Thermistor formation using batio3 powders synthesised by the pechini method
Barium titanate (BaTiO3) is a compound of interest in the field of electroceramics which is widely used in the manufacture of capacitors, piezoelectric transducers and resistive devices having a positive temperature coefficient (PTCR) and in manu- facturing pyroelectric and optoelectronic devices. M...
- Autores:
-
Fernández Perdomo, Claudia P.
Rodríguez Páez, Jorge E.
- Tipo de recurso:
- Article of journal
- Fecha de publicación:
- 2010
- Institución:
- Universidad Nacional de Colombia
- Repositorio:
- Universidad Nacional de Colombia
- Idioma:
- spa
- OAI Identifier:
- oai:repositorio.unal.edu.co:unal/29661
- Acceso en línea:
- https://repositorio.unal.edu.co/handle/unal/29661
http://bdigital.unal.edu.co/19709/
http://bdigital.unal.edu.co/19709/2/
http://bdigital.unal.edu.co/19709/3/
- Palabra clave:
- BaTiO3
caracterización eléctrica
Pechini
síntesis
termistor
BaTiO3
electrical characterisation
Pechini
synthe- sis
thermistor
- Rights
- openAccess
- License
- Atribución-NoComercial 4.0 Internacional
| id |
UNACIONAL2_b38b24920bfb59ce9e86d2de01add673 |
|---|---|
| oai_identifier_str |
oai:repositorio.unal.edu.co:unal/29661 |
| network_acronym_str |
UNACIONAL2 |
| network_name_str |
Universidad Nacional de Colombia |
| repository_id_str |
|
| dc.title.spa.fl_str_mv |
Thermistor formation using batio3 powders synthesised by the pechini method |
| title |
Thermistor formation using batio3 powders synthesised by the pechini method |
| spellingShingle |
Thermistor formation using batio3 powders synthesised by the pechini method BaTiO3 caracterización eléctrica Pechini síntesis termistor BaTiO3 electrical characterisation Pechini synthe- sis thermistor |
| title_short |
Thermistor formation using batio3 powders synthesised by the pechini method |
| title_full |
Thermistor formation using batio3 powders synthesised by the pechini method |
| title_fullStr |
Thermistor formation using batio3 powders synthesised by the pechini method |
| title_full_unstemmed |
Thermistor formation using batio3 powders synthesised by the pechini method |
| title_sort |
Thermistor formation using batio3 powders synthesised by the pechini method |
| dc.creator.fl_str_mv |
Fernández Perdomo, Claudia P. Rodríguez Páez, Jorge E. |
| dc.contributor.author.spa.fl_str_mv |
Fernández Perdomo, Claudia P. Rodríguez Páez, Jorge E. |
| dc.subject.proposal.spa.fl_str_mv |
BaTiO3 caracterización eléctrica Pechini síntesis termistor BaTiO3 electrical characterisation Pechini synthe- sis thermistor |
| topic |
BaTiO3 caracterización eléctrica Pechini síntesis termistor BaTiO3 electrical characterisation Pechini synthe- sis thermistor |
| description |
Barium titanate (BaTiO3) is a compound of interest in the field of electroceramics which is widely used in the manufacture of capacitors, piezoelectric transducers and resistive devices having a positive temperature coefficient (PTCR) and in manu- facturing pyroelectric and optoelectronic devices. Most of these devices are obtained by consolidating high purity, suitable sized particle ceramic powders; structured synthesis methods are required to ensure such requirements. BaTiO3 powders were synthesised by a polymeric precursor method (Pechini) in this work. Very pure, small particle sized, raw material was obtained. These powders were characterised using thermo- gravimetric and differential thermal analysis (TGDT), X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The results indicated that samples treated at 650°C presented cubic BaTiO3 as unique crystalline phase. If a sample were treated at 1,100°C, the tetragonal phase having a c/a |
| publishDate |
2010 |
| dc.date.issued.spa.fl_str_mv |
2010 |
| dc.date.accessioned.spa.fl_str_mv |
2019-06-26T13:43:53Z |
| dc.date.available.spa.fl_str_mv |
2019-06-26T13:43:53Z |
| dc.type.spa.fl_str_mv |
Artículo de revista |
| dc.type.coar.fl_str_mv |
http://purl.org/coar/resource_type/c_2df8fbb1 |
| dc.type.driver.spa.fl_str_mv |
info:eu-repo/semantics/article |
| dc.type.version.spa.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
| dc.type.coar.spa.fl_str_mv |
http://purl.org/coar/resource_type/c_6501 |
| dc.type.coarversion.spa.fl_str_mv |
http://purl.org/coar/version/c_970fb48d4fbd8a85 |
| dc.type.content.spa.fl_str_mv |
Text |
| dc.type.redcol.spa.fl_str_mv |
http://purl.org/redcol/resource_type/ART |
| format |
http://purl.org/coar/resource_type/c_6501 |
| status_str |
publishedVersion |
| dc.identifier.uri.none.fl_str_mv |
https://repositorio.unal.edu.co/handle/unal/29661 |
| dc.identifier.eprints.spa.fl_str_mv |
http://bdigital.unal.edu.co/19709/ http://bdigital.unal.edu.co/19709/2/ http://bdigital.unal.edu.co/19709/3/ |
| url |
https://repositorio.unal.edu.co/handle/unal/29661 http://bdigital.unal.edu.co/19709/ http://bdigital.unal.edu.co/19709/2/ http://bdigital.unal.edu.co/19709/3/ |
| dc.language.iso.spa.fl_str_mv |
spa |
| language |
spa |
| dc.relation.spa.fl_str_mv |
http://revistas.unal.edu.co/index.php/ingeinv/article/view/15745 |
| dc.relation.ispartof.spa.fl_str_mv |
Universidad Nacional de Colombia Revistas electrónicas UN Ingeniería e Investigación Ingeniería e Investigación |
| dc.relation.ispartofseries.none.fl_str_mv |
Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 2248-8723 0120-5609 |
| dc.relation.references.spa.fl_str_mv |
Fernández Perdomo, Claudia P. and Rodríguez Páez, Jorge E. (2010) Thermistor formation using batio3 powders synthesised by the pechini method. Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 2248-8723 0120-5609 . |
| dc.rights.spa.fl_str_mv |
Derechos reservados - Universidad Nacional de Colombia |
| dc.rights.coar.fl_str_mv |
http://purl.org/coar/access_right/c_abf2 |
| dc.rights.license.spa.fl_str_mv |
Atribución-NoComercial 4.0 Internacional |
| dc.rights.uri.spa.fl_str_mv |
http://creativecommons.org/licenses/by-nc/4.0/ |
| dc.rights.accessrights.spa.fl_str_mv |
info:eu-repo/semantics/openAccess |
| rights_invalid_str_mv |
Atribución-NoComercial 4.0 Internacional Derechos reservados - Universidad Nacional de Colombia http://creativecommons.org/licenses/by-nc/4.0/ http://purl.org/coar/access_right/c_abf2 |
| eu_rights_str_mv |
openAccess |
| dc.format.mimetype.spa.fl_str_mv |
application/pdf |
| dc.publisher.spa.fl_str_mv |
Universidad Nacional de Colombia - Facultad de Ingeniería |
| institution |
Universidad Nacional de Colombia |
| bitstream.url.fl_str_mv |
https://repositorio.unal.edu.co/bitstream/unal/29661/1/15745-48382-1-PB.pdf https://repositorio.unal.edu.co/bitstream/unal/29661/2/15745-48382-1-PB.pdf.jpg |
| bitstream.checksum.fl_str_mv |
e057d48a7cc0869d079b88fc12a21b88 38bce88bc7c80b770d88563ba68ec1e3 |
| bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
| repository.name.fl_str_mv |
Repositorio Institucional Universidad Nacional de Colombia |
| repository.mail.fl_str_mv |
repositorio_nal@unal.edu.co |
| _version_ |
1814089877643329536 |
| spelling |
Atribución-NoComercial 4.0 InternacionalDerechos reservados - Universidad Nacional de Colombiahttp://creativecommons.org/licenses/by-nc/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Fernández Perdomo, Claudia P.75332ee2-14d6-4e5a-980b-720cdc0e3fee300Rodríguez Páez, Jorge E.5f847774-60db-47c6-a545-3a33e5ac99963002019-06-26T13:43:53Z2019-06-26T13:43:53Z2010https://repositorio.unal.edu.co/handle/unal/29661http://bdigital.unal.edu.co/19709/http://bdigital.unal.edu.co/19709/2/http://bdigital.unal.edu.co/19709/3/Barium titanate (BaTiO3) is a compound of interest in the field of electroceramics which is widely used in the manufacture of capacitors, piezoelectric transducers and resistive devices having a positive temperature coefficient (PTCR) and in manu- facturing pyroelectric and optoelectronic devices. Most of these devices are obtained by consolidating high purity, suitable sized particle ceramic powders; structured synthesis methods are required to ensure such requirements. BaTiO3 powders were synthesised by a polymeric precursor method (Pechini) in this work. Very pure, small particle sized, raw material was obtained. These powders were characterised using thermo- gravimetric and differential thermal analysis (TGDT), X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The results indicated that samples treated at 650°C presented cubic BaTiO3 as unique crystalline phase. If a sample were treated at 1,100°C, the tetragonal phase having a c/aEl titanato de bario, BaTiO3, es un compuesto de gran interés en el ámbito de la electrocerámica, ya que se utiliza en la fabricación de condensadores, transductores piezoeléctricos y dispositivos resistivos con coeficiente positivo de temperatura (PTCR), así como en la manufactura de piroeléctricos y dispositivos optoelectrónicos, entre otros dispositivos. La mayoría de estos componentes son conformados con polvos cerámicos de elevada pureza y tamaño de partícula adecuado. Esto exige estructurar métodos de síntesis que garanticen es- tos requerimientos. En este trabajo se sintetizaron polvos cerámicos de BaTiO3 por el método de precursor polimérico (Pechini), obteniéndose una materia prima muy pura y con pequeño tamaño de partícula. Los polvos obtenidos se caracterizaron utilizando análisis térmico (ATD/TG), difracción de rayos X (DRX) y calorimetría diferencial de barrido (DSC). Los resultados indican que en las muestras tratadas a 650 °C la única fase cristalina presente es el BaTiO3 cúbico y a 1.100 °C la tetragonal, con una relación c/a and lt; 1.007. Las muestras tratadas a 1.100 °C presentaron una transición ferroeléctrica a paraeléctrica a una temperatura de T ≈ 123 °C. Los polvos cerámicos de BaTiO3 tetragonal fueron prensados uniaxialmente y posteriormente sinterizados a 1.200 °C durante 2 horas. Estas muestras se caracterizaron eléctricamente, obteniéndose curvas de resistencia eléctrica en función de la temperatura (R-T), evidenciándose en ellas su comportamiento termistor tipo PTCR. Además, se midió la variación de la corriente-voltaje (I-V) a diferentes temperaturas.application/pdfspaUniversidad Nacional de Colombia - Facultad de Ingenieríahttp://revistas.unal.edu.co/index.php/ingeinv/article/view/15745Universidad Nacional de Colombia Revistas electrónicas UN Ingeniería e InvestigaciónIngeniería e InvestigaciónIngeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 2248-8723 0120-5609Fernández Perdomo, Claudia P. and Rodríguez Páez, Jorge E. (2010) Thermistor formation using batio3 powders synthesised by the pechini method. Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 Ingeniería e Investigación; Vol. 30, núm. 2 (2010); 147-156 2248-8723 0120-5609 .Thermistor formation using batio3 powders synthesised by the pechini methodArtículo de revistainfo:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501http://purl.org/coar/resource_type/c_2df8fbb1http://purl.org/coar/version/c_970fb48d4fbd8a85Texthttp://purl.org/redcol/resource_type/ARTBaTiO3caracterización eléctricaPechinisíntesistermistorBaTiO3electrical characterisationPechinisynthe- sisthermistorORIGINAL15745-48382-1-PB.pdfapplication/pdf624875https://repositorio.unal.edu.co/bitstream/unal/29661/1/15745-48382-1-PB.pdfe057d48a7cc0869d079b88fc12a21b88MD51THUMBNAIL15745-48382-1-PB.pdf.jpg15745-48382-1-PB.pdf.jpgGenerated Thumbnailimage/jpeg9222https://repositorio.unal.edu.co/bitstream/unal/29661/2/15745-48382-1-PB.pdf.jpg38bce88bc7c80b770d88563ba68ec1e3MD52unal/29661oai:repositorio.unal.edu.co:unal/296612022-11-22 23:04:35.654Repositorio Institucional Universidad Nacional de Colombiarepositorio_nal@unal.edu.co |