Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos

In the present study the sludge ashes coming from water treatment operations of the treatment plant of Triple A company, in Barranquilla city are analyzed. These analyzes are intended to determine the usefulness of sludge as a hydraulic binder, creating an ecological arrangement of thereof, and help...

Full description

Autores:: Pacheco Tuesca, María Fernanda
Utria Lafaurie, Marledys

Tipo de recurso:: Trabajo de grado de pregrado

Fecha de publicación:: 2019

Institución:: Corporación Universidad de la Costa

Repositorio:: REDICUC - Repositorio CUC

Idioma:: spa

id	RCUC2_fe235ebfa48c326e07f558f5cfa9f63f
oai_identifier_str	oai:repositorio.cuc.edu.co:11323/5298
network_acronym_str	RCUC2
network_name_str	REDICUC - Repositorio CUC
repository_id_str
dc.title.spa.fl_str_mv	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
title	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
spellingShingle	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos Cenizas de lodo Material cementante complementario Concreto Resistencia a compresión Sludge ash Supplementary cementitious material Pozzolana Concrete Compressive strength
title_short	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
title_full	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
title_fullStr	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
title_full_unstemmed	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
title_sort	Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos
dc.creator.fl_str_mv	Pacheco Tuesca, María Fernanda Utria Lafaurie, Marledys
dc.contributor.advisor.spa.fl_str_mv	Cano, Heidis De Paoli, Fabricio
dc.contributor.author.spa.fl_str_mv	Pacheco Tuesca, María Fernanda Utria Lafaurie, Marledys
dc.subject.spa.fl_str_mv	Cenizas de lodo Material cementante complementario Concreto Resistencia a compresión Sludge ash Supplementary cementitious material Pozzolana Concrete Compressive strength
topic	Cenizas de lodo Material cementante complementario Concreto Resistencia a compresión Sludge ash Supplementary cementitious material Pozzolana Concrete Compressive strength
description	In the present study the sludge ashes coming from water treatment operations of the treatment plant of Triple A company, in Barranquilla city are analyzed. These analyzes are intended to determine the usefulness of sludge as a hydraulic binder, creating an ecological arrangement of thereof, and helping to minimize the extractive activities of raw materials used in the construction industry. Specimens were manufactured with a 5% and 10% replacement of cement by sludge ashes and a control mixture that required a theoretical compression strength of 4000 Psi (28 MPa) to be compared with the results and behavior of the modified concrete. The results from this study showed that sludge ashes from the water treatment can be replaced in small percentages with the Portland cement in concrete mixture without negatively affecting the compressive strength. It was obtained that the specimens tested for compression reach 3000 psi, which corresponds to a concrete of moderate resistance, which meets the requirements to be used in the construction of buildings of small housing type and simple buildings.
publishDate	2019
dc.date.accessioned.none.fl_str_mv	2019-09-25T13:54:04Z
dc.date.available.none.fl_str_mv	2019-09-25T13:54:04Z
dc.date.issued.none.fl_str_mv	2019
dc.type.spa.fl_str_mv	Trabajo de grado - Pregrado
dc.type.coar.spa.fl_str_mv	http://purl.org/coar/resource_type/c_7a1f
dc.type.content.spa.fl_str_mv	Text
dc.type.driver.spa.fl_str_mv	info:eu-repo/semantics/bachelorThesis
dc.type.redcol.spa.fl_str_mv	http://purl.org/redcol/resource_type/TP
dc.type.version.spa.fl_str_mv	info:eu-repo/semantics/acceptedVersion
format	http://purl.org/coar/resource_type/c_7a1f
status_str	acceptedVersion
dc.identifier.uri.spa.fl_str_mv	http://hdl.handle.net/11323/5298
dc.identifier.instname.spa.fl_str_mv	Corporación Universidad de la Costa
dc.identifier.reponame.spa.fl_str_mv	REDICUC - Repositorio CUC
dc.identifier.repourl.spa.fl_str_mv	https://repositorio.cuc.edu.co/
url	http://hdl.handle.net/11323/5298 https://repositorio.cuc.edu.co/
identifier_str_mv	Corporación Universidad de la Costa REDICUC - Repositorio CUC
dc.language.iso.none.fl_str_mv	spa
language	spa
dc.relation.references.spa.fl_str_mv	Aldana Tique, A. J. (2017). Propuesta para el tratamiento y aprovechamiento de lodos en una PTAP convencional. Caso de estudio: Planta de tratamiento de agua potable de el Espinal- Tolima. Universidad de La Salle, 1(Facultad de Ingenieria ambiental y sanitaria.), 106. Retrieved from http://repository.lasalle.edu.co/bitstream/handle/10185/22405/41112712_2017.pdf?sequence=1 Amaris, N. A., & Rondo, V. (2009). USO DEL SILICATO DE SODIO COMO ADICIÓN NATURAL DEL CONCRETO HIDRAULICO. Universidad de La Salle. Bermeo Barreto, A. M., & Idrovo Heredia, E. P. (2014). APROVECHAMIENTO DE LODOS DESHIDRATADOS GENERADOS EN PLANTAS DE TRATAMIENTO DE AGUA POTABLE Y RESIDUAL COMO AGREGADO PARA MATERIALES DE CONSTRUCCIÓN.”. Castilla, J. D. (2018, December 28). Este año hubo un incremento en la producción de cemento gris de 6,3%. La Republica. Retrieved from https://www.larepublica.co/economia/este-ano-hubo-un-incremento-en-la-produccion-de-cemento-gris-de-63-2810131 Centro de estudios y expermientación de obras públicas. (2011a). Blast Furnace Slag. Retrieved from http://www.cedexmateriales.es/catalogo-de-residuos/29/humo-de-silice/ Centro de estudios y expermientación de obras públicas. (2011b). Cenizas Volantes. Retrieved from http://www.cedexmateriales.es/catalogo-de-residuos/24/diciembre-2011/ Centro de estudios y expermientación de obras públicas. (2012). Humo de Silice. Retrieved from http://www.cedexmateriales.es/catalogo-de-residuos/29/humo-de-silice/ Daza Marquez, N., & Medina Sanchez, A. (2018). Analisis comparativo del contenido de oxidos. 1. Universidad de la Costa. Retrieved from http://hdl.handle.net/11323/301 de Oliveira Andrade, J. J., Wenzel, M. C., da Rocha, G. H., & da Silva, S. R. (2018). Performance of rendering mortars containing sludge from water treatment plants as fine recycled aggregate. Journal of Cleaner Production, 192, 159–168. https://doi.org/10.1016/j.jclepro.2018.04.246 Demanda, L. A., Carlos, J., & Alcaraz, D. (2008). La industria del cemento en colombia, 1–53. Fernández, A. G. R. (2003). “manejo de lodos producidos en la planta de tratamiento de agua potable, planta ii, del municipio de cartago, valle.” Universidad Nacional de Colombia. Garcia Meseguer, A. (2001). Hormigon armado. (Fundación escuela de la edificación Maestro Victoria, Ed.) (3rd ed.). Madrid: Toran S.A. Geyer, A. L. B. (2001). Contribuição ao estudo da disposição final e aproveitamento da cinza de lodo de estações de tratamento de esgotos sanitários como adição ao concreto, 216. Gutiérrez-Rosero, J. A., Ramírez-Fajardo, Á. I., Rivas, R., Linares, B., & Paredes, D. (2014). Tratamiento de lodos generados en el proceso convencional de potabilización de agua. Ingenierías Universidad de Medellín, 13(25), 13–27. INVE 410-07. (2007). Resistencia a La Compresion De Cilindros De Concreto, 16. Li, Z., Jiang, N., Wu, F., & Zhou, Z. (2013a). Experimental investigation of phosphorus adsorption capacity of the waterworks sludges from five cities in China. Ecological Engineering, 53, 165–172. https://doi.org/10.1016/J.ECOLENG.2012.12.038 Li, Z., Jiang, N., Wu, F., & Zhou, Z. (2013b). Experimental investigation of phosphorus adsorption capacity of the waterworks sludges from five cities in China. Ecological Engineering, 53(April 2013), 165–172. https://doi.org/10.1016/j.ecoleng.2012.12.038 Marroquin Moscoso, K. J. (2018). EVALUACIÓN DEL EFECTO EN LA RESISTENCIA A LA COMPRESIÓN DEL CEMENTO TIPO USO GENERAL, POR LA ADICIÓN DE PUZOLANA, FLY ASH Y CALIZA, A DIFERENTE TAMAÑO DE PARTÍCULA. Universidad de San Carlos de Guatemala. Monteiro, P. J. M., & Mehta, P. K. (2004). Concreto. (Instituto Mexicano de Cemento y Concreto, Ed.). Mexico. Retrieved from http://imcyc.com/redcyc/imcyc/biblioteca_digital/CONCRETO_ESTRUCTURA_PROPIEDADES_Y_MATERIALES.pdf Naisma Hernández, Mayda Ulloa, Yuri Almaguer, Y. R. (2014). EVALUACIÓN AMBIENTAL ASOCIADA A LA EXPLOTACIÓN DEL YACIMIENTO DE MATERIALES DE CONSTRUCCIÓN LA INAGUA, GUANTÁNAMO, CUBA, (38), 146–158. Norma Tecnica Colombiana 121. Especificación de deempeño para el cemento hidraulico (2014). Colombia. O’Kelly, B. C. (2010). Landfill Disposal of Alum Water Treatment Residues: Some Pertinent Geoengineering Properties. Journal of Residuals Science & Technology;7 (2): 95-113 Apr2010, 7(2), 95–113. Retrieved from http://www.thomsoninnovation.com/tip-innovation/%5Cnhttp://www.thomsoninnovation.com/tip-innovation/recordView.do?datasource=WOK&category=LIT&selRecord=1&totalRecords=1&databaseIds=WOS,CCC&idType=uid/recordid&recordKeys=000276957000004/WOS:000276957000004 Pacheco Jimenez, D., & Varela Gomez, K. V. (2019). ANÁLISIS ESTADISTICO COMPARATIVO DEL CONTENIDO DE ÓXIDOS PRESENTES EN LODOS SIN CALCINAR, LODOS CALCINADOS Y CEMENTO PORTLAND. Universidad de la costa. Pereira, Y. A., Velasquez, S. R., Valencia, J. J., Ramírez, M. C., & Muñoz, A. P. (2017). Análisis comparativo de la concentración de óxidos presentes en el cemento portland y lodos de plantas de tratamiento de agua potable. Afinidad, 74(577), 68–73. Retrieved from http://www.raco.cat/index.php/afinidad/article/view/320832/411315 Reglamento Colombiano de construcción Sismo Resistente. TITULO C: Concreto estructural (2010). Colombia. Rivera, G. (2008). Manejabilidad del concreto. In Manejabilidad del concreto (pp. 83–103). Romero Quintero, A. F., & Hernandez Rico, A. camilo. (2014). DISEÑO DE MEZCLAS DE HORMIGÓN POR EL MÉTODO A.C.I. Y EFECTOS DE LA ADICIÓN DE CENIZAS VOLANTES DE TERMOTASAJERO EN LA RESISTENCIA A LA COMPRESIÓN. Universidad de Santo Tomas. Sales, A., & de Souza, F. R. (2009). Concretes and mortars recycled with water treatment sludge and construction and demolition rubble. Construction and Building Materials, 23(6), 2362–2370. https://doi.org/10.1016/j.conbuildmat.2008.11.001 Sales, A., De Souza, F. R., & Almeida, F. D. C. R. (2011). Mechanical properties of concrete produced with a composite of water treatment sludge and sawdust. Construction and Building Materials, 25(6), 2793–2798. https://doi.org/10.1016/j.conbuildmat.2010.12.057 Sales, A., De Souza, F. R., Dos Santos, W. N., Zimer, A. M., & Almeida, F. D. C. R. (2010). Lightweight composite concrete produced with water treatment sludge and sawdust: Thermal properties and potential application. Construction and Building Materials, 24(12), 2446–2453. https://doi.org/10.1016/j.conbuildmat.2010.06.012 Sterba, F. (2018). El ordenador de procesos en la industria del cemento, 20. Tafarel, N. F., Macioski, G., De Carvalho, K. Q., Nagalli, A., De Freitas, D. C., & Passig, F. H. (2016). Avaliação das propriedades do concreto devido à incorporação de lodo de estação de tratamento de água. Revista Materia, 21(4), 974–986. https://doi.org/10.1590/S1517-707620160004.0090 Técnica, N., Volantes, C., & Naturales, Y. P. (2017). NTC, (571). Torres, P., Hernández, D., & Paredes, D. (2012). Uso productivo de lodos de plantas de tratamiento de agua potable en la fabricación de ladrillos cerámicos. Revista Ingenieria de Construccion, 27(3), 145–154. https://doi.org/10.4067/S0718-50732012000300003 TRIPLE A. (2017). Etapas de la potabilización del Agua 1. Unicef. (2006). El agua potable y el saneamiento básico en los planes de desarrollo. La infancia, el agua y el saneamiento básico en los planes de desarrollo departamentales y municipales. Retrieved from http://www.unicef.org.co/pdf/Agua3.pdf Universidad Pedagogica y Tecnologica de Colombia. (2017). Materiales cementantes suplementarios. Retrieved from http://www.uptc.edu.co/docentes/oscar_gutierrez/En_Concreto/Materia5 Valderama, C. P., Torres Agredo, J., & Mejia de Gutierrez, R. (2011). Características de desempeño de un concreto adicionado con cenizas volantesde alto nivel de inquemados. Universidad Nacional de colombia. Retrieved from https://revistas.unal.edu.co/index.php/ingeinv/rt/printerFriendly/20519/33850?fbclid=IwAR1VN-hRwC6JEuzqhvdyqaRxB9S56zRLpxNG6ZP6HdR7XWMWOHDyOe-JIJA Zhao, Y. Q. (2003). Correlations between floc physical properties and optimum polymer dosage in alum sludge conditioning and dewatering. Chemical Engineering Journal, 92(1–3), 227–235. https://doi.org/10.1016/S1385-8947(02)00253-X
dc.rights.spa.fl_str_mv	Attribution-NonCommercial-ShareAlike 4.0 International
dc.rights.uri.spa.fl_str_mv	http://creativecommons.org/licenses/by-nc-sa/4.0/
dc.rights.accessrights.spa.fl_str_mv	info:eu-repo/semantics/openAccess
dc.rights.coar.spa.fl_str_mv	http://purl.org/coar/access_right/c_abf2
rights_invalid_str_mv	Attribution-NonCommercial-ShareAlike 4.0 International http://creativecommons.org/licenses/by-nc-sa/4.0/ http://purl.org/coar/access_right/c_abf2
eu_rights_str_mv	openAccess
dc.publisher.spa.fl_str_mv	Universidad de la Costa
dc.publisher.program.spa.fl_str_mv	Ingeniería Civil
institution	Corporación Universidad de la Costa
bitstream.url.fl_str_mv	https://repositorio.cuc.edu.co/bitstreams/eaa9a72a-4715-4e3a-8299-26a00b514d36/download https://repositorio.cuc.edu.co/bitstreams/068cf094-4699-4ec4-a60f-3962ef923096/download https://repositorio.cuc.edu.co/bitstreams/a812a685-27e3-422b-b5c8-14f2c3ba1976/download https://repositorio.cuc.edu.co/bitstreams/89002dd9-99a5-4e3c-9ead-5ca6132eef74/download https://repositorio.cuc.edu.co/bitstreams/e6bc4f5f-b0fa-40c6-958d-45e91ae59251/download
bitstream.checksum.fl_str_mv	047ffa5754dc0cc622d3533cf004ecec 934f4ca17e109e0a05eaeaba504d7ce4 8a4605be74aa9ea9d79846c1fba20a33 19e7442ac869c97210b6554c84d736f6 bb03a47b32d0b4440e2ffb99397661b7
bitstream.checksumAlgorithm.fl_str_mv	MD5 MD5 MD5 MD5 MD5
repository.name.fl_str_mv	Repositorio de la Universidad de la Costa CUC
repository.mail.fl_str_mv	repdigital@cuc.edu.co
_version_	1811760668702932992
spelling	Cano, HeidisDe Paoli, FabricioPacheco Tuesca, María FernandaUtria Lafaurie, Marledys2019-09-25T13:54:04Z2019-09-25T13:54:04Z2019http://hdl.handle.net/11323/5298Corporación Universidad de la CostaREDICUC - Repositorio CUChttps://repositorio.cuc.edu.co/In the present study the sludge ashes coming from water treatment operations of the treatment plant of Triple A company, in Barranquilla city are analyzed. These analyzes are intended to determine the usefulness of sludge as a hydraulic binder, creating an ecological arrangement of thereof, and helping to minimize the extractive activities of raw materials used in the construction industry. Specimens were manufactured with a 5% and 10% replacement of cement by sludge ashes and a control mixture that required a theoretical compression strength of 4000 Psi (28 MPa) to be compared with the results and behavior of the modified concrete. The results from this study showed that sludge ashes from the water treatment can be replaced in small percentages with the Portland cement in concrete mixture without negatively affecting the compressive strength. It was obtained that the specimens tested for compression reach 3000 psi, which corresponds to a concrete of moderate resistance, which meets the requirements to be used in the construction of buildings of small housing type and simple buildings.En el presente estudio se analizaron las cenizas del lodo procedente de las operaciones de potabilización de agua de la Planta de Tratamiento de la Triple A, en la ciudad de Barranquilla. Estos análisis, tienen por objeto determinar la utilidad de las cenizas de los lodos como posible aglomerante hidráulico en mezclas de concreto de cemento portland, generando una disposición ecológica de los mismos, y contribuyendo a minimizar la actividad de explotación de materias primas empleadas en la industria de la construcción. Se fabricaron especímenes con un reemplazo del 5% y 10% de cenizas de lodo, y una mezcla de control que debía cumplir con un esfuerzo a la compresión teórico de 4000 Psi (28MPa) para comparar los resultados y el comportamiento del concreto fabricado. Los estudios demostraron que las cenizas de lodos procedentes de la planta de tratamiento de agua potable se pueden remplazar en pequeños porcentajes dentro de las mezclas de concreto de cemento Portland, sin que se vea afectada negativamente la resistencia a la compresión. Se obtuvo que los especímenes ensayados a compresión logran alcanzar los 3000 psi, lo que corresponde a un concreto de resistencia moderada, el cual cumple con los requerimientos para ser empleado en construcción de edificaciones de tipo habitacional de pequeña altura y edificaciones sencillas.spaUniversidad de la CostaIngeniería CivilAttribution-NonCommercial-ShareAlike 4.0 Internationalhttp://creativecommons.org/licenses/by-nc-sa/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Cenizas de lodoMaterial cementante complementarioConcretoResistencia a compresiónSludge ashSupplementary cementitious materialPozzolanaConcreteCompressive strengthComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodosTrabajo de grado - Pregradohttp://purl.org/coar/resource_type/c_7a1fTextinfo:eu-repo/semantics/bachelorThesishttp://purl.org/redcol/resource_type/TPinfo:eu-repo/semantics/acceptedVersionAldana Tique, A. J. (2017). Propuesta para el tratamiento y aprovechamiento de lodos en una PTAP convencional. Caso de estudio: Planta de tratamiento de agua potable de el Espinal- Tolima. Universidad de La Salle, 1(Facultad de Ingenieria ambiental y sanitaria.), 106. Retrieved from http://repository.lasalle.edu.co/bitstream/handle/10185/22405/41112712_2017.pdf?sequence=1 Amaris, N. A., & Rondo, V. (2009). USO DEL SILICATO DE SODIO COMO ADICIÓN NATURAL DEL CONCRETO HIDRAULICO. Universidad de La Salle. Bermeo Barreto, A. M., & Idrovo Heredia, E. P. (2014). APROVECHAMIENTO DE LODOS DESHIDRATADOS GENERADOS EN PLANTAS DE TRATAMIENTO DE AGUA POTABLE Y RESIDUAL COMO AGREGADO PARA MATERIALES DE CONSTRUCCIÓN.”. Castilla, J. D. (2018, December 28). Este año hubo un incremento en la producción de cemento gris de 6,3%. La Republica. Retrieved from https://www.larepublica.co/economia/este-ano-hubo-un-incremento-en-la-produccion-de-cemento-gris-de-63-2810131 Centro de estudios y expermientación de obras públicas. (2011a). Blast Furnace Slag. Retrieved from http://www.cedexmateriales.es/catalogo-de-residuos/29/humo-de-silice/ Centro de estudios y expermientación de obras públicas. (2011b). Cenizas Volantes. Retrieved from http://www.cedexmateriales.es/catalogo-de-residuos/24/diciembre-2011/ Centro de estudios y expermientación de obras públicas. (2012). Humo de Silice. Retrieved from http://www.cedexmateriales.es/catalogo-de-residuos/29/humo-de-silice/ Daza Marquez, N., & Medina Sanchez, A. (2018). Analisis comparativo del contenido de oxidos. 1. Universidad de la Costa. Retrieved from http://hdl.handle.net/11323/301 de Oliveira Andrade, J. J., Wenzel, M. C., da Rocha, G. H., & da Silva, S. R. (2018). Performance of rendering mortars containing sludge from water treatment plants as fine recycled aggregate. Journal of Cleaner Production, 192, 159–168. https://doi.org/10.1016/j.jclepro.2018.04.246 Demanda, L. A., Carlos, J., & Alcaraz, D. (2008). La industria del cemento en colombia, 1–53. Fernández, A. G. R. (2003). “manejo de lodos producidos en la planta de tratamiento de agua potable, planta ii, del municipio de cartago, valle.” Universidad Nacional de Colombia. Garcia Meseguer, A. (2001). Hormigon armado. (Fundación escuela de la edificación Maestro Victoria, Ed.) (3rd ed.). Madrid: Toran S.A. Geyer, A. L. B. (2001). Contribuição ao estudo da disposição final e aproveitamento da cinza de lodo de estações de tratamento de esgotos sanitários como adição ao concreto, 216. Gutiérrez-Rosero, J. A., Ramírez-Fajardo, Á. I., Rivas, R., Linares, B., & Paredes, D. (2014). Tratamiento de lodos generados en el proceso convencional de potabilización de agua. Ingenierías Universidad de Medellín, 13(25), 13–27. INVE 410-07. (2007). Resistencia a La Compresion De Cilindros De Concreto, 16. Li, Z., Jiang, N., Wu, F., & Zhou, Z. (2013a). Experimental investigation of phosphorus adsorption capacity of the waterworks sludges from five cities in China. Ecological Engineering, 53, 165–172. https://doi.org/10.1016/J.ECOLENG.2012.12.038 Li, Z., Jiang, N., Wu, F., & Zhou, Z. (2013b). Experimental investigation of phosphorus adsorption capacity of the waterworks sludges from five cities in China. Ecological Engineering, 53(April 2013), 165–172. https://doi.org/10.1016/j.ecoleng.2012.12.038 Marroquin Moscoso, K. J. (2018). EVALUACIÓN DEL EFECTO EN LA RESISTENCIA A LA COMPRESIÓN DEL CEMENTO TIPO USO GENERAL, POR LA ADICIÓN DE PUZOLANA, FLY ASH Y CALIZA, A DIFERENTE TAMAÑO DE PARTÍCULA. Universidad de San Carlos de Guatemala. Monteiro, P. J. M., & Mehta, P. K. (2004). Concreto. (Instituto Mexicano de Cemento y Concreto, Ed.). Mexico. Retrieved from http://imcyc.com/redcyc/imcyc/biblioteca_digital/CONCRETO_ESTRUCTURA_PROPIEDADES_Y_MATERIALES.pdf Naisma Hernández, Mayda Ulloa, Yuri Almaguer, Y. R. (2014). EVALUACIÓN AMBIENTAL ASOCIADA A LA EXPLOTACIÓN DEL YACIMIENTO DE MATERIALES DE CONSTRUCCIÓN LA INAGUA, GUANTÁNAMO, CUBA, (38), 146–158. Norma Tecnica Colombiana 121. Especificación de deempeño para el cemento hidraulico (2014). Colombia. O’Kelly, B. C. (2010). Landfill Disposal of Alum Water Treatment Residues: Some Pertinent Geoengineering Properties. Journal of Residuals Science & Technology;7 (2): 95-113 Apr2010, 7(2), 95–113. Retrieved from http://www.thomsoninnovation.com/tip-innovation/%5Cnhttp://www.thomsoninnovation.com/tip-innovation/recordView.do?datasource=WOK&category=LIT&selRecord=1&totalRecords=1&databaseIds=WOS,CCC&idType=uid/recordid&recordKeys=000276957000004/WOS:000276957000004 Pacheco Jimenez, D., & Varela Gomez, K. V. (2019). ANÁLISIS ESTADISTICO COMPARATIVO DEL CONTENIDO DE ÓXIDOS PRESENTES EN LODOS SIN CALCINAR, LODOS CALCINADOS Y CEMENTO PORTLAND. Universidad de la costa. Pereira, Y. A., Velasquez, S. R., Valencia, J. J., Ramírez, M. C., & Muñoz, A. P. (2017). Análisis comparativo de la concentración de óxidos presentes en el cemento portland y lodos de plantas de tratamiento de agua potable. Afinidad, 74(577), 68–73. Retrieved from http://www.raco.cat/index.php/afinidad/article/view/320832/411315 Reglamento Colombiano de construcción Sismo Resistente. TITULO C: Concreto estructural (2010). Colombia. Rivera, G. (2008). Manejabilidad del concreto. In Manejabilidad del concreto (pp. 83–103). Romero Quintero, A. F., & Hernandez Rico, A. camilo. (2014). DISEÑO DE MEZCLAS DE HORMIGÓN POR EL MÉTODO A.C.I. Y EFECTOS DE LA ADICIÓN DE CENIZAS VOLANTES DE TERMOTASAJERO EN LA RESISTENCIA A LA COMPRESIÓN. Universidad de Santo Tomas. Sales, A., & de Souza, F. R. (2009). Concretes and mortars recycled with water treatment sludge and construction and demolition rubble. Construction and Building Materials, 23(6), 2362–2370. https://doi.org/10.1016/j.conbuildmat.2008.11.001 Sales, A., De Souza, F. R., & Almeida, F. D. C. R. (2011). Mechanical properties of concrete produced with a composite of water treatment sludge and sawdust. Construction and Building Materials, 25(6), 2793–2798. https://doi.org/10.1016/j.conbuildmat.2010.12.057 Sales, A., De Souza, F. R., Dos Santos, W. N., Zimer, A. M., & Almeida, F. D. C. R. (2010). Lightweight composite concrete produced with water treatment sludge and sawdust: Thermal properties and potential application. Construction and Building Materials, 24(12), 2446–2453. https://doi.org/10.1016/j.conbuildmat.2010.06.012 Sterba, F. (2018). El ordenador de procesos en la industria del cemento, 20. Tafarel, N. F., Macioski, G., De Carvalho, K. Q., Nagalli, A., De Freitas, D. C., & Passig, F. H. (2016). Avaliação das propriedades do concreto devido à incorporação de lodo de estação de tratamento de água. Revista Materia, 21(4), 974–986. https://doi.org/10.1590/S1517-707620160004.0090 Técnica, N., Volantes, C., & Naturales, Y. P. (2017). NTC, (571). Torres, P., Hernández, D., & Paredes, D. (2012). Uso productivo de lodos de plantas de tratamiento de agua potable en la fabricación de ladrillos cerámicos. Revista Ingenieria de Construccion, 27(3), 145–154. https://doi.org/10.4067/S0718-50732012000300003 TRIPLE A. (2017). Etapas de la potabilización del Agua 1. Unicef. (2006). El agua potable y el saneamiento básico en los planes de desarrollo. La infancia, el agua y el saneamiento básico en los planes de desarrollo departamentales y municipales. Retrieved from http://www.unicef.org.co/pdf/Agua3.pdf Universidad Pedagogica y Tecnologica de Colombia. (2017). Materiales cementantes suplementarios. Retrieved from http://www.uptc.edu.co/docentes/oscar_gutierrez/En_Concreto/Materia5 Valderama, C. P., Torres Agredo, J., & Mejia de Gutierrez, R. (2011). Características de desempeño de un concreto adicionado con cenizas volantesde alto nivel de inquemados. Universidad Nacional de colombia. Retrieved from https://revistas.unal.edu.co/index.php/ingeinv/rt/printerFriendly/20519/33850?fbclid=IwAR1VN-hRwC6JEuzqhvdyqaRxB9S56zRLpxNG6ZP6HdR7XWMWOHDyOe-JIJA Zhao, Y. Q. (2003). Correlations between floc physical properties and optimum polymer dosage in alum sludge conditioning and dewatering. Chemical Engineering Journal, 92(1–3), 227–235. https://doi.org/10.1016/S1385-8947(02)00253-XPublicationORIGINALComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos.pdfComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos.pdfapplication/pdf1843058https://repositorio.cuc.edu.co/bitstreams/eaa9a72a-4715-4e3a-8299-26a00b514d36/download047ffa5754dc0cc622d3533cf004ececMD51CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-81031https://repositorio.cuc.edu.co/bitstreams/068cf094-4699-4ec4-a60f-3962ef923096/download934f4ca17e109e0a05eaeaba504d7ce4MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-81748https://repositorio.cuc.edu.co/bitstreams/a812a685-27e3-422b-b5c8-14f2c3ba1976/download8a4605be74aa9ea9d79846c1fba20a33MD53THUMBNAILComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos.pdf.jpgComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos.pdf.jpgimage/jpeg29870https://repositorio.cuc.edu.co/bitstreams/89002dd9-99a5-4e3c-9ead-5ca6132eef74/download19e7442ac869c97210b6554c84d736f6MD55TEXTComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos.pdf.txtComportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos.pdf.txttext/plain130568https://repositorio.cuc.edu.co/bitstreams/e6bc4f5f-b0fa-40c6-958d-45e91ae59251/downloadbb03a47b32d0b4440e2ffb99397661b7MD5611323/5298oai:repositorio.cuc.edu.co:11323/52982024-09-16 16:39:39.049http://creativecommons.org/licenses/by-nc-sa/4.0/Attribution-NonCommercial-ShareAlike 4.0 Internationalopen.accesshttps://repositorio.cuc.edu.coRepositorio de la Universidad de la Costa CUCrepdigital@cuc.edu.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

Comportamiento de mezcla de concreto cemento Portland con adiciones de 5 y 10% de cenizas de lodos

Publicaciones similares