Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado
ilustraciones, gráficas
- Autores:
-
Palencia Torres, Daniel Gustavo
- Tipo de recurso:
- Fecha de publicación:
- 2020
- Institución:
- Universidad Nacional de Colombia
- Repositorio:
- Universidad Nacional de Colombia
- Idioma:
- spa
- OAI Identifier:
- oai:repositorio.unal.edu.co:unal/79616
- Palabra clave:
- 690 - Construcción de edificios::691 - Materiales de construcción
PEAD (Polietileno De Alta Densidad)
Reologia
Compresión
HDPE (High Density Polyethylene)
Rheology
Compretion
- Rights
- openAccess
- License
- Atribución-NoComercial-SinDerivadas 4.0 Internacional
| id |
UNACIONAL2_35a46727eb9cfbc06c66b8f0d8e9c785 |
|---|---|
| oai_identifier_str |
oai:repositorio.unal.edu.co:unal/79616 |
| network_acronym_str |
UNACIONAL2 |
| network_name_str |
Universidad Nacional de Colombia |
| repository_id_str |
|
| dc.title.spa.fl_str_mv |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| dc.title.translated.eng.fl_str_mv |
Evaluation of the properties in fresh state of a self-consolidating concrete with the addition of high-density polyethylene recovered |
| title |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| spellingShingle |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado 690 - Construcción de edificios::691 - Materiales de construcción PEAD (Polietileno De Alta Densidad) Reologia Compresión HDPE (High Density Polyethylene) Rheology Compretion |
| title_short |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| title_full |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| title_fullStr |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| title_full_unstemmed |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| title_sort |
Evaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granulado |
| dc.creator.fl_str_mv |
Palencia Torres, Daniel Gustavo |
| dc.contributor.advisor.none.fl_str_mv |
Puerto Suarez, Julian David |
| dc.contributor.author.none.fl_str_mv |
Palencia Torres, Daniel Gustavo |
| dc.subject.ddc.spa.fl_str_mv |
690 - Construcción de edificios::691 - Materiales de construcción |
| topic |
690 - Construcción de edificios::691 - Materiales de construcción PEAD (Polietileno De Alta Densidad) Reologia Compresión HDPE (High Density Polyethylene) Rheology Compretion |
| dc.subject.proposal.spa.fl_str_mv |
PEAD (Polietileno De Alta Densidad) Reologia Compresión |
| dc.subject.proposal.eng.fl_str_mv |
HDPE (High Density Polyethylene) Rheology Compretion |
| description |
ilustraciones, gráficas |
| publishDate |
2020 |
| dc.date.issued.none.fl_str_mv |
2020 |
| dc.date.accessioned.none.fl_str_mv |
2021-06-08T18:13:36Z |
| dc.date.available.none.fl_str_mv |
2021-06-08T18:13:36Z |
| dc.type.spa.fl_str_mv |
Trabajo de grado - Maestría |
| dc.type.driver.spa.fl_str_mv |
info:eu-repo/semantics/masterThesis |
| dc.type.version.spa.fl_str_mv |
info:eu-repo/semantics/acceptedVersion |
| dc.type.content.spa.fl_str_mv |
Text |
| dc.type.redcol.spa.fl_str_mv |
http://purl.org/redcol/resource_type/TM |
| status_str |
acceptedVersion |
| dc.identifier.uri.none.fl_str_mv |
https://repositorio.unal.edu.co/handle/unal/79616 |
| dc.identifier.instname.spa.fl_str_mv |
Universidad Nacional de Colombia |
| dc.identifier.reponame.spa.fl_str_mv |
Repositorio Institucional Universidad Nacional de Colombia |
| dc.identifier.repourl.spa.fl_str_mv |
https://repositorio.unal.edu.co/ |
| url |
https://repositorio.unal.edu.co/handle/unal/79616 https://repositorio.unal.edu.co/ |
| identifier_str_mv |
Universidad Nacional de Colombia Repositorio Institucional Universidad Nacional de Colombia |
| dc.language.iso.spa.fl_str_mv |
spa |
| language |
spa |
| dc.relation.references.spa.fl_str_mv |
ACI 211.1-91. (2009). Standard Practice For Selecting Proportions For Normal, Heavyweight, And Mass Concrete, 0–15. ACI 237R-07. (2007). Self-Consolidating Concrete, 0–15. Aguado, A., & Salla, J. M. (1987). Los Hormigones Con Polímeros En La Construcción: Propiedades Y Aplicaciones. Informes de la Construcción, 39(389), 61–72. American Concrete Institute. (2002). ACI 116R Terminología Del Cemento Y El Hormigón, 1–124. ASTM Standard C125. (2010). Standard Terminology Relating To Concrete And Concrete Aggregate. ASTM International, (C), 1–6. ASTMC1610. (2015). Standard Test Method For Static Segregation Of Self-Consolidating Concrete Using Column Technique. ASTMC1610, i(c), 4. ASTMC1611. (2009). Standard Test Method For Slump Flow Of Self-Consolidating Concrete. Annual Book of ASTM Standards Volume 04.02, 1–6. ASTMC1621. (2014). Standard Test Method For Passing Ability Of Self-Consolidating Concrete By J-Ring. Annual Book of ASTM Standard, i, 5. Badache, A., Benosman, A. S., Senhadji, Y., & Mouli, M. (2018). Thermo-Physical And Mechanical Characteristics Of Sand-Based Lightweight Composite Mortars With Recycled High-Density Polyethylene (HDPE). Construction and Building Materials, 163, 40–52. Benito, F., Parra, C., Valcuende, M., Miñano, I., & Rodríguez López, C. (2015). Método para cuantificar la segregación en hormigones autocompactantes. Concreto y cemento: Investigación y desarrollo, 6(2), 48–63. Bono Cabre, R. (2012). Diseños Cuasi-Experimentales Y Longitudinales. Universidad de Barcelona. Facultad de Psicología., 1–85. Canales, F. H. De, Alvarado, E. L. De, & Pineda, E. B. (1994). Metodologia De La Investigacion (Vol. 35). Choi, Y. W., Moon, D. J., Kim, Y. J., & Lachemi, M. (2009). Characteristics Of Mortar And Concrete Containing Fine Aggregate Manufactured From Recycled Waste Polyethylene Terephthalate Bottles. Construction and Building Materials, 23(8), 2829–2835. Cortes, E., & Perilla, J. (2014). Estudio Comparativo De Las Características Fisico-Mecanicas De Cuatro Cementos Comerciales Portland Tipo I. EFNARC. (2003). Especificaciones Y Directrices Para El Hormigón Autocompactable, 44(0), 1–33. Faleschini, F., Jiménez, C., Barra, M., Aponte, D., Vázquez, E., & Pellegrino, C. (2014). Rheology Of Fresh Concretes With Recycled Aggregates. Construction and Building Materials, 73, 407–416. Fernandez Bernal, B., & Hernandez Saavedra, K. (2008). Diagnóstico De La Industria Del Cemento En Colombia Y Evaluación De Alternativas Tecnológicas Para El Cumplimiento De La Norma De Emisión De Fuentes Fijas. Universidad De La Salle. Frigione, M. (2010). Recycling Of PET Bottles As Fine Aggregate In Concrete. Waste Management, 30(6), 1101–1106. Galvez Moreno, D. (2015). Robustez De Un Concreto Autocompactable Producido Con Materiales Disponibles En La Región De Monterrey, Nuevo León. Germann Instruments. (s/f-a). ICAR Rheometer. Product Specifications, 71–75. Germann Instruments. (s/f-b). Rheology Using The ICAR Plus – An Introduction, 1–10. Gómez, M. S., Carvajal, A. M., & Santelices, V. (2011). Influencia Del Polietileno De Alta Densidad (PEAD) Usado Como Adición En El Mortero De Cemento. Revista de la Construccion, 10(3), 110–121. Gómez Nemocón, S. A. (2019). Efectos De La Adición De Microesferas Huecas De Vidrio En Concreto Hidráulico. Hinislioglu, S., & Agar, E. (2004). Use Of Waste High Density Polyethylene As Bitumen Modifier In Asphalt Concrete Mix. Materials Letters, 58(3–4), 267–271. Ismail, Z. Z., & AL-Hashmi, E. A. (2008). Use Of Waste Plastic In Concrete Mixture As Aggregate Replacement. Waste Management, 28(11), 2041–2047. Kozikowski, R. L., & Zemajtis, J. Z. (2006). Identifying Incompatible Combinations Of Concrete Materials : - Volume II – Test Protocol. Kurdowski, W. (2014). Cement And Concrete Chemistry. Cement and Concrete Chemistry, 9789400779, 1–700. Martinez Barrera, G., Hernandez zaragoza, J. B., Lopez Lara, T., & Memchaca Campos, C. (2015). Materiales Sustentables Y Reciclados En La Construcción. Morales Carhuayano, M. R. (2016). Estudio Del Comportamiento Del Concreto Incorporando Pet Reciclado. Universidad Nacional De Ingenieria Peru. Newman, J., & Choo, B. seng. (2003). Advanced Concrete Technology. Adimxtures for concrete, mortar and grout, 1–69. NRMCA. (s/f). CIP 37 - Concreto Autocompactante (CAC). Concrete. NTC121. (2014). Especificación De Desempeño Para Cemento Hidráulico. NTC121, (571), 17. NTC1377. (2010). Ingeniería Civil Y Arquitectura. Elaboración Y Curado De Especímenes De Concreto Para Ensayos En El Laboratorio, (571). NTC174. (2000). Concretos. Especificaciones De Los Agregados Para Concreto. Concreto, 22. NTC176. (2019). Ingeniería Civil Y Arquitectura. Método De Ensayo Para Determinar La Densidad Y La Absorción Del Agregado Grueso. NTC237. (2001). Ingeniería Civil Y Arquitectura. Método Para Determinar La Densidad Y La Absorción Del Agregado Fino. NTC3459. (2001). Concretos. Agua Para La Elaboración De Concreto. NTC3674. (2001). Ingeniería Civil Y Arquitectura. Práctica Para La Reducción Del Tamaño De Las Muestras De Agregados, Tomadas En Campo, Para La Realización De Ensayos. NTC396. (1992). Ingeniería Civil Y Arquitectura. Método De Ensayo Para Determinar El Asentamiento Del Concreto. NTC5222. (2003). Concretos. Métodos De Ensayo Para Medir El Flujo Libre, Flujo Restringido Y Segregación En Concretos Autocompactantes. NTC673. (2010). Concretos. Ensayo De Resistencia A La Compresión De Especimenes Cilíndricos De Concreto. NTC77. (2007). Concretos. Método De Ensayo Para El Análisis Por Tamizado De Los Agregados Finos Y Gruesos. NTC92. (1995). Ingeniería Civil Y Arquitectura. Determinación De La Masa Unitaria Y Los Vacíos Entre Partículas De Agregados. Pacheco-Torgal, F., Ding, Y., & Jalali, S. (2012). Properties And Durability Of Concrete Containing Polymeric Wastes (Tyre Rubber And Polyethylene Terephthalate Bottles): An Overview. Construction and Building Materials, 30, 714–724. Palencia Torres, D. G., & Nuñes Rangel, J. J. (2016). Estudio Comparativo Del Concreto Modificado Con Hdpe (Polietileno De Alta Densidad) Reciclado Y Concreto Convencional. Universidad Francisco de Paula Santander. Pešić, N., Živanović, S., Garcia, R., & Papastergiou, P. (2016). Mechanical Properties Of Concrete Reinforced With Recycled HDPE Plastic Fibres. Construction and Building Materials, 115, 362–370. Rivera, G. A. (2009). Concreto Simple. Universidad del cauca. Sánchez De Guzmán, D. (2001). Tecnología del concreto y del mortero (Quinta). Bhsnda. Sea Studios Foundation. (s/f). Guía Inteligente sobre Plásticos. She, B., & Xu, B. (2017). Research On Mechanical Properties Of HDPE Plastic Fiber Reinforced Concrete Structure. Revista de la facultad de ingenieria U.V.C, 32, 669–674. Soroushian, P., Khan, A., & Hsu, J. (1992). Mechanical Properties Of Concrete Materials Reinforced With Polypropylene Or Polyethylene Fibers. ACI Materials Journal, 89(6), 1–6. Thorneycroft, J., Orr, J., Savoikar, P., & Ball, R. J. (2018). Performance Of Structural Concrete With Recycled Plastic Waste As A Partial Replacement For Sand. Construction and Building Materials, 161, 63–69. Zuñiga Diaz, F. A. (2015). Evaluación Del Tereftarato De Polietileno (Pet) Como Agregado En La Elaboración De Mortero Para Ladrillos Y Concreto. Universidad de la salle Colombia. |
| dc.rights.spa.fl_str_mv |
Derechos Reservados - Universidad Nacional de Colombia, 2021 |
| dc.rights.coar.fl_str_mv |
http://purl.org/coar/access_right/c_abf2 |
| dc.rights.license.spa.fl_str_mv |
Atribución-NoComercial-SinDerivadas 4.0 Internacional |
| dc.rights.uri.spa.fl_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ |
| dc.rights.accessrights.spa.fl_str_mv |
info:eu-repo/semantics/openAccess |
| rights_invalid_str_mv |
Atribución-NoComercial-SinDerivadas 4.0 Internacional Derechos Reservados - Universidad Nacional de Colombia, 2021 http://creativecommons.org/licenses/by-nc-nd/4.0/ http://purl.org/coar/access_right/c_abf2 |
| eu_rights_str_mv |
openAccess |
| dc.format.extent.spa.fl_str_mv |
1 recurso en linea (162 paginas) |
| dc.format.mimetype.spa.fl_str_mv |
application/pdf |
| dc.publisher.spa.fl_str_mv |
Universidad Nacional De Colombia |
| dc.publisher.program.spa.fl_str_mv |
Bogotá - Ingeniería - Maestría en Ingeniería - Estructuras |
| dc.publisher.department.spa.fl_str_mv |
Departamento de Ingeniería Civil y Agrícola |
| dc.publisher.faculty.spa.fl_str_mv |
Facultad de Ingeniería |
| dc.publisher.place.spa.fl_str_mv |
Bogotá, Colombia |
| dc.publisher.branch.spa.fl_str_mv |
Universidad Nacional de Colombia - Sede Bogotá |
| institution |
Universidad Nacional de Colombia |
| bitstream.url.fl_str_mv |
https://repositorio.unal.edu.co/bitstream/unal/79616/1/license.txt https://repositorio.unal.edu.co/bitstream/unal/79616/2/EVALUACION%20DE%20LAS%20PROPIEDADES%20EN%20ESTADO%20FRESCO%20DE%20UN%20CONCRETO%20AUTOCOMPACTANTE%20CON%20ADICION%20DE%20POLIETILENO%20DE%20ALTA%20DENSIDAD%20RECUPERADO%20GRANULADO.pdf https://repositorio.unal.edu.co/bitstream/unal/79616/3/license_rdf https://repositorio.unal.edu.co/bitstream/unal/79616/4/EVALUACION%20DE%20LAS%20PROPIEDADES%20EN%20ESTADO%20FRESCO%20DE%20UN%20CONCRETO%20AUTOCOMPACTANTE%20CON%20ADICION%20DE%20POLIETILENO%20DE%20ALTA%20DENSIDAD%20RECUPERADO%20GRANULADO.pdf.jpg |
| bitstream.checksum.fl_str_mv |
cccfe52f796b7c63423298c2d3365fc6 61070be6ec5c5e43f1c363a547c3bc9b 4460e5956bc1d1639be9ae6146a50347 f084f709968d0e5ad9718f188b695f95 |
| bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
| repository.name.fl_str_mv |
Repositorio Institucional Universidad Nacional de Colombia |
| repository.mail.fl_str_mv |
repositorio_nal@unal.edu.co |
| _version_ |
1814089348922998784 |
| spelling |
Atribución-NoComercial-SinDerivadas 4.0 InternacionalDerechos Reservados - Universidad Nacional de Colombia, 2021http://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Puerto Suarez, Julian David7a94a9390572c7c4e1fd86ffbfda2a68Palencia Torres, Daniel Gustavo6beddc6f9c2346e044d713fad3a76dbc2021-06-08T18:13:36Z2021-06-08T18:13:36Z2020https://repositorio.unal.edu.co/handle/unal/79616Universidad Nacional de ColombiaRepositorio Institucional Universidad Nacional de Colombiahttps://repositorio.unal.edu.co/ilustraciones, gráficasLa investigación tiene como objetivo principal obtener propiedades en estado fresco de un concreto autocompactante con adición PEAD granulado recuperado. En este se compararán los resultados de los diversos ensayos requeridos para hallar las propiedades en estado fresco como la capacidad de llenado, la capacidad de paso, la resistencia, la segregación y las propiedades reológicas según el reómetro ICAR 5000, además se evaluó la resistencia a la compresión (propiedad en estado endurecido). Se decidió utilizar un 8%, 10% y 12% de Polietileno de alta densidad (PEAD) como parte del agregado fino, los ensayos realizados son: el ensayo slump flow, mide forma indirecta relaciona la fluidez de la mezcla y se relaciona con la capacidad de llenado, el ensayo de flujo asentamiento t50cm o Flujo Libre conduce a un concepto indirecto de la viscosidad de la mezcla; el ensayo del anillo japonés o Anillo J, representa un valor indirecto de la resistencia al bloqueo y fluidez; la caja en L a la fluidez y la columna de segregación mide indirectamente la segregación de la mezcla. A partir de los resultados obtenidos de estos ensayos se concluye que la mezcla del concreto autocompactante cumple las disposiciones de las normas colombianas e internacionales, para la utilización de este concreto, Las principales características de estos concretos es que presentan bloqueo considerable en el ensayo del Anillo J, por lo tanto, se hace necesario imprimir energía de colocación, cuando se esté vaciando el concreto, pero no en exceso, ya que el PEAD podría salir a flote, mientras que en los ensayos de capacidad de llenado y segregación, los resultados cumplieron con los indicadores presentes en la literatura. Según los datos obtenidos con el Reómetro ICAR 5000, se concluye que el concreto con modificación de PEAD, posee un menor esfuerzo de fluencia y un menor esfuerzo máximo de cortante que el del concreto patrón, por tal motivo, se deduce que el concreto posee una mejor trabajabilidad. Además, se midió la resistencia a la compresión, la cual arrojo que esta disminuye en aproximadamente un 16% respecto a la muestra patrón; es una realidad que este es el principal indicador en el diseño de estructuras, sin embargo, el concreto modificado con PEAD es una solución que apoya los objetivos de desarrollo sostenible (ODS) promulgados por la Organización de Naciones Unidas (ONU), debido a que podría disminuir la contaminación por plástico y por tal motivo fomentar la innovación y proteger el planeta.The main objective of the research is to obtain fresh properties of a self-compacting concrete with reclaimed granulated HDPE addition. This will compare the results of the various tests required to find the properties in the fresh state such as filling capacity, throughput, resistance, segregation and rheological properties according by the use of the ICAR 5000 rheometer, and the resistance to compression (property in hardened state). It was decided to use 8%, 10% and 12% of High Density Polyethylene (HDPE) as part of the fine aggregate. The tests carried out are: the slump flow test, it measures indirectly and relates the fluidity of the mixture and is related to the filling capacity, the leakage test under the Slump Flow leads to an indirect concept of the viscosity of the mixture, the Japanese ring or J-Ring test represents an indirect value of the resistance to blocking and fluidity, the L-box to fluidity and the column of segregation indirectly measures the segregation of the mixture. From the results obtained from these tests, it is concluded that the mixture of self-compacting concrete complies with the provisions of Colombian and international regulations, for the use of this concrete. The main characteristics of these concrete are that they present considerable blockage in the Ring test. J, therefore, it is necessary to print placement energy, when the concrete is being poured, but not in excess, since the HDPE could float, while in the filling capacity and segregation tests, the results met with the indicators present in the literature. According to the data obtained by the ICAR 5000 Rheometer, it is concluded that concrete with HDPE modification has a lower creep stress and a lower maximum shear stress than that of standard concrete, for this reason, the concrete is said to have a better workability. In addition, the compressive strength was measured, which showed that it decreases by approximately 16% compared to the standard sample, it is a reality that this is the main indicator in the design of structures, however, Concrete modified with HDPE is a solution that supports the Sustainable Development Goals (SDG) promulgated by the United Nations (UN), because it could reduce plastic pollution and for this reason promote innovation and protect the planet.MaestríaMagister en Ingeniería - EstructurasEl estudio se clasifico como investigación experimental o de laboratorio.Materiales Para la Construcción1 recurso en linea (162 paginas)application/pdfspaUniversidad Nacional De ColombiaBogotá - Ingeniería - Maestría en Ingeniería - EstructurasDepartamento de Ingeniería Civil y AgrícolaFacultad de IngenieríaBogotá, ColombiaUniversidad Nacional de Colombia - Sede Bogotá690 - Construcción de edificios::691 - Materiales de construcciónPEAD (Polietileno De Alta Densidad)ReologiaCompresiónHDPE (High Density Polyethylene)RheologyCompretionEvaluación de las propiedades en estado fresco de un concreto autocompactante con adición de polietileno de alta densidad recuperado granuladoEvaluation of the properties in fresh state of a self-consolidating concrete with the addition of high-density polyethylene recoveredTrabajo de grado - Maestríainfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/acceptedVersionTexthttp://purl.org/redcol/resource_type/TMACI 211.1-91. (2009). Standard Practice For Selecting Proportions For Normal, Heavyweight, And Mass Concrete, 0–15.ACI 237R-07. (2007). Self-Consolidating Concrete, 0–15.Aguado, A., & Salla, J. M. (1987). Los Hormigones Con Polímeros En La Construcción: Propiedades Y Aplicaciones. Informes de la Construcción, 39(389), 61–72.American Concrete Institute. (2002). ACI 116R Terminología Del Cemento Y El Hormigón, 1–124.ASTM Standard C125. (2010). Standard Terminology Relating To Concrete And Concrete Aggregate. ASTM International, (C), 1–6.ASTMC1610. (2015). Standard Test Method For Static Segregation Of Self-Consolidating Concrete Using Column Technique. ASTMC1610, i(c), 4.ASTMC1611. (2009). Standard Test Method For Slump Flow Of Self-Consolidating Concrete. Annual Book of ASTM Standards Volume 04.02, 1–6.ASTMC1621. (2014). Standard Test Method For Passing Ability Of Self-Consolidating Concrete By J-Ring. Annual Book of ASTM Standard, i, 5.Badache, A., Benosman, A. S., Senhadji, Y., & Mouli, M. (2018). Thermo-Physical And Mechanical Characteristics Of Sand-Based Lightweight Composite Mortars With Recycled High-Density Polyethylene (HDPE). Construction and Building Materials, 163, 40–52.Benito, F., Parra, C., Valcuende, M., Miñano, I., & Rodríguez López, C. (2015). Método para cuantificar la segregación en hormigones autocompactantes. Concreto y cemento: Investigación y desarrollo, 6(2), 48–63.Bono Cabre, R. (2012). Diseños Cuasi-Experimentales Y Longitudinales. Universidad de Barcelona. Facultad de Psicología., 1–85.Canales, F. H. De, Alvarado, E. L. De, & Pineda, E. B. (1994). Metodologia De La Investigacion (Vol. 35).Choi, Y. W., Moon, D. J., Kim, Y. J., & Lachemi, M. (2009). Characteristics Of Mortar And Concrete Containing Fine Aggregate Manufactured From Recycled Waste Polyethylene Terephthalate Bottles. Construction and Building Materials, 23(8), 2829–2835.Cortes, E., & Perilla, J. (2014). Estudio Comparativo De Las Características Fisico-Mecanicas De Cuatro Cementos Comerciales Portland Tipo I.EFNARC. (2003). Especificaciones Y Directrices Para El Hormigón Autocompactable, 44(0), 1–33.Faleschini, F., Jiménez, C., Barra, M., Aponte, D., Vázquez, E., & Pellegrino, C. (2014). Rheology Of Fresh Concretes With Recycled Aggregates. Construction and Building Materials, 73, 407–416.Fernandez Bernal, B., & Hernandez Saavedra, K. (2008). Diagnóstico De La Industria Del Cemento En Colombia Y Evaluación De Alternativas Tecnológicas Para El Cumplimiento De La Norma De Emisión De Fuentes Fijas. Universidad De La Salle.Frigione, M. (2010). Recycling Of PET Bottles As Fine Aggregate In Concrete. Waste Management, 30(6), 1101–1106.Galvez Moreno, D. (2015). Robustez De Un Concreto Autocompactable Producido Con Materiales Disponibles En La Región De Monterrey, Nuevo León.Germann Instruments. (s/f-a). ICAR Rheometer. Product Specifications, 71–75.Germann Instruments. (s/f-b). Rheology Using The ICAR Plus – An Introduction, 1–10.Gómez, M. S., Carvajal, A. M., & Santelices, V. (2011). Influencia Del Polietileno De Alta Densidad (PEAD) Usado Como Adición En El Mortero De Cemento. Revista de la Construccion, 10(3), 110–121.Gómez Nemocón, S. A. (2019). Efectos De La Adición De Microesferas Huecas De Vidrio En Concreto Hidráulico.Hinislioglu, S., & Agar, E. (2004). Use Of Waste High Density Polyethylene As Bitumen Modifier In Asphalt Concrete Mix. Materials Letters, 58(3–4), 267–271.Ismail, Z. Z., & AL-Hashmi, E. A. (2008). Use Of Waste Plastic In Concrete Mixture As Aggregate Replacement. Waste Management, 28(11), 2041–2047.Kozikowski, R. L., & Zemajtis, J. Z. (2006). Identifying Incompatible Combinations Of Concrete Materials : - Volume II – Test Protocol.Kurdowski, W. (2014). Cement And Concrete Chemistry. Cement and Concrete Chemistry, 9789400779, 1–700.Martinez Barrera, G., Hernandez zaragoza, J. B., Lopez Lara, T., & Memchaca Campos, C. (2015). Materiales Sustentables Y Reciclados En La Construcción.Morales Carhuayano, M. R. (2016). Estudio Del Comportamiento Del Concreto Incorporando Pet Reciclado. Universidad Nacional De Ingenieria Peru.Newman, J., & Choo, B. seng. (2003). Advanced Concrete Technology. Adimxtures for concrete, mortar and grout, 1–69.NRMCA. (s/f). CIP 37 - Concreto Autocompactante (CAC). Concrete.NTC121. (2014). Especificación De Desempeño Para Cemento Hidráulico. NTC121, (571), 17.NTC1377. (2010). Ingeniería Civil Y Arquitectura. Elaboración Y Curado De Especímenes De Concreto Para Ensayos En El Laboratorio, (571).NTC174. (2000). Concretos. Especificaciones De Los Agregados Para Concreto. Concreto, 22.NTC176. (2019). Ingeniería Civil Y Arquitectura. Método De Ensayo Para Determinar La Densidad Y La Absorción Del Agregado Grueso.NTC237. (2001). Ingeniería Civil Y Arquitectura. Método Para Determinar La Densidad Y La Absorción Del Agregado Fino.NTC3459. (2001). Concretos. Agua Para La Elaboración De Concreto.NTC3674. (2001). Ingeniería Civil Y Arquitectura. Práctica Para La Reducción Del Tamaño De Las Muestras De Agregados, Tomadas En Campo, Para La Realización De Ensayos.NTC396. (1992). Ingeniería Civil Y Arquitectura. Método De Ensayo Para Determinar El Asentamiento Del Concreto.NTC5222. (2003). Concretos. Métodos De Ensayo Para Medir El Flujo Libre, Flujo Restringido Y Segregación En Concretos Autocompactantes.NTC673. (2010). Concretos. Ensayo De Resistencia A La Compresión De Especimenes Cilíndricos De Concreto.NTC77. (2007). Concretos. Método De Ensayo Para El Análisis Por Tamizado De Los Agregados Finos Y Gruesos.NTC92. (1995). Ingeniería Civil Y Arquitectura. Determinación De La Masa Unitaria Y Los Vacíos Entre Partículas De Agregados.Pacheco-Torgal, F., Ding, Y., & Jalali, S. (2012). Properties And Durability Of Concrete Containing Polymeric Wastes (Tyre Rubber And Polyethylene Terephthalate Bottles): An Overview. Construction and Building Materials, 30, 714–724.Palencia Torres, D. G., & Nuñes Rangel, J. J. (2016). Estudio Comparativo Del Concreto Modificado Con Hdpe (Polietileno De Alta Densidad) Reciclado Y Concreto Convencional. Universidad Francisco de Paula Santander.Pešić, N., Živanović, S., Garcia, R., & Papastergiou, P. (2016). Mechanical Properties Of Concrete Reinforced With Recycled HDPE Plastic Fibres. Construction and Building Materials, 115, 362–370.Rivera, G. A. (2009). Concreto Simple. Universidad del cauca.Sánchez De Guzmán, D. (2001). Tecnología del concreto y del mortero (Quinta). Bhsnda.Sea Studios Foundation. (s/f). Guía Inteligente sobre Plásticos.She, B., & Xu, B. (2017). Research On Mechanical Properties Of HDPE Plastic Fiber Reinforced Concrete Structure. Revista de la facultad de ingenieria U.V.C, 32, 669–674.Soroushian, P., Khan, A., & Hsu, J. (1992). Mechanical Properties Of Concrete Materials Reinforced With Polypropylene Or Polyethylene Fibers. ACI Materials Journal, 89(6), 1–6.Thorneycroft, J., Orr, J., Savoikar, P., & Ball, R. J. (2018). Performance Of Structural Concrete With Recycled Plastic Waste As A Partial Replacement For Sand. Construction and Building Materials, 161, 63–69.Zuñiga Diaz, F. A. (2015). Evaluación Del Tereftarato De Polietileno (Pet) Como Agregado En La Elaboración De Mortero Para Ladrillos Y Concreto. Universidad de la salle Colombia.LICENSElicense.txtlicense.txttext/plain; charset=utf-83964https://repositorio.unal.edu.co/bitstream/unal/79616/1/license.txtcccfe52f796b7c63423298c2d3365fc6MD51ORIGINALEVALUACION DE LAS PROPIEDADES EN ESTADO FRESCO DE UN CONCRETO AUTOCOMPACTANTE CON ADICION DE POLIETILENO DE ALTA DENSIDAD RECUPERADO GRANULADO.pdfEVALUACION DE LAS PROPIEDADES EN ESTADO FRESCO DE UN CONCRETO AUTOCOMPACTANTE CON ADICION DE POLIETILENO DE ALTA DENSIDAD RECUPERADO GRANULADO.pdfTesis de Maestría en Ingeniería - Estructurasapplication/pdf5750912https://repositorio.unal.edu.co/bitstream/unal/79616/2/EVALUACION%20DE%20LAS%20PROPIEDADES%20EN%20ESTADO%20FRESCO%20DE%20UN%20CONCRETO%20AUTOCOMPACTANTE%20CON%20ADICION%20DE%20POLIETILENO%20DE%20ALTA%20DENSIDAD%20RECUPERADO%20GRANULADO.pdf61070be6ec5c5e43f1c363a547c3bc9bMD52CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-8805https://repositorio.unal.edu.co/bitstream/unal/79616/3/license_rdf4460e5956bc1d1639be9ae6146a50347MD53THUMBNAILEVALUACION DE LAS PROPIEDADES EN ESTADO FRESCO DE UN CONCRETO AUTOCOMPACTANTE CON ADICION DE POLIETILENO DE ALTA DENSIDAD RECUPERADO GRANULADO.pdf.jpgEVALUACION DE LAS PROPIEDADES EN ESTADO FRESCO DE UN CONCRETO AUTOCOMPACTANTE CON ADICION DE POLIETILENO DE ALTA DENSIDAD RECUPERADO GRANULADO.pdf.jpgGenerated Thumbnailimage/jpeg4844https://repositorio.unal.edu.co/bitstream/unal/79616/4/EVALUACION%20DE%20LAS%20PROPIEDADES%20EN%20ESTADO%20FRESCO%20DE%20UN%20CONCRETO%20AUTOCOMPACTANTE%20CON%20ADICION%20DE%20POLIETILENO%20DE%20ALTA%20DENSIDAD%20RECUPERADO%20GRANULADO.pdf.jpgf084f709968d0e5ad9718f188b695f95MD54unal/79616oai:repositorio.unal.edu.co:unal/796162023-07-21 23:03:57.444Repositorio Institucional Universidad Nacional de Colombiarepositorio_nal@unal.edu.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 |