Steel cable failure analysis

This article describes the failure analysis performed on two samples of steel cables that suffered sudden failure under normal workload conditions. The fault was caused by a load less than the nominal capacity. After optical inspection it was evidenced that the fault was caused by fatigue of the mat...

Full description

Autores:
Ossa, E. A.
Paniagua, M A.
Tipo de recurso:
Fecha de publicación:
2005
Institución:
Universidad EAFIT
Repositorio:
Repositorio EAFIT
Idioma:
spa
OAI Identifier:
oai:repository.eafit.edu.co:10784/14574
Acceso en línea:
http://hdl.handle.net/10784/14574
Palabra clave:
Cables
Fault Analysis
Forensic Mechanics
Mechanical Tests
Metallography
Fractography
Cables
Análisis De Fallas
Mecánica Forense
Ensayos Mecánicos
Metalografía
Fractografía
Rights
License
Copyright (c) 2005 E. A. Ossa, M A. Paniagua
id REPOEAFIT2_cd200fe4f1d263b5a18573df85f82507
oai_identifier_str oai:repository.eafit.edu.co:10784/14574
network_acronym_str REPOEAFIT2
network_name_str Repositorio EAFIT
repository_id_str
spelling Medellín de: Lat: 06 15 00 N degrees minutes Lat: 6.2500 decimal degrees Long: 075 36 00 W degrees minutes Long: -75.6000 decimal degrees2005-12-012019-11-22T19:22:14Z2005-12-012019-11-22T19:22:14Z2256-43141794-9165http://hdl.handle.net/10784/14574This article describes the failure analysis performed on two samples of steel cables that suffered sudden failure under normal workload conditions. The fault was caused by a load less than the nominal capacity. After optical inspection it was evidenced that the fault was caused by fatigue of the material of one of the cables.Este artículo describe el análisis de falla realizado en dos muestras de cables de acero que sufrieron falla súbita bajo condiciones de carga de trabajo normales. La falla fue causada por una carga menor a la capacidad nominal. Luego de inspección óptica se evidenció que la falla fue ocasionada por fatiga del material de uno de los cables.application/pdfspaUniversidad EAFIThttp://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/498http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/498Copyright (c) 2005 E. A. Ossa, M A. PaniaguaAcceso abiertohttp://purl.org/coar/access_right/c_abf2instname:Universidad EAFITreponame:Repositorio Institucional Universidad EAFITIngeniería y Ciencia; Vol 1, No 2 (2005)Steel cable failure analysisAnálisis de falla en cable de aceroarticleinfo:eu-repo/semantics/articlepublishedVersioninfo:eu-repo/semantics/publishedVersionArtículohttp://purl.org/coar/version/c_970fb48d4fbd8a85http://purl.org/coar/resource_type/c_6501http://purl.org/coar/resource_type/c_2df8fbb1CablesFault AnalysisForensic MechanicsMechanical TestsMetallographyFractographyCablesAnálisis De FallasMecánica ForenseEnsayos MecánicosMetalografíaFractografíaOssa, E. A.Paniagua, M A.University of NottinghamUniversidad EAFITIngeniería y Ciencia1297103ing.cienc.ORIGINALdocument (2).pdfdocument (2).pdfTexto completo PDFapplication/pdf254934https://repository.eafit.edu.co/bitstreams/c76963ab-4722-4257-a5da-471946f5adb4/download114ee6463b2595379ac9d85b2c33eb00MD52articulo.htmlarticulo.htmlTexto completo HTMLtext/html373https://repository.eafit.edu.co/bitstreams/f999d747-5390-4012-8809-348b6ae8e7f6/downloaddfbfc703ecb6c81f64a86bc78d91e99bMD53THUMBNAILminaitura-ig_Mesa de trabajo 1.jpgminaitura-ig_Mesa de trabajo 1.jpgimage/jpeg265796https://repository.eafit.edu.co/bitstreams/6b92575f-2f9e-4352-a4c2-5ea3514afdb0/downloadda9b21a5c7e00c7f1127cef8e97035e0MD5110784/14574oai:repository.eafit.edu.co:10784/145742020-02-11 21:01:03.011open.accesshttps://repository.eafit.edu.coRepositorio Institucional Universidad EAFITrepositorio@eafit.edu.co
dc.title.eng.fl_str_mv Steel cable failure analysis
dc.title.spa.fl_str_mv Análisis de falla en cable de acero
title Steel cable failure analysis
spellingShingle Steel cable failure analysis
Cables
Fault Analysis
Forensic Mechanics
Mechanical Tests
Metallography
Fractography
Cables
Análisis De Fallas
Mecánica Forense
Ensayos Mecánicos
Metalografía
Fractografía
title_short Steel cable failure analysis
title_full Steel cable failure analysis
title_fullStr Steel cable failure analysis
title_full_unstemmed Steel cable failure analysis
title_sort Steel cable failure analysis
dc.creator.fl_str_mv Ossa, E. A.
Paniagua, M A.
dc.contributor.author.spa.fl_str_mv Ossa, E. A.
Paniagua, M A.
dc.contributor.affiliation.spa.fl_str_mv University of Nottingham
Universidad EAFIT
dc.subject.keyword.eng.fl_str_mv Cables
Fault Analysis
Forensic Mechanics
Mechanical Tests
Metallography
Fractography
topic Cables
Fault Analysis
Forensic Mechanics
Mechanical Tests
Metallography
Fractography
Cables
Análisis De Fallas
Mecánica Forense
Ensayos Mecánicos
Metalografía
Fractografía
dc.subject.keyword.spa.fl_str_mv Cables
Análisis De Fallas
Mecánica Forense
Ensayos Mecánicos
Metalografía
Fractografía
description This article describes the failure analysis performed on two samples of steel cables that suffered sudden failure under normal workload conditions. The fault was caused by a load less than the nominal capacity. After optical inspection it was evidenced that the fault was caused by fatigue of the material of one of the cables.
publishDate 2005
dc.date.issued.none.fl_str_mv 2005-12-01
dc.date.available.none.fl_str_mv 2019-11-22T19:22:14Z
dc.date.accessioned.none.fl_str_mv 2019-11-22T19:22:14Z
dc.date.none.fl_str_mv 2005-12-01
dc.type.eng.fl_str_mv article
info:eu-repo/semantics/article
publishedVersion
info:eu-repo/semantics/publishedVersion
dc.type.coarversion.fl_str_mv http://purl.org/coar/version/c_970fb48d4fbd8a85
dc.type.coar.fl_str_mv http://purl.org/coar/resource_type/c_6501
http://purl.org/coar/resource_type/c_2df8fbb1
dc.type.local.spa.fl_str_mv Artículo
status_str publishedVersion
dc.identifier.issn.none.fl_str_mv 2256-4314
1794-9165
dc.identifier.uri.none.fl_str_mv http://hdl.handle.net/10784/14574
identifier_str_mv 2256-4314
1794-9165
url http://hdl.handle.net/10784/14574
dc.language.iso.spa.fl_str_mv spa
language spa
dc.relation.isversionof.none.fl_str_mv http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/498
dc.relation.uri.none.fl_str_mv http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/498
dc.rights.eng.fl_str_mv Copyright (c) 2005 E. A. Ossa, M A. Paniagua
dc.rights.coar.fl_str_mv http://purl.org/coar/access_right/c_abf2
dc.rights.local.spa.fl_str_mv Acceso abierto
rights_invalid_str_mv Copyright (c) 2005 E. A. Ossa, M A. Paniagua
Acceso abierto
http://purl.org/coar/access_right/c_abf2
dc.format.none.fl_str_mv application/pdf
dc.coverage.spatial.eng.fl_str_mv Medellín de: Lat: 06 15 00 N degrees minutes Lat: 6.2500 decimal degrees Long: 075 36 00 W degrees minutes Long: -75.6000 decimal degrees
dc.publisher.spa.fl_str_mv Universidad EAFIT
dc.source.none.fl_str_mv instname:Universidad EAFIT
reponame:Repositorio Institucional Universidad EAFIT
dc.source.spa.fl_str_mv Ingeniería y Ciencia; Vol 1, No 2 (2005)
instname_str Universidad EAFIT
institution Universidad EAFIT
reponame_str Repositorio Institucional Universidad EAFIT
collection Repositorio Institucional Universidad EAFIT
bitstream.url.fl_str_mv https://repository.eafit.edu.co/bitstreams/c76963ab-4722-4257-a5da-471946f5adb4/download
https://repository.eafit.edu.co/bitstreams/f999d747-5390-4012-8809-348b6ae8e7f6/download
https://repository.eafit.edu.co/bitstreams/6b92575f-2f9e-4352-a4c2-5ea3514afdb0/download
bitstream.checksum.fl_str_mv 114ee6463b2595379ac9d85b2c33eb00
dfbfc703ecb6c81f64a86bc78d91e99b
da9b21a5c7e00c7f1127cef8e97035e0
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
repository.name.fl_str_mv Repositorio Institucional Universidad EAFIT
repository.mail.fl_str_mv repositorio@eafit.edu.co
_version_ 1814110659284041728

Publicaciones similares