 118, ago. 2021, doi: 10.1016/J.OPTMAT.2021.111236.D. Sharma y R. Jha, “Transition metal (Co, Mn) co-doped ZnO nanoparticles: Effect on structural and optical properties”, J Alloys Compd, vol. 698, pp. 532–538, 2017, doi: 10.1016/j.jallcom.2016.12.227.M. Nirmala, P. Smitha, y A. Anukaliani, “Optical and electrical properties of undoped and (Mn, Co) co-doped ZnO nanoparticles synthesized by DC thermal plasma method”, Superlattices Microstruct, vol. 50, no 5, pp. 563–571, nov. 2011, doi: 10.1016/j.spmi.2011.09.002.V. K. Sharma, M. Najim, A. K. Srivastava, y G. D. Varma, “Structural and magnetic studies on transition metal (Mn, Co) doped ZnO nanoparticles”, J Magn Magn Mater, vol. 324, no 5, pp. 683–689, mar. 2012, doi: 10.1016/j.jmmm.2011.08.061.ELEAZAR GÁNDARA MARTÍNEZ, “SÍNTESIS Y CARACTERIZACIÓN DE HETEROESTRUCTURAS DE PELÍCULAS DELGADAS DE ZNO: AL/ZNS”, dic. 2015, Accedido: 22 de enero de 2022. [En línea]. Disponible en: http://eprints.uanl.mx/id/eprint/11783N. Kamarulzaman, M. F. Kasim, y R. Rusdi, “Band Gap Narrowing and Widening of ZnO Nanostructures and Doped Materials”, Nanoscale Res Lett, vol. 10, no 1, pp. 1–12, dic. 2015, doi: 10.1186/S11671-015-1034-9/TABLES/4.De atocha Martín Enrique A., “Propiedades estructurales, morfologicas y optoelectronicas de peliculas delgadas de oxido de zinc preparadas por rf-sputtering”. Accedido: 15 de enero de 2022. [En línea]. Disponible en: https://www.researchgate.net/publication/317452869_Propiedades_estructurales_morfologicas_y_optoelectronicas_de_peliculas_delgadas_de_oxido_de_zinc_preparadas_por_rf-sputtering#pf11A. M. Luis Angelats Silva, A. López Milla, J. Rodríguez Rodríguez, O. Perales-Pérez, y S. Rojas Flores, “CRECIMIENTO Y MORFOLOGÍA DE NANOESTRUCTURAS DE ZnO OBTENIDAS POR ROCIADO PIROLÍTICO GROWTH AND MORPHOLOGY OF ZnO NANOESTRUCTURES OBTAINED BY SPRAYED PYROLITIC”, Pueblo Cont, vol. 24, pp. 105–112, 2013.HINESTROZA SAMIR AGÁMEZ, “Determinación de la Longitud del Enlace Zn − O en el Semiconductor ZnO Dopado con Ce Mediante Espectroscopía Infrarroja con Transformada de Fourier y Difracción de Rayos X”, 2021.R. Yakimova, “Developments in the growth of wide bandgap semiconductors*”, Phys Scr, vol. 2006, no T126, p. 121, ago. 2006, doi: 10.1088/0031-8949/2006/T126/027.M. López Ponce, “PROPIEDADES ÓPTICAS Y ESTRUCTURALES DE NANOESTRUCTURAS DE Zn(Cd)(Mg)O”, 2015.E. , P. R. , & R. L. . Villegas, “Métodos de medición de espesores de películas delgadas basadas en óxidos semiconductores”, Revista mexicana de física, 64(4), 364-367., 2018.E. Adrián, D. E. Atocha, y M. Tovar, “‘PROPIEDADES ESTRUCTURALES, MORFOLÓGICAS Y OPTOELECTRÓNICAS DE PELÍCULAS DELGADAS DE ÓXIDO DE ZINC PREPARADAS POR RF-SPUTTERING’ TESIS PRESENTADA POR”, 2010.L. M.-A. a, A. G. H.-Z. Alondra S. Mendoza-Villeda, “Caracterización morfológica de nanotubos de ZnO”, TEPEXI Boletín Científico de la Escuela Superior Tepeji del Río, 2020.N. Yanira y B. Sapuyes, “Preparación y caracterización del semiconductor ZnO con impurezas magnéticas”, 2019.L. A. Florez Galvan, “CORRELACIÓN ENTRE LAS PROPIEDADES ESTRUCTURALES Y ÓPTICAS DEL ÓXIDO DE ZINC NANOESTRUCTURADO DOPADO CON COBALTO”, 2020.J. J. Beltrán, C. A. Barrero, y A. Punnoose, “Identifying the sources of ferromagnetism in sol-gel synthesized Zn1−xCoxO (0≤x≤0.10) nanoparticles”, J Solid State Chem, vol. 240, pp. 30–42, ago. 2016, doi: 10.1016/J.JSSC.2016.05.013.Y. Kumar, A. Sahai, S. F. Olive-Méndez, N. Goswami, y V. Agarwal, “Morphological transformations in cobalt doped zinc oxide nanostructures: Effect of doping concentration”, Ceram Int, vol. 42, no 4, pp. 5184–5194, mar. 2016, doi: 10.1016/J.CERAMINT.2015.12.041.V. Gandhi, R. Ganesan, H. Hameed, A. Syedahamed, y M. Thaiyan, “Effect of Cobalt Doping on Structural, Optical, and Magnetic Properties of ZnO Nanoparticles Synthesized by Coprecipitation Method”, 2016.N. M. Basith, J. J. Vijaya, L. J. Kennedy, M. Bououdina, S. Jenefar, y V. Kaviyarasan, “Co-Doped ZnO Nanoparticles: Structural, Morphological, Optical, Magnetic and Antibacterial Studies”, J Mater Sci Technol, vol. 30, no 11, pp. 1108–1117, nov. 2014, doi: 10.1016/J.JMST.2014.07.013.DEISY RAMÍREZ VINASCO y LILIANA PATRICIA VERA L, “PELÍCULAS DELGADAS DE Zn 1-x Mn x O”, 2009.H. fu Zhang, R. jin Liu, H. fa Liu, C. xin Lei, D. tai Feng, y C. K. Yuan, “Mn-doped ZnO transparent conducting films deposited by DC magnetron sputtering”, Mater Lett, vol. 64, no 5, pp. 605–607, mar. 2010, doi: 10.1016/j.matlet.2009.12.015.M. A. Borysiewicz, “ZnO as a Functional Material, a Review”, Crystals, vol. 9, no. 10, p. 505, 2019., 2019, doi: 10.3390/cryst9100505.Dmitry Bokov, Abduladheem Turki Jalil, Supat Chupradit, y Wanich Suksatan, “Nanomaterial by Sol-Gel Method: Synthesis and Application”, Advances in Materials Science and Engineering, 2021.Jesús Herranz Zamorano, “Crecimiento por Epitaxia de Haces Moleculares de puntos cuánticos de InAs sobre GaAs(001) con control en su lugar de formación para su integración en microcavidades ópticas”, Instituto de Microelectrónica de Madrid, 2015.L. Guillermo, A. Gutiérrez, D. C. Constanza, y P. Espinosa, “SÍNTESIS DE PELÍCULAS DELGADAS POR LA TÉCNICA DE MAGNETRÓN SPUTTERING A PARTIR DE BLANCOS DE RENIO Y BORO”, 2017.J. A. Juhasz y S. M. Best, “Surface modification of biomaterials by calcium phosphate deposition”, Surface Modification of Biomaterials: Methods Analysis and Applications, pp. 143–169, ene. 2011, doi: 10.1533/9780857090768.1.143.M. Camino, “Electrodeposición de películas delgadass de ZnO para aplicaciones fotovoltaicas”, 2020. [En línea]. Disponible en: http://rinfi.fi.mdp.edu.arhttp://rinfi.fi.mdp.edu.ar/xmlui/handle/123456789/424C. C. Jorge Arturo, “ESTUDIO DE LAS PROPIEDADES ÓPTICAS Y ELÉCTRICAS DEL COMPUESTO Ga 1-x Mn x Sb USADO PARA APLICACIONES EN ESPINTRÓNICA”, 2016.Recursos para el espectrofotómetro UV-Vis, “Recursos para el espectrofotómetro UV-Vis”, Thermo Fisher Scientific Inc. Accedido: 21 de noviembre de 2023. [En línea]. Disponible en: https://www.thermofisher.com/co/en/home/industrial/spectroscopy-elemental-isotope-analysisJ. Sánchez-González, A. Díaz-Parralejo, A. L. Ortiz, y F. Guiberteau, “Determination of optical properties in nanostructured thin films using the Swanepoel method”, Appl Surf Sci, vol. 252, no 17, pp. 6013–6017, jun. 2006, doi: 10.1016/J.APSUSC.2005.11.009.F. Mesa, V. Ballesteros, y A. Dussan, “Cálculo de constantes ópticas de películas delgadas de Cu3BiS3 a través del método de Wolfe”, Univ Sci (Bogota), vol. 19, no 2, mar. 2014, doi: 10.11144/Javeriana.SC19-2.ccop.S. R. Bhattacharyya, R. N. Gayen, R. Paul, y A. K. Pal, “Determination of optical constants of thin films from transmittance trace”, Thin Solid Films, vol. 517, no 18, pp. 5530–5536, jul. 2009, doi: 10.1016/j.tsf.2009.03.168.M. Nowak, “Thin Solid Films”, 254 (1995) 200.D. Poelman y P. F. Smet, “Methods for the determination of the optical constants of thin films from single transmission measurements: a critical review”, J Phys D Appl Phys, vol. 36, no 15, pp. 1850–1857, ago. 2003, doi: 10.1088/0022-3727/36/15/316.I. O. D. Franta, “Optical characterization of inhomogeneous thin films of ZrO2 by spectroscopic ellipsometry and spectroscopic reflectometry”, Wiley Analytical Science, 2000.Ana Iris Peña Maldonado., “LINAN LABORATORIO NACIONAL DE INVESTIGACIONES EN NANOCIENCIAS Y NANOTECNOLOGÍA IPICYT”.J. Ernesto y V. Cadre, “Microscopía de Fuerza Atómica”, 2020, doi: 10.13140/RG.2.2.17860.24963.E. N. La, C. De Materiales, M. Ipohorski, y P. B. Bozzano, “MICROSCOPÍA ELECTRÓNICA DE BARRIDO”.“Microscópio electrónico escaneando HistoriayPrincipios y Capacidades”, Microscópio electrónico escaneando HistoriayPrincipios y capacidades, https://hmong.es/wiki/Scanning_electron_microscope (accessed 10 December 2023).A. Patricia y L. Díaz, “SÍNTESIS Y ESTUDIO DEL EFECTO DEL Mn SOBRE LAS PROPIEDADES ESTRUCTURALES Y ELÉCTRICAS DE NANOESTRUCTURAS DE ZnO”, 2023.“Microscopía electrónica de barrido de emisión de campo : Servicio de Microscopía Electrónica : UPV”. Accedido: 12 de enero de 2024. [En línea]. Disponible en: https://www.upv.es/entidades/SME/info/859071normalc.html#C. Á. Romero, M. Teresa, y D. Carbó, “APLICACIÓN DE LA TÉCNICA DE MICROSCOPIA ELECTRÓNICA DE BARRIDO DE EMISIÓN DE CAMPO CON HAZ DE IONES FOCALIZADO-MICROANÁLISIS DE RAYOS X A COLECCIONES NUMISMÁTICAS”.B. D. (Bernard D. Cullity, Elements of x-ray diffraction. Addison-Wesley Publishing Company, Inc, 1978.G. F. Harrington y J. Santiso, “Back-to-Basics tutorial: X-ray diffraction of thin films”, J Electroceram, vol. 47, no 4, pp. 141–163, dic. 2021, doi: 10.1007/s10832-021-00263-6.Y. Waseda, E. Matsubara, y K. Shinoda, “X-Ray Diffraction Crystallography”, X-Ray Diffraction Crystallography, 2011, doi: 10.1007/978-3-642-16635-8.U. Nacional, A. De México, M. Luisa, y R. García, “Centro de Investigación en Energía Introducción al Método Rietveld Septiembre de 2007”.V. Esteve, “El método de Rietveld”, 2006, Accedido: 12 de enero de 2024. [En línea]. Disponible en: https://latam.casadellibro.com/libro-el-metodo-rietveld/9788480215756/1133058J. Otero, “Espectroscopía Raman: Fundamento y aplicaciones”, 2015, doi: 10.13140/RG.2.1.5015.5362.A. Carrero, V. Sagredo, C. Pernechele, y J. Larionova, “Propiedades estructurales, ópticas y magnéticas del ZnO: Co preparado por el método sol gel autocombustión”, 2014.José M. Albella, Capas delgadas y modificación superficial de materiales. 2018.T. MARIA FERNANDEZ NAVARRO Doctor en Ciencias Químicas, “Nucleación y cristalización en vidrios”.“Shalimova_K_V_Fisica_De_Los_Semiconducto”, Editorial MIR MOSCU, 1975.P. Makuła, M. Pacia, y W. Macyk, “How To Correctly Determine the Band Gap Energy of Modified Semiconductor Photocatalysts Based on UV-Vis Spectra”, 6 de diciembre de 2018, American Chemical Society. doi: 10.1021/acs.jpclett.8b02892.Gerardo García Naumis, “Nuevas tecnologías que surgen del desorden: LOS MATERIALES AMORFOS”, 2003.I. C. R. H. P. P. Oslen Dilayder Jaimes, “Correlation Method in a ZnO Crystal”, Ciencia en Desarrollo, Vol. 9 No. 2, 2018.Marcel Schumm, “ZnO-based semiconductors studied by Raman spectroscopy: semimagnetic alloying, doping, and nanostructures”, 2008.“Nanopartículas de Óxido de Zinc Dopadas con Co, Cr, Fe, Mn y Ni. Propiedades Y Aplicación En La Degradación Fotocatalítica De Compuestos Orgánicos Contaminantes”. Accedido: 27 de enero de 2024. [En línea]. Disponible en: https://repositorio.unal.edu.co/handle/unal/83694M. I. Medina-Montes et al., “Physical properties of photoconductive Ag-Sb-S thin films prepared by thermal evaporation”, Mater Sci Semicond Process, vol. 137, p. 106167, ene. 2022, doi: 10.1016/J.MSSP.2021.106167.E. M. García Martínez, “Aplicación de la ley de Lambert-Beer en espectroscopía UV-visible”, jun. 2012, Accedido: 22 de julio de 2024. [En línea]. Disponible en: https://riunet.upv.es:443/handle/10251/16360“Microscopio de Fuerza Atómica (ATM)”. Accedido: 3 de enero de 2024. [En línea]. Disponible en: http://www.linan-ipicyt.mx/Microscopio_de_Fuerza_Atomica.htmlB. J. Inkson, “Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) for materials characterization”, Materials Characterization Using Nondestructive Evaluation (NDE) Methods, pp. 17–43, ene. 2016, doi: 10.1016/B978-0-08-100040-3.00002-X.“The Raman Spectrophotometer”. Accedido: 12 de enero de 2024. [En línea]. Disponible en: https://www.sas.upenn.edu/~crulli/TheRamanSpectrophotometer.htmlPúblico generalLICENSElicense.txtlicense.txttext/plain; charset=utf-85879https://repositorio.unal.edu.co/bitstream/unal/86922/1/license.txteb34b1cf90b7e1103fc9dfd26be24b4aMD51ORIGINAL1016054985.2024.pdf1016054985.2024.pdfTrabajo de Maestría en Ciencias Físicaapplication/pdf4155788https://repositorio.unal.edu.co/bitstream/unal/86922/2/1016054985.2024.pdfc865b7cc5c00fd13214377a95c48f922MD52THUMBNAIL1016054985.2024.pdf.jpg1016054985.2024.pdf.jpgGenerated Thumbnailimage/jpeg5189https://repositorio.unal.edu.co/bitstream/unal/86922/3/1016054985.2024.pdf.jpgb0432bbbead1054b2769f66448d17ba2MD53unal/86922oai:repositorio.unal.edu.co:unal/869222024-10-10 00:18:39.458Repositorio Institucional Universidad Nacional de Colombiarepositorio_nal@unal.edu.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

Publicaciones similares