Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60
ilustraciones, diagramas
- Autores:
-
Rua Patiño, Robinson Fernando
- Tipo de recurso:
- Fecha de publicación:
- 2023
- Institución:
- Universidad Nacional de Colombia
- Repositorio:
- Universidad Nacional de Colombia
- Idioma:
- spa
- OAI Identifier:
- oai:repositorio.unal.edu.co:unal/84961
- Palabra clave:
- 620 - Ingeniería y operaciones afines
690 - Construcción de edificios::691 - Materiales de construcción
Materiales de construcción
Building materials
Adherencia
Ensayo mecánico de arrancamiento
Cementos activados alcalinamente
Ceniza volante de carbón
Micro-concreto activado alcalinamente
Bond, Mechanical pull-out test
Alkaline activated cements
Carbon fly ash
Alkaline-activated micro-concrete
- Rights
- openAccess
- License
- Atribución-NoComercial 4.0 Internacional
| id |
UNACIONAL2_99e4df19a93724582518adbf908c957a |
|---|---|
| oai_identifier_str |
oai:repositorio.unal.edu.co:unal/84961 |
| network_acronym_str |
UNACIONAL2 |
| network_name_str |
Universidad Nacional de Colombia |
| repository_id_str |
|
| dc.title.spa.fl_str_mv |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| dc.title.translated.eng.fl_str_mv |
Evaluation of the adhesion between an alkaline activated concrete based on coal fly ash and grade 60 reinforcing steel |
| title |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| spellingShingle |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 620 - Ingeniería y operaciones afines 690 - Construcción de edificios::691 - Materiales de construcción Materiales de construcción Building materials Adherencia Ensayo mecánico de arrancamiento Cementos activados alcalinamente Ceniza volante de carbón Micro-concreto activado alcalinamente Bond, Mechanical pull-out test Alkaline activated cements Carbon fly ash Alkaline-activated micro-concrete |
| title_short |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| title_full |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| title_fullStr |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| title_full_unstemmed |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| title_sort |
Evaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60 |
| dc.creator.fl_str_mv |
Rua Patiño, Robinson Fernando |
| dc.contributor.advisor.none.fl_str_mv |
Hoyos Montilla, Ary Alain Tobón, Jorge Iván |
| dc.contributor.author.none.fl_str_mv |
Rua Patiño, Robinson Fernando |
| dc.contributor.researchgroup.spa.fl_str_mv |
Grupo del Cemento y Materiales de Construcción |
| dc.contributor.orcid.spa.fl_str_mv |
Rua Patiño, Robinson Fernando [0000-0003-0431-8625] |
| dc.contributor.cvlac.spa.fl_str_mv |
Rua Patiño, Robinson Fernando [0001595541] |
| dc.subject.ddc.spa.fl_str_mv |
620 - Ingeniería y operaciones afines 690 - Construcción de edificios::691 - Materiales de construcción |
| topic |
620 - Ingeniería y operaciones afines 690 - Construcción de edificios::691 - Materiales de construcción Materiales de construcción Building materials Adherencia Ensayo mecánico de arrancamiento Cementos activados alcalinamente Ceniza volante de carbón Micro-concreto activado alcalinamente Bond, Mechanical pull-out test Alkaline activated cements Carbon fly ash Alkaline-activated micro-concrete |
| dc.subject.lemb.spa.fl_str_mv |
Materiales de construcción |
| dc.subject.lemb.eng.fl_str_mv |
Building materials |
| dc.subject.proposal.spa.fl_str_mv |
Adherencia Ensayo mecánico de arrancamiento Cementos activados alcalinamente Ceniza volante de carbón Micro-concreto activado alcalinamente |
| dc.subject.proposal.eng.fl_str_mv |
Bond, Mechanical pull-out test Alkaline activated cements Carbon fly ash Alkaline-activated micro-concrete |
| description |
ilustraciones, diagramas |
| publishDate |
2023 |
| dc.date.accessioned.none.fl_str_mv |
2023-11-27T14:06:21Z |
| dc.date.available.none.fl_str_mv |
2023-11-27T14:06:21Z |
| dc.date.issued.none.fl_str_mv |
2024 |
| dc.type.spa.fl_str_mv |
Trabajo de grado - Maestría |
| dc.type.driver.spa.fl_str_mv |
info:eu-repo/semantics/masterThesis |
| dc.type.version.spa.fl_str_mv |
info:eu-repo/semantics/acceptedVersion |
| dc.type.content.spa.fl_str_mv |
Text |
| dc.type.redcol.spa.fl_str_mv |
http://purl.org/redcol/resource_type/TM |
| status_str |
acceptedVersion |
| dc.identifier.uri.none.fl_str_mv |
https://repositorio.unal.edu.co/handle/unal/84961 |
| dc.identifier.instname.spa.fl_str_mv |
Universidad Nacional de Colombia |
| dc.identifier.reponame.spa.fl_str_mv |
Repositorio Institucional Universidad Nacional de Colombia |
| dc.identifier.repourl.spa.fl_str_mv |
https://repositorio.unal.edu.co/ |
| url |
https://repositorio.unal.edu.co/handle/unal/84961 https://repositorio.unal.edu.co/ |
| identifier_str_mv |
Universidad Nacional de Colombia Repositorio Institucional Universidad Nacional de Colombia |
| dc.language.iso.spa.fl_str_mv |
spa |
| language |
spa |
| dc.relation.indexed.spa.fl_str_mv |
RedCol LaReferencia |
| dc.relation.references.spa.fl_str_mv |
G. P. Gambarova P. G., Rosati, “Bond and splitting in bar pull-out: behavioural laws. Magazine of Concrete Research,” . Mag. Concr. Res., vol. 49, no. 179, pp. 99–110, 1997. M. J. A. Mijarsh, M. A. Megat Johari, and Z. A. Ahmad, “Compressive strength of treated palm oil fuel ash based geopolymer mortar containing calcium hydroxide, aluminum hydroxide and silica fume as mineral additives,” Cem. Concr. Compos., vol. 60, pp. 65–81, Jul. 2015. T. Xie, P. Visintin, X. Zhao, and R. Gravina, “Mix design and mechanical properties of geopolymer and alkali activated concrete: Review of the state-of-the-art and the development of a new unified approach,” Constr. Build. Mater., vol. 256, p. 119380, 2020. F. Guo, J. Pei, J. Zhang, B. Xue, G. Sun, and R. Li, “Study on the adhesion property between asphalt binder and aggregate: A state-of-the-art review,” Constr. Build. Mater., vol. 256, p. 119474, 2020. A. Alain, “Evolución de la reacción y estructura del sistema portlandita - ceniza volante de carbón activado alcalinamente,” p. 155, 2018. G. Metelli and G. A. Plizzari, “Influence of the relative rib area on bond behaviour,” Mag. Concr. Res., vol. 66, no. 6, pp. 277–294, 2014. M. M. Huelva, “propuesta de un modelo de evaluación estruct ...,” no. January 2005, 2015. D. L. L. Segrera, J. Oliver, and A. E. Huespe, “Simulación numérica del proceso de fractura en concreto reforzado mediante la metodología de discontinuidades fuertes de continuo. Parte II: Aplicación a páneles sometidos a cortante,” Ing. e Investig., vol. 30, no. 3, pp. 16–26, 2010. L. P. Güereca, “Evaluación comparativa de los impactos ambientales de la producción de clínker con combustible fósil frente a combustible derivado de los residuos municipales,” Gac. del Inst. Ing., pp. 2010–2013, 2013. IDEAM, Y Departamental De Gases Efecto Invernadero - De Gases Efecto. 2016. M. Morales, “Universidad San Pedro Filial - Sullana,” p. 80, 2018. J. Ignacio and D. Orso, “LAS MEZCLAS DE CONCRETO HIDRÁULICO CON ADITIVOS INCLUSORES DE AIRE ‘CENIZAS VOLANTES,’” 2016. A. Castel and S. J. Foster, “Bond strength between blended slag and Class F fly ash geopolymer concrete with steel reinforcement,” Cem. Concr. Res., vol. 72, pp. 48–53, 2015. G. Xu and X. Shi, “Characteristics and applications of fly ash as a sustainable construction material: A state-of-the-art review,” Resour. Conserv. Recycl., vol. 136, no. April, pp. 95–109, 2018. American Society for Testing and Materials, “ASTM C136-14_Método de prueba estándar para la determinación granulométrica de agregados finos y gruesos,” Annu. B. ASTM Stand., pp. 3–7, 2014. P. Lorca Aranda, “‘Efecto de la Adición de Hidróxido Cálcico sobre Mezclas con Alta Sustitución de Cemento por Ceniza Volante,’” 2015. A. Hassan, M. Arif, and M. Shariq, “Use of geopolymer concrete for a cleaner and sustainable environment – A review of mechanical properties and microstructure,” J. Clean. Prod., vol. 223, pp. 704–728, 2019. N. Dominguez Ramirez, “La adherencia en el concreto reforzado : breve revisión histórica de la investigación del fenómeno Steel-concrete bonding phenomenon : a brief review of the phenomenon ’ s research,” Investig. y Ciencia21, vol. 21, pp. 61–72, 2013. V. Bilek, S. Bonczková, J. Hurta, D. Pytlík, and M. Mrovec, “Bond Strength between Reinforcing Steel and Different Types of Concrete,” Procedia Eng., vol. 190, pp. 243–247, 2017. M. Molina, J. P. Gutiérrez, and M. D. García, “Influencia del diámetro de la barra y del recubrimiento en las características adherentes del hormigón armado,” Bol. la Soc. Esp. Ceram. y Vidr., vol. 43, no. 2, pp. 560–564, 2004. D. Hardjito, S. E. Wallah, D. M. J. Sumajouw, and B. V. Rangan, “On the development of fly ash-based geopolymer concrete,” ACI Mater. J., vol. 101, no. 6, pp. 467–472, 2004. A. Hassan, M. Arif, and M. Shariq, “A review of properties and behaviour of reinforced geopolymer concrete structural elements- A clean technology option for sustainable development,” J. Clean. Prod., vol. 245, 2020. L. Lemnitzer, S. Schröder, A. Lindorf, and M. Curbach, “Bond behaviour between reinforcing steel and concrete under multiaxial loading conditions in concrete containments,” React. Technol., no. SMiRT 20, pp. 1–12, 2009. G. REHM, “No TitleThe fundamental law of bond,” in Proceedings of the Symposium on Bond and Crack Formation in Reinforced Concrete, Stockholm, 1958. G. REHM, The basic principle of bond between steel and concrete., Deustcher. Biblioteca C&CA, 1968. LUTZ, L. A., GERGELY, P., WINTER, G., “No TitleThe mechanics of bond and slip of deformed reinforcing bars in concrete.,” Struct. Eng. Rep., vol. 324, 1966. M. M. Huelva, “Propuesta De Un Modelo De Evaluación Estruct ...,” no. January 2005, 2015. Tepfers, “TepfersDrThesis,” A BONUS THEORY Appl. TO SUPERPOSED Tens. Reinf. POWER Deform. BARS, p. 330, 1973. R. Eligehausen, E. P. Popov, and V. V. Bertéro, “Local bond stress-slip relationship of ribbed bars under generalized excitations,” 1979. V. V. ELIGEHAUSEN, R., POPOV, E. P. BERTERO, “Local bond stress-slip relationships of deformed bars under generalized excitations,” Univ. Calif., vol. UCB/EERC-8, 1983. V. González Fernández, Á. Barrios-Padura, and M. Molina-Huelva, “Aplicaciones de las técnicas no destructivas Pull-Off y ultrasonidos en el control de calidad del refuerzo con materiales compuestos en estructuras de concreto,” Cienc. e Ing. Neogranadina, vol. 28, no. 1, pp. 5–26, Mar. 2018. R. EliGEHAUSEN, E. P. POPOV, and Vite. V. BERTERO, “CONICET_Digital_Nro.16669,” LOCAL Bond Stress. RELATIONSHIPS Deform. BARS UNDER Gen. Excit., p. 180. R. Tepfers and P.-A. Olsson, “Ring test for evaluation of bond properties of reinforcing bars,” Bond Concr. - From Res. to Pract. Riga, Latv., vol. 1, pp. 89–99, 1992. R. Eligehausen, E. P. Popov, and V. V. Bertero, “Local Bond Stress-Slip Relationships of Deformed Bars Under Generalized Excitations.,” vol. 4, pp. 69–80, 1982. P. LUTZ, L. A., GERGELY, “Mechanics of bond and slip of deformed bars in concrete,” ACI Struct. J., vol. 64 (11), pp. 711–721, 1967. GOTO, “Cracks formed in concrete around tension bars,” ACI J., vol. 68(4), pp. 244–251, 1971. M. Raous and M. A. Karray, “Model coupling friction and adhesion for steel-concrete interfaces,” Int. J. Comput. Appl. Technol., vol. 34, no. 1, pp. 42–51, 2009. M. A. Eyre J. R., Nokhasteh, “Strength assessment of corrosion damaged reinforced concrete slabs and beams.,” Proc. Inst. Civ. Eng. Struct. Build., vol. 94, pp. 197-203., 1992. Z. P. Bažant, Z. Li, and M. Thoma, “Identification of stress-slip law for bar or fiber pullout by size effect tests,” J. Eng. Mech., vol. 121, no. 5, pp. 620–625, 1995. C. J., “Alternative strategies for temporary support during structural repair of reinforced-concrete beams.,” J. Struct. Eng., vol. 122, pp. 238–246, 1996. L. Z. Raoof M., “Structural characteristics of RC beams with exposed main steel,” Proc. Inst. Civ. Eng., vol. 122, pp. 35–51, 1996. K. LUNDGREN, “Three-dimensional modelling of bond in reinforced concrete,” University of Technology, 1999. K. LUNDGREN, “Pull-out tests of steel-encased speci-mens subjected to reversed cyclic loading,” Mater. Struct., 2000. D. ZUO, J., DARWIN, “Bond slip of high relative rib area bars under cyclic loading.,” ACI Struct. J., vol. 97(2), pp. 331–334, 2000. G. L. KOCH, R. G., BALAZS, “Limit states for long term and cyclic loading. ‘Bond in concrete,’” Conf. held Budapest Univ. Techno logy Econ., vol. 211, pp. 220, 2002, 2002. B. H. Oh, O. C. Choi, L. Chung, and Korea Concrete Institute., Fracture mechanics of concrete and concrete structures : proceedings of the 7th International Conference on Fracture Mechanics of Concrete and Concrete Structures, Jeju, Korea, May 23-28, 2010. M. Molina, J. P. Gutiérrez, and M. D. García, “Influencia del diámetro de la barra y del recubrimiento en las características adherentes del hormigón armado,” in Boletin de la Sociedad Espanola de Ceramica y Vidrio, 2004, vol. 43, no. 2, pp. 560–564. S. Hong and S. K. Park, “Uniaxial bond stress-slip relationship of reinforcing bars in concrete,” Adv. Mater. Sci. Eng., vol. 2012, 2012. P. K. Sarker, “Bond strength of reinforcing steel embedded in fly ash-based geopolymer concrete,” Mater. Struct. Constr., vol. 44, no. 5, pp. 1021–1030, 2011. H. Costa, “La unión entre el hormigón alcalino activado y del Acero,” 2014. H. Y. Zhang, V. Kodur, B. Wu, J. Yan, and Z. S. Yuan, “Effect of temperature on bond characteristics of geopolymer concrete,” Constr. Build. Mater., vol. 163, pp. 277–285, 2018. S. Steel and R. Alloys, “Standard Specification for Deformed and Plain Low-Alloy Steel Bars for Concrete,” pp. 1–7, 2014. Astm, “Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use,” Annu. B. ASTM Stand., no. C, pp. 3–6, 2010. A. Guriérrez Torres, “Obtención Y Caracterización De Geopolímeros Sintetizados a Partir De La Escoria Granulada De Alto Horno Como Uso Alternativo Del Cemento Portland,” p. 258, 2017. J. Of, S. Engineering, and M. Sciences, “Advanced Search http://ascelibrary.aip.org/vsearch/servlet/VerityServlet?KEY=JSEN...,” vol. 9445, no. August, p. 2007, 2007 B. V. Silva, M. P. Barbosa, L. C. P. Silva Filho, and M. S. Lorrain, “Experimental investigation on the use of steel-concrete bond tests for estimating axial compressive strength of concrete. Part 2: APULOT,” Rev. IBRACON Estruturas e Mater., vol. 7, no. 5, pp. 856–878, 2014. ASTM, “Standard test method for pullout strenght of hardened concrete ASTM C 900,” Am. Soc. Test. Mater., no. 1, pp. 1–10, 2013. K. S. Kotova and G. S. Slavcheva, “Composite materials cohesion parameters,” IOP Conf. Ser. Mater. Sci. Eng., vol. 489, no. 1, 2019. A 615/A 615M – 12, “Standard Specification for Deformed and Plain Carbon-Steel Bars for Concrete Reinforcement,” Astm, p. 6, 2012. ASTM International, “Astm C188-17,” Annu. B. ASTM Stand., pp. 1–3, 2017. C204-18, “Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability,” ASTM Int., pp. 1–11, 2019. ASTM, “ASTM: Standard Test Method for Ash in the Analysis Sample of Coal and Coke from Coal 1,” ASTM Int., vol. 05, no. Reapproved 2018, pp. 1–6, 2002. ASTM, “Standard Test Method for Compressive Strength of Hydraulic Cement Mortars ( Using 2-in . or [ 50-mm ] Cube Specimens ) 1,” Chem. Anal., vol. 04, no. C109/C109M – 11b, pp. 1–9, 2010. American Society for Testing and Materials (ASTM), “Standard Test Method for Pullout Strength of Hardened Concrete 1,” Astm C900, no. 5, pp. 1–10, 2015. A. Mu, “ANÁLISIS DE LA RESISTENCIA A LA COMPRESIÓN F´c DEL CONCRETO HIDRÁULICO ADICIONADO CON SILICATO DE SODIO, MEDIANTE ENSAYOS DE MADUREZ Y RESISTENCIA A LA COMPRESIÓN.,” J. Chem. Inf. Model., vol. 53, no. 9, pp. 1689–1699, 2019. American Society for Testing and Materials International, “American Society for Testing and Materials. ASTM C128: Standard Test Method for Relative Density (Specific Gravity) and Absorption of Fine Aggregate,” ASTM Int., vol. i, p. 6, 2015. Astm:C29/C29M-09, “Standard Test Method for Bulk Density (‘ Unit Weight ’) and Voids in Aggregate,” ASTM Int., vol. i, no. c, pp. 1–5, 2009. ASTM, “ASTM C566-19_Standard Test Method for Total Evaporable Moisture Content of Aggregate by Drying,” Annu. B. ASTM Stand., pp. 5–7, 2019. ASTM C143/C143M, “Standard Test Method for Slump of Hydraulic-Cement Concrete,” Astm C143, no. 1, pp. 1–4, 2015. G. Guevara Fallas, C. Hidalgo Madrigal, M. Pizarro García, I. Rodríguez Valenciano, L. D. Rojas Vega, and G. Segura Guzmán, “Efecto de la variación agua/cemento en el concreto,” Rev. Tecnol. en Marcha, vol. 25, no. 2, p. 80, 2012. |
| dc.rights.coar.fl_str_mv |
http://purl.org/coar/access_right/c_abf2 |
| dc.rights.license.spa.fl_str_mv |
Atribución-NoComercial 4.0 Internacional |
| dc.rights.uri.spa.fl_str_mv |
http://creativecommons.org/licenses/by-nc/4.0/ |
| dc.rights.accessrights.spa.fl_str_mv |
info:eu-repo/semantics/openAccess |
| rights_invalid_str_mv |
Atribución-NoComercial 4.0 Internacional http://creativecommons.org/licenses/by-nc/4.0/ http://purl.org/coar/access_right/c_abf2 |
| eu_rights_str_mv |
openAccess |
| dc.format.extent.spa.fl_str_mv |
xv, 72 página |
| dc.format.mimetype.spa.fl_str_mv |
application/pdf |
| dc.coverage.country.none.fl_str_mv |
Colombia |
| dc.publisher.spa.fl_str_mv |
Universidad Nacional de Colombia |
| dc.publisher.program.spa.fl_str_mv |
Medellín - Minas - Maestría en Ingeniería - Materiales y Procesos |
| dc.publisher.faculty.spa.fl_str_mv |
Facultad de Minas |
| dc.publisher.place.spa.fl_str_mv |
Medellín, Colombia |
| dc.publisher.branch.spa.fl_str_mv |
Universidad Nacional de Colombia - Sede Medellín |
| institution |
Universidad Nacional de Colombia |
| bitstream.url.fl_str_mv |
https://repositorio.unal.edu.co/bitstream/unal/84961/1/license.txt https://repositorio.unal.edu.co/bitstream/unal/84961/3/1128390648.2020.pdf.jpg https://repositorio.unal.edu.co/bitstream/unal/84961/5/Tesis%20MSc%20Robinson%20Fernando%20Rua%20P..pdf.jpg https://repositorio.unal.edu.co/bitstream/unal/84961/4/Tesis%20MSc%20Robinson%20Fernando%20Rua%20P..pdf |
| bitstream.checksum.fl_str_mv |
eb34b1cf90b7e1103fc9dfd26be24b4a 24f4242b7b2fe528f39481d45de94f23 3f50cc45af8dcec46548c88fdef369f3 35f39fd9f8064d1f7d080f2537e0a7b9 |
| bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
| repository.name.fl_str_mv |
Repositorio Institucional Universidad Nacional de Colombia |
| repository.mail.fl_str_mv |
repositorio_nal@unal.edu.co |
| _version_ |
1814089690584711168 |
| spelling |
Atribución-NoComercial 4.0 Internacionalhttp://creativecommons.org/licenses/by-nc/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Hoyos Montilla, Ary Alainb7077a3e748a382421838b2d05c04feaTobón, Jorge Ivánbfb9bdf72e2b2fed1fb614b88d646838Rua Patiño, Robinson Fernando5d7f065bc705e8dabe8b72fe90e28195Grupo del Cemento y Materiales de ConstrucciónRua Patiño, Robinson Fernando [0000-0003-0431-8625]Rua Patiño, Robinson Fernando [0001595541]2023-11-27T14:06:21Z2023-11-27T14:06:21Z2024https://repositorio.unal.edu.co/handle/unal/84961Universidad Nacional de ColombiaRepositorio Institucional Universidad Nacional de Colombiahttps://repositorio.unal.edu.co/ilustraciones, diagramasEn la búsqueda de la mejora del concreto armado por parte de la industria de la construcción y la comunidad científica, surgen los cementos activados alcalinamente como una propuesta de material cementante. Este tipo de concreto presenta buenas propiedades de durabilidad y mecánicas. Sin embargo, todavía existen interrogantes en torno a la adherencia y la funcionalidad de su zona adherente. En esta tesis se estudió la adherencia entre un micro-concreto activado alcalinamente (AAMH) con base en ceniza volante y la matriz de acero. Para la investigación se realizó un diseño de experimentos factorial combinado, donde el primer factor es el espesor de la matriz circundante y sus dos niveles son 31,7 mm y 44,4 mm. De acuerdo con la literatura consultada, los dos niveles, corresponden a 4,9 veces el diámetro de la barra (Φ), que es el espesor mínimo de la matriz de concreto circundante, para que exista la zona adherente y el elemento no falle por splitting. El segundo nivel es 6,9 veces el diámetro de la barra (Φ), que corresponde a la zona media del espesor de la matriz circundante [1]. El segundo factor es la relación sílice – alúmina y sus niveles son 3,06; 4,06; 5,06; que son los valores de un intervalo de resultados que reporta la literatura. La sílice/alúmina que es de 3,06 corresponde a la cantidad de sílice reactiva que contiene la ceniza volante al solo ser activada con el precursor de hidróxido de sodio, las otras dos sílice/alúmina 4,06 y 5,06; se aumentan en el sistema por medio de la mezcla del precursor de hidróxido de sodio con silicato de sodio, donde este último reactivo aumenta la cantidad de sílice en las muestras [2], [3], [4]. El aumento de la sílice/alúmina en las muestras, aumenta directamente con la relación del Silicato de sodio-Hidróxido de sodio. Esta última relación de los precursores la cual es la encargada de variar el contenido de la sílice en el sistema de las muestras a lo largo del documento se identificará como el factor R. La sílice/alúmina (1) corresponde solo a la cantidad de Sílice y alúmina reactiva que contiene la ceniza volante. La ceniza se activada por medio del precursor hidróxido de sodio. La sílice/alúmina (2), (3) se les vario el contenido de la sílice en el sistema de las muestras, esta se hizo aumentando el factor R de las muestras, hasta alcanzar los valores que son objeto del estudio en esta tesis. Sílice alúmina (1) = 3,06 → Silicato de sodio Hidroxido de sodio (1) = 0,00 ; Sílice alúmina (2) = 4,06 → Silicato de sodio Hidroxido de sodio (2) = 0,53; Sílice alúmina (3) = 5,06 → Silicato de sodio Hidroxido de sodio (3) = 1,06. Los resultados muestran que el aumento de la cantidad de sílice en estos cementos permite un refinamiento de poros en los micro-concretos, que, a su vez, mejoran sus propiedades mecánicas. Una explicación a las variaciones en las propiedades mecánicas y microestructurales es que el contenido de sílice y la presencia del hidróxido de calcio, favorecen, respectivamente, los procesos de formación de los geles de Aluminosilicato de Sodio Hidratado (N-A-S-H) y Aluminosilicato de Calcio Hidratado (C-A-S-H). La literatura encontrada plantea que, al aumentar el espesor de la matriz circundante de concreto, se aumenta la resistencia a la tracción, dado que el esfuerzo de compresión radial que se genera por la matriz de concreto sobre la matriz de acero aumenta la fuerza de resistencia al arrancamiento. Los resultados obtenidos permiten inferir que si la matriz de concreto es suficientemente densa y poco porosa por el enriquecimiento de sílice que favorece la formación de los geles N-A-S-H y C-A-S-H, que aumenta las fuerzas de cohesión, la adherencia mejora independientemente del espesor de la matriz circundante.(Texto tomado de la fuente)In the search for the improvement of reinforced concrete by the construction industry and the scientific community, alkaline-activated cements emerge as a proposal for cementing material. This type of concrete has good durability and mechanical properties. However, there are still questions about the adherence and functionality of its adhesive zone. In this thesis, the adherence between an alkaline activated micro-concrete (AAMH) based on fly ash and the steel matrix was studied. For the research, a combined factorial design of experiments was carried out, where the first factor is the thickness of the surrounding matrix, and its two levels are 31.7 mm and 44.4 mm. According to the literature consulted, the two levels correspond to 4.9 times the diameter of the bar (Φ), which is the minimum thickness of the surrounding concrete matrix, so that the adherent zone exists, and the element does not fail due to splitting. The second level is 6.9 times the diameter of the bar (Φ), which corresponds to the middle of the thickness of the surrounding matrix [1]. The second factor is the silica-alumina ratio and its levels are 3.06; 4.06; 5.06; which are the values of an interval of results reported in the literature. The silica / alumina which is 3.06 corresponds to the amount of reactive silica that the fly ash contains when it is only activated with the sodium hydroxide precursor, the other two silica / alumina 4.06 and 5.06; they are increased in the system by mixing the sodium hydroxide precursor with sodium silicate, where the latter reagent increases the amount of silica in the samples [2], [3], [4]. The increase in silica / alumina in the samples increases directly with the ratio of Sodium Silicate-Sodium Hydroxide. This last relationship of the precursors which is responsible for varying the content of silica in the sample system throughout the document will be identified as the R factor. Silica / alumina (1) corresponds only to the amount of Silica and reactive alumina containing fly ash. The ash is activated by means of the sodium hydroxide precursor. The silica / alumina (2), (3) the silica content in the sample system was varied, this was done by increasing the R factor of the samples, until reaching the values that are the object of the study in this thesis. Sílica alumina (1) = 3,06 → Sodium silicate Sodium hydroxide (1) = 0,00 ; Sílica alumina (2) = 4,06 → Sodium silicate Sodium hydroxide (2) = 0,53; Sílica alumina (3) = 5,06 → Sodium silicate Sodium hydroxide (3) = 1,06. The results show that the increase in the amount of silica in these cements allows a refinement of pores in the micro-concretes, which in turn, improves their mechanical properties. One explanation for the variations in mechanical and microstructural properties is that the silica content and the presence of calcium hydroxide favor, respectively, the formation processes of hydrated Sodium Aluminosilicate (NASH) and Hydrated Calcium Aluminosilicate gels (CASH). The literature found proposes that by increasing the thickness of the surrounding concrete matrix, the tensile strength is increased, since the radial compression stress that is generated by the concrete matrix on the steel matrix increases the resistance force. To plucking. The results obtained allow us to infer that if the concrete matrix is sufficiently dense and not very porous due to the enrichment of silica that favors the formation of the NASH and CASH gels, which increases the cohesion forces, the adherence improves regardless of the thickness of the surrounding matrix.MaestríaMagíster en Ingeniería - Materiales y ProcesosAdherencia en Concretos activados alcalinamente base ceniza volanteÁrea Curricular de Materiales y Nanotecnologíaxv, 72 páginaapplication/pdfspaUniversidad Nacional de ColombiaMedellín - Minas - Maestría en Ingeniería - Materiales y ProcesosFacultad de MinasMedellín, ColombiaUniversidad Nacional de Colombia - Sede Medellín620 - Ingeniería y operaciones afines690 - Construcción de edificios::691 - Materiales de construcciónMateriales de construcciónBuilding materialsAdherenciaEnsayo mecánico de arrancamientoCementos activados alcalinamenteCeniza volante de carbónMicro-concreto activado alcalinamenteBond, Mechanical pull-out testAlkaline activated cementsCarbon fly ashAlkaline-activated micro-concreteEvaluación de la adherencia entre un concreto activado alcalinamente con base en ceniza volante de carbón y el acero de refuerzo grado 60Evaluation of the adhesion between an alkaline activated concrete based on coal fly ash and grade 60 reinforcing steelTrabajo de grado - Maestríainfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/acceptedVersionTexthttp://purl.org/redcol/resource_type/TMColombiaRedColLaReferenciaG. P. Gambarova P. G., Rosati, “Bond and splitting in bar pull-out: behavioural laws. Magazine of Concrete Research,” . Mag. Concr. Res., vol. 49, no. 179, pp. 99–110, 1997.M. J. A. Mijarsh, M. A. Megat Johari, and Z. A. Ahmad, “Compressive strength of treated palm oil fuel ash based geopolymer mortar containing calcium hydroxide, aluminum hydroxide and silica fume as mineral additives,” Cem. Concr. Compos., vol. 60, pp. 65–81, Jul. 2015.T. Xie, P. Visintin, X. Zhao, and R. Gravina, “Mix design and mechanical properties of geopolymer and alkali activated concrete: Review of the state-of-the-art and the development of a new unified approach,” Constr. Build. Mater., vol. 256, p. 119380, 2020.F. Guo, J. Pei, J. Zhang, B. Xue, G. Sun, and R. Li, “Study on the adhesion property between asphalt binder and aggregate: A state-of-the-art review,” Constr. Build. Mater., vol. 256, p. 119474, 2020.A. Alain, “Evolución de la reacción y estructura del sistema portlandita - ceniza volante de carbón activado alcalinamente,” p. 155, 2018.G. Metelli and G. A. Plizzari, “Influence of the relative rib area on bond behaviour,” Mag. Concr. Res., vol. 66, no. 6, pp. 277–294, 2014.M. M. Huelva, “propuesta de un modelo de evaluación estruct ...,” no. January 2005, 2015.D. L. L. Segrera, J. Oliver, and A. E. Huespe, “Simulación numérica del proceso de fractura en concreto reforzado mediante la metodología de discontinuidades fuertes de continuo. Parte II: Aplicación a páneles sometidos a cortante,” Ing. e Investig., vol. 30, no. 3, pp. 16–26, 2010.L. P. Güereca, “Evaluación comparativa de los impactos ambientales de la producción de clínker con combustible fósil frente a combustible derivado de los residuos municipales,” Gac. del Inst. Ing., pp. 2010–2013, 2013.IDEAM, Y Departamental De Gases Efecto Invernadero - De Gases Efecto. 2016.M. Morales, “Universidad San Pedro Filial - Sullana,” p. 80, 2018.J. Ignacio and D. Orso, “LAS MEZCLAS DE CONCRETO HIDRÁULICO CON ADITIVOS INCLUSORES DE AIRE ‘CENIZAS VOLANTES,’” 2016.A. Castel and S. J. Foster, “Bond strength between blended slag and Class F fly ash geopolymer concrete with steel reinforcement,” Cem. Concr. Res., vol. 72, pp. 48–53, 2015.G. Xu and X. Shi, “Characteristics and applications of fly ash as a sustainable construction material: A state-of-the-art review,” Resour. Conserv. Recycl., vol. 136, no. April, pp. 95–109, 2018.American Society for Testing and Materials, “ASTM C136-14_Método de prueba estándar para la determinación granulométrica de agregados finos y gruesos,” Annu. B. ASTM Stand., pp. 3–7, 2014.P. Lorca Aranda, “‘Efecto de la Adición de Hidróxido Cálcico sobre Mezclas con Alta Sustitución de Cemento por Ceniza Volante,’” 2015.A. Hassan, M. Arif, and M. Shariq, “Use of geopolymer concrete for a cleaner and sustainable environment – A review of mechanical properties and microstructure,” J. Clean. Prod., vol. 223, pp. 704–728, 2019.N. Dominguez Ramirez, “La adherencia en el concreto reforzado : breve revisión histórica de la investigación del fenómeno Steel-concrete bonding phenomenon : a brief review of the phenomenon ’ s research,” Investig. y Ciencia21, vol. 21, pp. 61–72, 2013.V. Bilek, S. Bonczková, J. Hurta, D. Pytlík, and M. Mrovec, “Bond Strength between Reinforcing Steel and Different Types of Concrete,” Procedia Eng., vol. 190, pp. 243–247, 2017.M. Molina, J. P. Gutiérrez, and M. D. García, “Influencia del diámetro de la barra y del recubrimiento en las características adherentes del hormigón armado,” Bol. la Soc. Esp. Ceram. y Vidr., vol. 43, no. 2, pp. 560–564, 2004.D. Hardjito, S. E. Wallah, D. M. J. Sumajouw, and B. V. Rangan, “On the development of fly ash-based geopolymer concrete,” ACI Mater. J., vol. 101, no. 6, pp. 467–472, 2004.A. Hassan, M. Arif, and M. Shariq, “A review of properties and behaviour of reinforced geopolymer concrete structural elements- A clean technology option for sustainable development,” J. Clean. Prod., vol. 245, 2020.L. Lemnitzer, S. Schröder, A. Lindorf, and M. Curbach, “Bond behaviour between reinforcing steel and concrete under multiaxial loading conditions in concrete containments,” React. Technol., no. SMiRT 20, pp. 1–12, 2009.G. REHM, “No TitleThe fundamental law of bond,” in Proceedings of the Symposium on Bond and Crack Formation in Reinforced Concrete, Stockholm, 1958.G. REHM, The basic principle of bond between steel and concrete., Deustcher. Biblioteca C&CA, 1968.LUTZ, L. A., GERGELY, P., WINTER, G., “No TitleThe mechanics of bond and slip of deformed reinforcing bars in concrete.,” Struct. Eng. Rep., vol. 324, 1966.M. M. Huelva, “Propuesta De Un Modelo De Evaluación Estruct ...,” no. January 2005, 2015.Tepfers, “TepfersDrThesis,” A BONUS THEORY Appl. TO SUPERPOSED Tens. Reinf. POWER Deform. BARS, p. 330, 1973.R. Eligehausen, E. P. Popov, and V. V. Bertéro, “Local bond stress-slip relationship of ribbed bars under generalized excitations,” 1979.V. V. ELIGEHAUSEN, R., POPOV, E. P. BERTERO, “Local bond stress-slip relationships of deformed bars under generalized excitations,” Univ. Calif., vol. UCB/EERC-8, 1983.V. González Fernández, Á. Barrios-Padura, and M. Molina-Huelva, “Aplicaciones de las técnicas no destructivas Pull-Off y ultrasonidos en el control de calidad del refuerzo con materiales compuestos en estructuras de concreto,” Cienc. e Ing. Neogranadina, vol. 28, no. 1, pp. 5–26, Mar. 2018.R. EliGEHAUSEN, E. P. POPOV, and Vite. V. BERTERO, “CONICET_Digital_Nro.16669,” LOCAL Bond Stress. RELATIONSHIPS Deform. BARS UNDER Gen. Excit., p. 180.R. Tepfers and P.-A. Olsson, “Ring test for evaluation of bond properties of reinforcing bars,” Bond Concr. - From Res. to Pract. Riga, Latv., vol. 1, pp. 89–99, 1992.R. Eligehausen, E. P. Popov, and V. V. Bertero, “Local Bond Stress-Slip Relationships of Deformed Bars Under Generalized Excitations.,” vol. 4, pp. 69–80, 1982.P. LUTZ, L. A., GERGELY, “Mechanics of bond and slip of deformed bars in concrete,” ACI Struct. J., vol. 64 (11), pp. 711–721, 1967.GOTO, “Cracks formed in concrete around tension bars,” ACI J., vol. 68(4), pp. 244–251, 1971.M. Raous and M. A. Karray, “Model coupling friction and adhesion for steel-concrete interfaces,” Int. J. Comput. Appl. Technol., vol. 34, no. 1, pp. 42–51, 2009.M. A. Eyre J. R., Nokhasteh, “Strength assessment of corrosion damaged reinforced concrete slabs and beams.,” Proc. Inst. Civ. Eng. Struct. Build., vol. 94, pp. 197-203., 1992.Z. P. Bažant, Z. Li, and M. Thoma, “Identification of stress-slip law for bar or fiber pullout by size effect tests,” J. Eng. Mech., vol. 121, no. 5, pp. 620–625, 1995.C. J., “Alternative strategies for temporary support during structural repair of reinforced-concrete beams.,” J. Struct. Eng., vol. 122, pp. 238–246, 1996.L. Z. Raoof M., “Structural characteristics of RC beams with exposed main steel,” Proc. Inst. Civ. Eng., vol. 122, pp. 35–51, 1996.K. LUNDGREN, “Three-dimensional modelling of bond in reinforced concrete,” University of Technology, 1999.K. LUNDGREN, “Pull-out tests of steel-encased speci-mens subjected to reversed cyclic loading,” Mater. Struct., 2000.D. ZUO, J., DARWIN, “Bond slip of high relative rib area bars under cyclic loading.,” ACI Struct. J., vol. 97(2), pp. 331–334, 2000.G. L. KOCH, R. G., BALAZS, “Limit states for long term and cyclic loading. ‘Bond in concrete,’” Conf. held Budapest Univ. Techno logy Econ., vol. 211, pp. 220, 2002, 2002.B. H. Oh, O. C. Choi, L. Chung, and Korea Concrete Institute., Fracture mechanics of concrete and concrete structures : proceedings of the 7th International Conference on Fracture Mechanics of Concrete and Concrete Structures, Jeju, Korea, May 23-28, 2010.M. Molina, J. P. Gutiérrez, and M. D. García, “Influencia del diámetro de la barra y del recubrimiento en las características adherentes del hormigón armado,” in Boletin de la Sociedad Espanola de Ceramica y Vidrio, 2004, vol. 43, no. 2, pp. 560–564.S. Hong and S. K. Park, “Uniaxial bond stress-slip relationship of reinforcing bars in concrete,” Adv. Mater. Sci. Eng., vol. 2012, 2012.P. K. Sarker, “Bond strength of reinforcing steel embedded in fly ash-based geopolymer concrete,” Mater. Struct. Constr., vol. 44, no. 5, pp. 1021–1030, 2011.H. Costa, “La unión entre el hormigón alcalino activado y del Acero,” 2014.H. Y. Zhang, V. Kodur, B. Wu, J. Yan, and Z. S. Yuan, “Effect of temperature on bond characteristics of geopolymer concrete,” Constr. Build. Mater., vol. 163, pp. 277–285, 2018.S. Steel and R. Alloys, “Standard Specification for Deformed and Plain Low-Alloy Steel Bars for Concrete,” pp. 1–7, 2014.Astm, “Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use,” Annu. B. ASTM Stand., no. C, pp. 3–6, 2010.A. Guriérrez Torres, “Obtención Y Caracterización De Geopolímeros Sintetizados a Partir De La Escoria Granulada De Alto Horno Como Uso Alternativo Del Cemento Portland,” p. 258, 2017.J. Of, S. Engineering, and M. Sciences, “Advanced Search http://ascelibrary.aip.org/vsearch/servlet/VerityServlet?KEY=JSEN...,” vol. 9445, no. August, p. 2007, 2007B. V. Silva, M. P. Barbosa, L. C. P. Silva Filho, and M. S. Lorrain, “Experimental investigation on the use of steel-concrete bond tests for estimating axial compressive strength of concrete. Part 2: APULOT,” Rev. IBRACON Estruturas e Mater., vol. 7, no. 5, pp. 856–878, 2014.ASTM, “Standard test method for pullout strenght of hardened concrete ASTM C 900,” Am. Soc. Test. Mater., no. 1, pp. 1–10, 2013.K. S. Kotova and G. S. Slavcheva, “Composite materials cohesion parameters,” IOP Conf. Ser. Mater. Sci. Eng., vol. 489, no. 1, 2019.A 615/A 615M – 12, “Standard Specification for Deformed and Plain Carbon-Steel Bars for Concrete Reinforcement,” Astm, p. 6, 2012.ASTM International, “Astm C188-17,” Annu. B. ASTM Stand., pp. 1–3, 2017.C204-18, “Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability,” ASTM Int., pp. 1–11, 2019.ASTM, “ASTM: Standard Test Method for Ash in the Analysis Sample of Coal and Coke from Coal 1,” ASTM Int., vol. 05, no. Reapproved 2018, pp. 1–6, 2002.ASTM, “Standard Test Method for Compressive Strength of Hydraulic Cement Mortars ( Using 2-in . or [ 50-mm ] Cube Specimens ) 1,” Chem. Anal., vol. 04, no. C109/C109M – 11b, pp. 1–9, 2010.American Society for Testing and Materials (ASTM), “Standard Test Method for Pullout Strength of Hardened Concrete 1,” Astm C900, no. 5, pp. 1–10, 2015.A. Mu, “ANÁLISIS DE LA RESISTENCIA A LA COMPRESIÓN F´c DEL CONCRETO HIDRÁULICO ADICIONADO CON SILICATO DE SODIO, MEDIANTE ENSAYOS DE MADUREZ Y RESISTENCIA A LA COMPRESIÓN.,” J. Chem. Inf. Model., vol. 53, no. 9, pp. 1689–1699, 2019.American Society for Testing and Materials International, “American Society for Testing and Materials. ASTM C128: Standard Test Method for Relative Density (Specific Gravity) and Absorption of Fine Aggregate,” ASTM Int., vol. i, p. 6, 2015.Astm:C29/C29M-09, “Standard Test Method for Bulk Density (‘ Unit Weight ’) and Voids in Aggregate,” ASTM Int., vol. i, no. c, pp. 1–5, 2009.ASTM, “ASTM C566-19_Standard Test Method for Total Evaporable Moisture Content of Aggregate by Drying,” Annu. B. ASTM Stand., pp. 5–7, 2019.ASTM C143/C143M, “Standard Test Method for Slump of Hydraulic-Cement Concrete,” Astm C143, no. 1, pp. 1–4, 2015.G. Guevara Fallas, C. Hidalgo Madrigal, M. Pizarro García, I. Rodríguez Valenciano, L. D. Rojas Vega, and G. Segura Guzmán, “Efecto de la variación agua/cemento en el concreto,” Rev. Tecnol. en Marcha, vol. 25, no. 2, p. 80, 2012.EstudiantesInvestigadoresMaestrosLICENSElicense.txtlicense.txttext/plain; charset=utf-85879https://repositorio.unal.edu.co/bitstream/unal/84961/1/license.txteb34b1cf90b7e1103fc9dfd26be24b4aMD51THUMBNAIL1128390648.2020.pdf.jpg1128390648.2020.pdf.jpgGenerated Thumbnailimage/jpeg3877https://repositorio.unal.edu.co/bitstream/unal/84961/3/1128390648.2020.pdf.jpg24f4242b7b2fe528f39481d45de94f23MD53Tesis MSc Robinson Fernando Rua P..pdf.jpgTesis MSc Robinson Fernando Rua P..pdf.jpgGenerated Thumbnailimage/jpeg3846https://repositorio.unal.edu.co/bitstream/unal/84961/5/Tesis%20MSc%20Robinson%20Fernando%20Rua%20P..pdf.jpg3f50cc45af8dcec46548c88fdef369f3MD55ORIGINALTesis MSc Robinson Fernando Rua P..pdfTesis MSc Robinson Fernando Rua P..pdfTesis de Maestría en Ingeniería - Materiales y Procesosapplication/pdf2164477https://repositorio.unal.edu.co/bitstream/unal/84961/4/Tesis%20MSc%20Robinson%20Fernando%20Rua%20P..pdf35f39fd9f8064d1f7d080f2537e0a7b9MD54unal/84961oai:repositorio.unal.edu.co:unal/849612024-09-24 00:50:17.164Repositorio Institucional Universidad Nacional de Colombiarepositorio_nal@unal.edu.coUEFSVEUgMS4gVMOJUk1JTk9TIERFIExBIExJQ0VOQ0lBIFBBUkEgUFVCTElDQUNJw5NOIERFIE9CUkFTIEVOIEVMIFJFUE9TSVRPUklPIElOU1RJVFVDSU9OQUwgVU5BTC4KCkxvcyBhdXRvcmVzIHkvbyB0aXR1bGFyZXMgZGUgbG9zIGRlcmVjaG9zIHBhdHJpbW9uaWFsZXMgZGUgYXV0b3IsIGNvbmZpZXJlbiBhIGxhIFVuaXZlcnNpZGFkIE5hY2lvbmFsIGRlIENvbG9tYmlhIHVuYSBsaWNlbmNpYSBubyBleGNsdXNpdmEsIGxpbWl0YWRhIHkgZ3JhdHVpdGEgc29icmUgbGEgb2JyYSBxdWUgc2UgaW50ZWdyYSBlbiBlbCBSZXBvc2l0b3JpbyBJbnN0aXR1Y2lvbmFsLCBiYWpvIGxvcyBzaWd1aWVudGVzIHTDqXJtaW5vczoKCgphKQlMb3MgYXV0b3JlcyB5L28gbG9zIHRpdHVsYXJlcyBkZSBsb3MgZGVyZWNob3MgcGF0cmltb25pYWxlcyBkZSBhdXRvciBzb2JyZSBsYSBvYnJhIGNvbmZpZXJlbiBhIGxhIFVuaXZlcnNpZGFkIE5hY2lvbmFsIGRlIENvbG9tYmlhIHVuYSBsaWNlbmNpYSBubyBleGNsdXNpdmEgcGFyYSByZWFsaXphciBsb3Mgc2lndWllbnRlcyBhY3RvcyBzb2JyZSBsYSBvYnJhOiBpKSByZXByb2R1Y2lyIGxhIG9icmEgZGUgbWFuZXJhIGRpZ2l0YWwsIHBlcm1hbmVudGUgbyB0ZW1wb3JhbCwgaW5jbHV5ZW5kbyBlbCBhbG1hY2VuYW1pZW50byBlbGVjdHLDs25pY28sIGFzw60gY29tbyBjb252ZXJ0aXIgZWwgZG9jdW1lbnRvIGVuIGVsIGN1YWwgc2UgZW5jdWVudHJhIGNvbnRlbmlkYSBsYSBvYnJhIGEgY3VhbHF1aWVyIG1lZGlvIG8gZm9ybWF0byBleGlzdGVudGUgYSBsYSBmZWNoYSBkZSBsYSBzdXNjcmlwY2nDs24gZGUgbGEgcHJlc2VudGUgbGljZW5jaWEsIHkgaWkpIGNvbXVuaWNhciBhbCBww7pibGljbyBsYSBvYnJhIHBvciBjdWFscXVpZXIgbWVkaW8gbyBwcm9jZWRpbWllbnRvLCBlbiBtZWRpb3MgYWzDoW1icmljb3MgbyBpbmFsw6FtYnJpY29zLCBpbmNsdXllbmRvIGxhIHB1ZXN0YSBhIGRpc3Bvc2ljacOzbiBlbiBhY2Nlc28gYWJpZXJ0by4gQWRpY2lvbmFsIGEgbG8gYW50ZXJpb3IsIGVsIGF1dG9yIHkvbyB0aXR1bGFyIGF1dG9yaXphIGEgbGEgVW5pdmVyc2lkYWQgTmFjaW9uYWwgZGUgQ29sb21iaWEgcGFyYSBxdWUsIGVuIGxhIHJlcHJvZHVjY2nDs24geSBjb211bmljYWNpw7NuIGFsIHDDumJsaWNvIHF1ZSBsYSBVbml2ZXJzaWRhZCByZWFsaWNlIHNvYnJlIGxhIG9icmEsIGhhZ2EgbWVuY2nDs24gZGUgbWFuZXJhIGV4cHJlc2EgYWwgdGlwbyBkZSBsaWNlbmNpYSBDcmVhdGl2ZSBDb21tb25zIGJham8gbGEgY3VhbCBlbCBhdXRvciB5L28gdGl0dWxhciBkZXNlYSBvZnJlY2VyIHN1IG9icmEgYSBsb3MgdGVyY2Vyb3MgcXVlIGFjY2VkYW4gYSBkaWNoYSBvYnJhIGEgdHJhdsOpcyBkZWwgUmVwb3NpdG9yaW8gSW5zdGl0dWNpb25hbCwgY3VhbmRvIHNlYSBlbCBjYXNvLiBFbCBhdXRvciB5L28gdGl0dWxhciBkZSBsb3MgZGVyZWNob3MgcGF0cmltb25pYWxlcyBkZSBhdXRvciBwb2Ryw6EgZGFyIHBvciB0ZXJtaW5hZGEgbGEgcHJlc2VudGUgbGljZW5jaWEgbWVkaWFudGUgc29saWNpdHVkIGVsZXZhZGEgYSBsYSBEaXJlY2Npw7NuIE5hY2lvbmFsIGRlIEJpYmxpb3RlY2FzIGRlIGxhIFVuaXZlcnNpZGFkIE5hY2lvbmFsIGRlIENvbG9tYmlhLiAKCmIpIAlMb3MgYXV0b3JlcyB5L28gdGl0dWxhcmVzIGRlIGxvcyBkZXJlY2hvcyBwYXRyaW1vbmlhbGVzIGRlIGF1dG9yIHNvYnJlIGxhIG9icmEgY29uZmllcmVuIGxhIGxpY2VuY2lhIHNlw7FhbGFkYSBlbiBlbCBsaXRlcmFsIGEpIGRlbCBwcmVzZW50ZSBkb2N1bWVudG8gcG9yIGVsIHRpZW1wbyBkZSBwcm90ZWNjacOzbiBkZSBsYSBvYnJhIGVuIHRvZG9zIGxvcyBwYcOtc2VzIGRlbCBtdW5kbywgZXN0byBlcywgc2luIGxpbWl0YWNpw7NuIHRlcnJpdG9yaWFsIGFsZ3VuYS4KCmMpCUxvcyBhdXRvcmVzIHkvbyB0aXR1bGFyZXMgZGUgZGVyZWNob3MgcGF0cmltb25pYWxlcyBkZSBhdXRvciBtYW5pZmllc3RhbiBlc3RhciBkZSBhY3VlcmRvIGNvbiBxdWUgbGEgcHJlc2VudGUgbGljZW5jaWEgc2Ugb3RvcmdhIGEgdMOtdHVsbyBncmF0dWl0bywgcG9yIGxvIHRhbnRvLCByZW51bmNpYW4gYSByZWNpYmlyIGN1YWxxdWllciByZXRyaWJ1Y2nDs24gZWNvbsOzbWljYSBvIGVtb2x1bWVudG8gYWxndW5vIHBvciBsYSBwdWJsaWNhY2nDs24sIGRpc3RyaWJ1Y2nDs24sIGNvbXVuaWNhY2nDs24gcMO6YmxpY2EgeSBjdWFscXVpZXIgb3RybyB1c28gcXVlIHNlIGhhZ2EgZW4gbG9zIHTDqXJtaW5vcyBkZSBsYSBwcmVzZW50ZSBsaWNlbmNpYSB5IGRlIGxhIGxpY2VuY2lhIENyZWF0aXZlIENvbW1vbnMgY29uIHF1ZSBzZSBwdWJsaWNhLgoKZCkJUXVpZW5lcyBmaXJtYW4gZWwgcHJlc2VudGUgZG9jdW1lbnRvIGRlY2xhcmFuIHF1ZSBwYXJhIGxhIGNyZWFjacOzbiBkZSBsYSBvYnJhLCBubyBzZSBoYW4gdnVsbmVyYWRvIGxvcyBkZXJlY2hvcyBkZSBwcm9waWVkYWQgaW50ZWxlY3R1YWwsIGluZHVzdHJpYWwsIG1vcmFsZXMgeSBwYXRyaW1vbmlhbGVzIGRlIHRlcmNlcm9zLiBEZSBvdHJhIHBhcnRlLCAgcmVjb25vY2VuIHF1ZSBsYSBVbml2ZXJzaWRhZCBOYWNpb25hbCBkZSBDb2xvbWJpYSBhY3TDumEgY29tbyB1biB0ZXJjZXJvIGRlIGJ1ZW5hIGZlIHkgc2UgZW5jdWVudHJhIGV4ZW50YSBkZSBjdWxwYSBlbiBjYXNvIGRlIHByZXNlbnRhcnNlIGFsZ8O6biB0aXBvIGRlIHJlY2xhbWFjacOzbiBlbiBtYXRlcmlhIGRlIGRlcmVjaG9zIGRlIGF1dG9yIG8gcHJvcGllZGFkIGludGVsZWN0dWFsIGVuIGdlbmVyYWwuIFBvciBsbyB0YW50bywgbG9zIGZpcm1hbnRlcyAgYWNlcHRhbiBxdWUgY29tbyB0aXR1bGFyZXMgw7puaWNvcyBkZSBsb3MgZGVyZWNob3MgcGF0cmltb25pYWxlcyBkZSBhdXRvciwgYXN1bWlyw6FuIHRvZGEgbGEgcmVzcG9uc2FiaWxpZGFkIGNpdmlsLCBhZG1pbmlzdHJhdGl2YSB5L28gcGVuYWwgcXVlIHB1ZWRhIGRlcml2YXJzZSBkZSBsYSBwdWJsaWNhY2nDs24gZGUgbGEgb2JyYS4gIAoKZikJQXV0b3JpemFuIGEgbGEgVW5pdmVyc2lkYWQgTmFjaW9uYWwgZGUgQ29sb21iaWEgaW5jbHVpciBsYSBvYnJhIGVuIGxvcyBhZ3JlZ2Fkb3JlcyBkZSBjb250ZW5pZG9zLCBidXNjYWRvcmVzIGFjYWTDqW1pY29zLCBtZXRhYnVzY2Fkb3Jlcywgw61uZGljZXMgeSBkZW3DoXMgbWVkaW9zIHF1ZSBzZSBlc3RpbWVuIG5lY2VzYXJpb3MgcGFyYSBwcm9tb3ZlciBlbCBhY2Nlc28geSBjb25zdWx0YSBkZSBsYSBtaXNtYS4gCgpnKQlFbiBlbCBjYXNvIGRlIGxhcyB0ZXNpcyBjcmVhZGFzIHBhcmEgb3B0YXIgZG9ibGUgdGl0dWxhY2nDs24sIGxvcyBmaXJtYW50ZXMgc2Vyw6FuIGxvcyByZXNwb25zYWJsZXMgZGUgY29tdW5pY2FyIGEgbGFzIGluc3RpdHVjaW9uZXMgbmFjaW9uYWxlcyBvIGV4dHJhbmplcmFzIGVuIGNvbnZlbmlvLCBsYXMgbGljZW5jaWFzIGRlIGFjY2VzbyBhYmllcnRvIENyZWF0aXZlIENvbW1vbnMgeSBhdXRvcml6YWNpb25lcyBhc2lnbmFkYXMgYSBzdSBvYnJhIHBhcmEgbGEgcHVibGljYWNpw7NuIGVuIGVsIFJlcG9zaXRvcmlvIEluc3RpdHVjaW9uYWwgVU5BTCBkZSBhY3VlcmRvIGNvbiBsYXMgZGlyZWN0cmljZXMgZGUgbGEgUG9sw610aWNhIEdlbmVyYWwgZGUgbGEgQmlibGlvdGVjYSBEaWdpdGFsLgoKCmgpCVNlIGF1dG9yaXphIGEgbGEgVW5pdmVyc2lkYWQgTmFjaW9uYWwgZGUgQ29sb21iaWEgY29tbyByZXNwb25zYWJsZSBkZWwgdHJhdGFtaWVudG8gZGUgZGF0b3MgcGVyc29uYWxlcywgZGUgYWN1ZXJkbyBjb24gbGEgbGV5IDE1ODEgZGUgMjAxMiBlbnRlbmRpZW5kbyBxdWUgc2UgZW5jdWVudHJhbiBiYWpvIG1lZGlkYXMgcXVlIGdhcmFudGl6YW4gbGEgc2VndXJpZGFkLCBjb25maWRlbmNpYWxpZGFkIGUgaW50ZWdyaWRhZCwgeSBzdSB0cmF0YW1pZW50byB0aWVuZSB1bmEgZmluYWxpZGFkIGhpc3TDs3JpY2EsIGVzdGFkw61zdGljYSBvIGNpZW50w61maWNhIHNlZ8O6biBsbyBkaXNwdWVzdG8gZW4gbGEgUG9sw610aWNhIGRlIFRyYXRhbWllbnRvIGRlIERhdG9zIFBlcnNvbmFsZXMuCgoKClBBUlRFIDIuIEFVVE9SSVpBQ0nDk04gUEFSQSBQVUJMSUNBUiBZIFBFUk1JVElSIExBIENPTlNVTFRBIFkgVVNPIERFIE9CUkFTIEVOIEVMIFJFUE9TSVRPUklPIElOU1RJVFVDSU9OQUwgVU5BTC4KClNlIGF1dG9yaXphIGxhIHB1YmxpY2FjacOzbiBlbGVjdHLDs25pY2EsIGNvbnN1bHRhIHkgdXNvIGRlIGxhIG9icmEgcG9yIHBhcnRlIGRlIGxhIFVuaXZlcnNpZGFkIE5hY2lvbmFsIGRlIENvbG9tYmlhIHkgZGUgc3VzIHVzdWFyaW9zIGRlIGxhIHNpZ3VpZW50ZSBtYW5lcmE6CgphLglDb25jZWRvIGxpY2VuY2lhIGVuIGxvcyB0w6lybWlub3Mgc2XDsWFsYWRvcyBlbiBsYSBwYXJ0ZSAxIGRlbCBwcmVzZW50ZSBkb2N1bWVudG8sIGNvbiBlbCBvYmpldGl2byBkZSBxdWUgbGEgb2JyYSBlbnRyZWdhZGEgc2VhIHB1YmxpY2FkYSBlbiBlbCBSZXBvc2l0b3JpbyBJbnN0aXR1Y2lvbmFsIGRlIGxhIFVuaXZlcnNpZGFkIE5hY2lvbmFsIGRlIENvbG9tYmlhIHkgcHVlc3RhIGEgZGlzcG9zaWNpw7NuIGVuIGFjY2VzbyBhYmllcnRvIHBhcmEgc3UgY29uc3VsdGEgcG9yIGxvcyB1c3VhcmlvcyBkZSBsYSBVbml2ZXJzaWRhZCBOYWNpb25hbCBkZSBDb2xvbWJpYSAgYSB0cmF2w6lzIGRlIGludGVybmV0LgoKCgpQQVJURSAzIEFVVE9SSVpBQ0nDk04gREUgVFJBVEFNSUVOVE8gREUgREFUT1MgUEVSU09OQUxFUy4KCkxhIFVuaXZlcnNpZGFkIE5hY2lvbmFsIGRlIENvbG9tYmlhLCBjb21vIHJlc3BvbnNhYmxlIGRlbCBUcmF0YW1pZW50byBkZSBEYXRvcyBQZXJzb25hbGVzLCBpbmZvcm1hIHF1ZSBsb3MgZGF0b3MgZGUgY2Fyw6FjdGVyIHBlcnNvbmFsIHJlY29sZWN0YWRvcyBtZWRpYW50ZSBlc3RlIGZvcm11bGFyaW8sIHNlIGVuY3VlbnRyYW4gYmFqbyBtZWRpZGFzIHF1ZSBnYXJhbnRpemFuIGxhIHNlZ3VyaWRhZCwgY29uZmlkZW5jaWFsaWRhZCBlIGludGVncmlkYWQgeSBzdSB0cmF0YW1pZW50byBzZSByZWFsaXphIGRlIGFjdWVyZG8gYWwgY3VtcGxpbWllbnRvIG5vcm1hdGl2byBkZSBsYSBMZXkgMTU4MSBkZSAyMDEyIHkgZGUgbGEgUG9sw610aWNhIGRlIFRyYXRhbWllbnRvIGRlIERhdG9zIFBlcnNvbmFsZXMgZGUgbGEgVW5pdmVyc2lkYWQgTmFjaW9uYWwgZGUgQ29sb21iaWEuIFB1ZWRlIGVqZXJjZXIgc3VzIGRlcmVjaG9zIGNvbW8gdGl0dWxhciBhIGNvbm9jZXIsIGFjdHVhbGl6YXIsIHJlY3RpZmljYXIgeSByZXZvY2FyIGxhcyBhdXRvcml6YWNpb25lcyBkYWRhcyBhIGxhcyBmaW5hbGlkYWRlcyBhcGxpY2FibGVzIGEgdHJhdsOpcyBkZSBsb3MgY2FuYWxlcyBkaXNwdWVzdG9zIHkgZGlzcG9uaWJsZXMgZW4gd3d3LnVuYWwuZWR1LmNvIG8gZS1tYWlsOiBwcm90ZWNkYXRvc19uYUB1bmFsLmVkdS5jbyIKClRlbmllbmRvIGVuIGN1ZW50YSBsbyBhbnRlcmlvciwgYXV0b3Jpem8gZGUgbWFuZXJhIHZvbHVudGFyaWEsIHByZXZpYSwgZXhwbMOtY2l0YSwgaW5mb3JtYWRhIGUgaW5lcXXDrXZvY2EgYSBsYSBVbml2ZXJzaWRhZCBOYWNpb25hbCBkZSBDb2xvbWJpYSBhIHRyYXRhciBsb3MgZGF0b3MgcGVyc29uYWxlcyBkZSBhY3VlcmRvIGNvbiBsYXMgZmluYWxpZGFkZXMgZXNwZWPDrWZpY2FzIHBhcmEgZWwgZGVzYXJyb2xsbyB5IGVqZXJjaWNpbyBkZSBsYXMgZnVuY2lvbmVzIG1pc2lvbmFsZXMgZGUgZG9jZW5jaWEsIGludmVzdGlnYWNpw7NuIHkgZXh0ZW5zacOzbiwgYXPDrSBjb21vIGxhcyByZWxhY2lvbmVzIGFjYWTDqW1pY2FzLCBsYWJvcmFsZXMsIGNvbnRyYWN0dWFsZXMgeSB0b2RhcyBsYXMgZGVtw6FzIHJlbGFjaW9uYWRhcyBjb24gZWwgb2JqZXRvIHNvY2lhbCBkZSBsYSBVbml2ZXJzaWRhZC4gCgo= |