Wear and corrosion behaviour of Al2O3-TiO2 coatings produced by flame thermal projection
Evaluated the wear resistance and the coatings corrosion behaviour of Al2O3-TiO2 prepared by thermal spraying by flame on AISI 1020 carbon steel substrates, previously coated with an alloy base Ni. For this purpose, were controlled parameters of thermal spraying and the use of powders of similar but...
- Autores:
-
Hector Jaime, Dulce-Moreno
Ferrer, Martha
Vargas, Fabio
- Tipo de recurso:
- Article of journal
- Fecha de publicación:
- 2017
- Institución:
- UNIVERSIDAD FRANCISCO DE PAULA SANTANDER
- Repositorio:
- Repositorio Digital UFPS
- Idioma:
- eng
- OAI Identifier:
- oai:repositorio.ufps.edu.co:ufps/1487
- Acceso en línea:
- http://repositorio.ufps.edu.co/handle/ufps/1487
- Palabra clave:
- Rights
- openAccess
- License
- Atribución 4.0 Internacional (CC BY 4.0)
| Summary: | Evaluated the wear resistance and the coatings corrosion behaviour of Al2O3-TiO2 prepared by thermal spraying by flame on AISI 1020 carbon steel substrates, previously coated with an alloy base Ni. For this purpose, were controlled parameters of thermal spraying and the use of powders of similar but different chemical composition is taken as a variable commercial reference for ceramic coating. SEM images allowed to know the morphology of the powders and coatings. Electrochemical techniques (Tafel) were applied to evaluate the protection against corrosion. Coatings were tested for wear with a tribometer configuration bola-disco. It was determined that the phases present in coatings are directly relate to the behaviour against corrosion and wear them. Keywords: wear, corrosion, thermal imaging. |
|---|