Effect of silica fume addition on the chloride related transport properties of high performance concrete
Corrosion of steel reinforcement due to chloride penetration is the major cause of durability problems in concrete. In that way, this paper summarizes the results of an experimental research carried out in order to investigate the influence of the Silica Fume (SF) content on some chloride related tr...
- Autores:
-
Lizarazo Marriaga, Juan Manuel
López Yépez, Lucio Guillermo
- Tipo de recurso:
- Article of journal
- Fecha de publicación:
- 2012
- Institución:
- Universidad Nacional de Colombia
- Repositorio:
- Universidad Nacional de Colombia
- Idioma:
- spa
- OAI Identifier:
- oai:repositorio.unal.edu.co:unal/33544
- Acceso en línea:
- https://repositorio.unal.edu.co/handle/unal/33544
http://bdigital.unal.edu.co/23624/
- Palabra clave:
- Ion chloride
high performance concrete
silica fume
transport properties
- Rights
- openAccess
- License
- Atribución-NoComercial 4.0 Internacional
| Summary: | Corrosion of steel reinforcement due to chloride penetration is the major cause of durability problems in concrete. In that way, this paper summarizes the results of an experimental research carried out in order to investigate the influence of the Silica Fume (SF) content on some chloride related transport properties. To achieve this, the compressive strength, the self diffusion chloride penetration, the charge passed under a non steady chloride migration test (ASTM C1202) and the AC resistivity were measured on concrete mixes of high performance concrete. Four concrete mixes were cast incorporating 0, 5 10 and 15% of SF as addition of Ordinary Portland Cement. The results showed that the silica fume in concrete causes an increase in strength and a reduction in chloride ion permeability; however, clear differences were found between the results of long diffusion and rapid electrical tests. |
|---|