Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol

In this work, low density polyethylene (LDPE) was modified in the melt state with a maleinized hyperbranched polyester polyol (HBPAM), using several proportions of dicumyl peroxide (0.5, 1.0, 1.5 and 2.0 %). Infrared analysis showed the signals of OH, C=O, -COOR and -C=C- groups of the HBPAM in the...

Full description

Autores:
Ararat, Carlos A
Murillo, Edwin A.
Tipo de recurso:
Fecha de publicación:
2016
Institución:
Universidad EAFIT
Repositorio:
Repositorio EAFIT
Idioma:
spa
OAI Identifier:
oai:repository.eafit.edu.co:10784/11287
Acceso en línea:
http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/3220
http://hdl.handle.net/10784/11287
Palabra clave:
low density polyethylene
hyperbranched polyester
functionalization
thermal analysis
mechanical properties
83.80.Sg
61.25.hk
81.05.Lg
82.35.Lr
engineering
polietileno de baja densidad
poliéster altamente ramificado
funcionalización
análisis térmico
propiedades mecánicas
Rights
License
Copyright (c) 2016 Ingeniería y Ciencia | ing.cienc.
id REPOEAFIT2_999d3a20633c80b3edc2da47ee07801e
oai_identifier_str oai:repository.eafit.edu.co:10784/11287
network_acronym_str REPOEAFIT2
network_name_str Repositorio EAFIT
repository_id_str
dc.title.eng.fl_str_mv Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
dc.title.spa.fl_str_mv Polietileno de baja densidad funcionalizado con un poliéster poliol altamente ramificado maleinizado
title Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
spellingShingle Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
low density polyethylene
hyperbranched polyester
functionalization
thermal analysis
mechanical properties
83.80.Sg
61.25.hk
81.05.Lg
82.35.Lr
engineering
polietileno de baja densidad
poliéster altamente ramificado
funcionalización
análisis térmico
propiedades mecánicas
title_short Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
title_full Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
title_fullStr Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
title_full_unstemmed Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
title_sort Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester Polyol
dc.creator.fl_str_mv Ararat, Carlos A
Murillo, Edwin A.
dc.contributor.author.none.fl_str_mv Ararat, Carlos A
Murillo, Edwin A.
dc.contributor.affiliation.spa.fl_str_mv Universidad Francisco de Paula Santander
dc.subject.keyword.eng.fl_str_mv low density polyethylene
hyperbranched polyester
functionalization
thermal analysis
mechanical properties
83.80.Sg
61.25.hk
81.05.Lg
82.35.Lr
topic low density polyethylene
hyperbranched polyester
functionalization
thermal analysis
mechanical properties
83.80.Sg
61.25.hk
81.05.Lg
82.35.Lr
engineering
polietileno de baja densidad
poliéster altamente ramificado
funcionalización
análisis térmico
propiedades mecánicas
dc.subject.keyword.spa.fl_str_mv engineering
polietileno de baja densidad
poliéster altamente ramificado
funcionalización
análisis térmico
propiedades mecánicas
description In this work, low density polyethylene (LDPE) was modified in the melt state with a maleinized hyperbranched polyester polyol (HBPAM), using several proportions of dicumyl peroxide (0.5, 1.0, 1.5 and 2.0 %). Infrared analysis showed the signals of OH, C=O, -COOR and -C=C- groups of the HBPAM in the spectra of the functionalized samples (LDPE-g-HBPAM). Grafting degree (GD) was between 9.14 and 9.82 %. Melt flow index of the samples LDPE-g-HBPAM was lower than that of the LDPE, and it did not exhibit dependency on the dicumyl peroxide content and GD. Exceptfor the sample obtained with a 2.0 % of dicumyl peroxide, all melting temperatures of the samples of LDPE-g-HBPAM were similar to that of the LDPE. The melting enthalpy of the samples LDPE-g-HBPAM decreased with the concentration of dicumyl peroxide and GD. The tensile modulus of these samples was higher than that of LDPE, but the elongation at break was lower.
publishDate 2016
dc.date.issued.none.fl_str_mv 2016-02-22
dc.date.available.none.fl_str_mv 2017-04-03T16:10:27Z
dc.date.accessioned.none.fl_str_mv 2017-04-03T16:10:27Z
dc.date.none.fl_str_mv 2016-02-22
dc.type.eng.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
article
publishedVersion
dc.type.coarversion.fl_str_mv http://purl.org/coar/version/c_970fb48d4fbd8a85
dc.type.coar.fl_str_mv http://purl.org/coar/resource_type/c_6501
http://purl.org/coar/resource_type/c_2df8fbb1
dc.type.local.spa.fl_str_mv Artículo
status_str publishedVersion
dc.identifier.issn.none.fl_str_mv 2256-4314
1794–9165
dc.identifier.uri.none.fl_str_mv http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/3220
http://hdl.handle.net/10784/11287
dc.identifier.doi.none.fl_str_mv 10.17230/ingciencia.12.23.7
identifier_str_mv 2256-4314
1794–9165
10.17230/ingciencia.12.23.7
url http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/3220
http://hdl.handle.net/10784/11287
dc.language.iso.none.fl_str_mv spa
language spa
dc.relation.isversionof.none.fl_str_mv http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/3220
dc.rights.spa.fl_str_mv Copyright (c) 2016 Ingeniería y Ciencia | ing.cienc.
http://creativecommons.org/licenses/by/4.0
dc.rights.coar.fl_str_mv http://purl.org/coar/access_right/c_abf2
dc.rights.local.spa.fl_str_mv Acceso abierto
rights_invalid_str_mv Copyright (c) 2016 Ingeniería y Ciencia | ing.cienc.
http://creativecommons.org/licenses/by/4.0
Acceso abierto
http://purl.org/coar/access_right/c_abf2
dc.format.none.fl_str_mv application/pdf
dc.publisher.spa.fl_str_mv Universidad EAFIT
dc.source.none.fl_str_mv instname:Universidad EAFIT
reponame:Repositorio Institucional Universidad EAFIT
dc.source.eng.fl_str_mv Ingeniería y Ciencia | ing.cienc.; Vol 12, No 23 (2016); 127-144
dc.source.spa.fl_str_mv Ingeniería y Ciencia | ing.cienc.; Vol 12, No 23 (2016); 127-144
instname_str Universidad EAFIT
institution Universidad EAFIT
reponame_str Repositorio Institucional Universidad EAFIT
collection Repositorio Institucional Universidad EAFIT
bitstream.url.fl_str_mv https://repository.eafit.edu.co/bitstreams/6cd2609a-e3d9-452c-86d9-e5a431129a65/download
https://repository.eafit.edu.co/bitstreams/2a6c1077-664a-4896-9bbb-c8886413f6f0/download
https://repository.eafit.edu.co/bitstreams/e70b0996-b06d-4e23-bcb8-f0636101e2c0/download
bitstream.checksum.fl_str_mv 29b8a81485c61739efa109282d27f7cf
42dd44196a2e7e3a967bc3727678fb2a
da9b21a5c7e00c7f1127cef8e97035e0
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
repository.name.fl_str_mv Repositorio Institucional Universidad EAFIT
repository.mail.fl_str_mv repositorio@eafit.edu.co
_version_ 1814110513328553984
spelling 2016-02-222017-04-03T16:10:27Z2016-02-222017-04-03T16:10:27Z2256-43141794–9165http://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/3220http://hdl.handle.net/10784/1128710.17230/ingciencia.12.23.7In this work, low density polyethylene (LDPE) was modified in the melt state with a maleinized hyperbranched polyester polyol (HBPAM), using several proportions of dicumyl peroxide (0.5, 1.0, 1.5 and 2.0 %). Infrared analysis showed the signals of OH, C=O, -COOR and -C=C- groups of the HBPAM in the spectra of the functionalized samples (LDPE-g-HBPAM). Grafting degree (GD) was between 9.14 and 9.82 %. Melt flow index of the samples LDPE-g-HBPAM was lower than that of the LDPE, and it did not exhibit dependency on the dicumyl peroxide content and GD. Exceptfor the sample obtained with a 2.0 % of dicumyl peroxide, all melting temperatures of the samples of LDPE-g-HBPAM were similar to that of the LDPE. The melting enthalpy of the samples LDPE-g-HBPAM decreased with the concentration of dicumyl peroxide and GD. The tensile modulus of these samples was higher than that of LDPE, but the elongation at break was lower.En este trabajo, polietileno de baja densidad (PEBD) fue modificado en estado fundido con un poliester poliol altamente ramificado maleinizado (HBPAM), usando varias proporciones de peróxido de dicumilo (0.5, 1.0, 1.5 y 2.0%). El análisis infrarrojo mostró las señales de grupos OH, C=O, -COOR y -C=C- del HBPAM en el espectro de las muestras funcionalizadas (PEBD-g-HBPAM). El grado de injerto (GI) fue entre 9.14 y 9.82%. El índice de fluidez de las muestras PEBD-g-HBPAM fue más bajo que el del PEBD, y no exhibió una dependencia con el contenido de peróxido de dicumilo y GI. Excepto para la muestra obtenida con un 2.0% de peróxido de dicumilo, todas las temperaturas de fusión de las muestras de PEBD-g-HBPAM fueron similares a la del PEBD. La entalpia de fusión de las muestras de PEBD-g-HBPAM disminuyó con la concentración de peróxido de dicumilo y GI. El módulo ténsil de estas muestras fue más alto que el del PEBD, pero la elongación a la ruptura fue más baja.application/pdfspaUniversidad EAFIThttp://publicaciones.eafit.edu.co/index.php/ingciencia/article/view/3220Copyright (c) 2016 Ingeniería y Ciencia | ing.cienc.http://creativecommons.org/licenses/by/4.0Acceso abiertohttp://purl.org/coar/access_right/c_abf2instname:Universidad EAFITreponame:Repositorio Institucional Universidad EAFITIngeniería y Ciencia | ing.cienc.; Vol 12, No 23 (2016); 127-144Ingeniería y Ciencia | ing.cienc.; Vol 12, No 23 (2016); 127-144Functionalized Low Density Polyethylene with Maleinized Hyperbranched Polyester PolyolPolietileno de baja densidad funcionalizado con un poliéster poliol altamente ramificado maleinizadoinfo:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionarticlepublishedVersionArtículohttp://purl.org/coar/version/c_970fb48d4fbd8a85http://purl.org/coar/resource_type/c_6501http://purl.org/coar/resource_type/c_2df8fbb1low density polyethylenehyperbranched polyesterfunctionalizationthermal analysismechanical properties83.80.Sg61.25.hk81.05.Lg82.35.Lrengineeringpolietileno de baja densidadpoliéster altamente ramificadofuncionalizaciónanálisis térmicopropiedades mecánicasArarat, Carlos AMurillo, Edwin A.Universidad Francisco de Paula SantanderIngeniería y Ciencia1223127144ing.ciencORIGINALdocument (35).pdfdocument (35).pdfTexto completo PDFapplication/pdf526286https://repository.eafit.edu.co/bitstreams/6cd2609a-e3d9-452c-86d9-e5a431129a65/download29b8a81485c61739efa109282d27f7cfMD52articulo.htmlarticulo.htmlTexto completo HTMLtext/html374https://repository.eafit.edu.co/bitstreams/2a6c1077-664a-4896-9bbb-c8886413f6f0/download42dd44196a2e7e3a967bc3727678fb2aMD54THUMBNAILminaitura-ig_Mesa de trabajo 1.jpgminaitura-ig_Mesa de trabajo 1.jpgimage/jpeg265796https://repository.eafit.edu.co/bitstreams/e70b0996-b06d-4e23-bcb8-f0636101e2c0/downloadda9b21a5c7e00c7f1127cef8e97035e0MD5310784/11287oai:repository.eafit.edu.co:10784/112872020-07-17 14:49:11.593open.accesshttps://repository.eafit.edu.coRepositorio Institucional Universidad EAFITrepositorio@eafit.edu.co