Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland

In this research work, the quantities of oxides present in sludge coming from drinking water treatment plant in Barranquilla, Colombia was determined; part of specimen (2.0 kg) was calcined at 800 °C and the other portion was dried during three days with surrounding temperature. The concentration of...

Full description

Autores:: Pacheco Jiménez, Doralis
Varela Gómez, Kelly Vanessa

Tipo de recurso:: Trabajo de grado de pregrado

Fecha de publicación:: 2019

Institución:: Corporación Universidad de la Costa

Repositorio:: REDICUC - Repositorio CUC

Idioma:: spa

id	RCUC2_d7ef32a22e1c315c5adc4982636fa831
oai_identifier_str	oai:repositorio.cuc.edu.co:11323/4724
network_acronym_str	RCUC2
network_name_str	REDICUC - Repositorio CUC
repository_id_str
dc.title.spa.fl_str_mv	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
title	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
spellingShingle	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland Cenizas de lodo Material cementante suplementario XRF Sludge ash Supplementary cementitious material XRF
title_short	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
title_full	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
title_fullStr	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
title_full_unstemmed	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
title_sort	Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland
dc.creator.fl_str_mv	Pacheco Jiménez, Doralis Varela Gómez, Kelly Vanessa
dc.contributor.advisor.spa.fl_str_mv	Avila Pereira, Yoleimy Del Carmen De Paoli, Fabricio
dc.contributor.author.spa.fl_str_mv	Pacheco Jiménez, Doralis Varela Gómez, Kelly Vanessa
dc.subject.spa.fl_str_mv	Cenizas de lodo Material cementante suplementario XRF Sludge ash Supplementary cementitious material XRF
topic	Cenizas de lodo Material cementante suplementario XRF Sludge ash Supplementary cementitious material XRF
description	In this research work, the quantities of oxides present in sludge coming from drinking water treatment plant in Barranquilla, Colombia was determined; part of specimen (2.0 kg) was calcined at 800 °C and the other portion was dried during three days with surrounding temperature. The concentration of oxide in sludge calcined and sludge not calcined was get by X-rays fluorescence, the results were validated by ASTM C114, to compare the results with oxides concentration in Portland cement type I. Statistically it was revealed there is a significant ifference in calcium oxide, silicon dioxide, ferric oxides and aluminum oxide concentrations of the sludge and the Portland cement. The sludge coming from drinking water treatment plant have a high cementitious potential when classified as a class F pozzolan with low calcium oxide content, in accordance with ASTM C618. The percentages of magnesium oxide and sulfur rioxide in the sludge don’t exceed the values required by the ASTM C150 standard
publishDate	2019
dc.date.accessioned.none.fl_str_mv	2019-05-27T14:33:24Z
dc.date.available.none.fl_str_mv	2019-05-27T14:33:24Z
dc.date.issued.none.fl_str_mv	2019-05-17
dc.type.spa.fl_str_mv	Trabajo de grado - Pregrado
dc.type.coar.spa.fl_str_mv	http://purl.org/coar/resource_type/c_7a1f
dc.type.content.spa.fl_str_mv	Text
dc.type.driver.spa.fl_str_mv	info:eu-repo/semantics/bachelorThesis
dc.type.redcol.spa.fl_str_mv	http://purl.org/redcol/resource_type/TP
dc.type.version.spa.fl_str_mv	info:eu-repo/semantics/acceptedVersion
format	http://purl.org/coar/resource_type/c_7a1f
status_str	acceptedVersion
dc.identifier.uri.spa.fl_str_mv	https://hdl.handle.net/11323/4724
dc.identifier.instname.spa.fl_str_mv	Corporación Universidad de la Costa
dc.identifier.reponame.spa.fl_str_mv	REDICUC - Repositorio CUC
dc.identifier.repourl.spa.fl_str_mv	https://repositorio.cuc.edu.co/
url	https://hdl.handle.net/11323/4724 https://repositorio.cuc.edu.co/
identifier_str_mv	Corporación Universidad de la Costa REDICUC - Repositorio CUC
dc.language.iso.none.fl_str_mv	spa
language	spa
dc.relation.references.spa.fl_str_mv	ACI Committee. (2013). Cementitious Materials for Concrete. ACI Education Bulletin E3-13. ACI Committee E-701. (2013). ACI Education Bulletin E3-13 Cementitious Materials for Concrete. Recuperado 15 de mayo de 2019, de https://docplayer.net/30078272-Aci education-bulletin-e3-13-cementitious-materials-for-concrete.html Ahmad, T., Ahmad, K., & Alam, M. (2016). Characterization of Water Treatment Plant’s Sludge and its Safe Disposal Options. Procedia Environmental Sciences, 35, 950-955. https://doi.org/10.1016/j.proenv.2016.07.088 American Society for Testing and. Materials. (2018). ASTM C618-17a Especificación estándar para Ceniza volante de carbón y puzolana natural cruda o calcinada para su uso en hormigón. Recuperado 15 de mayo de 2019, de https://www.astm.org/Standards/C618 SP.htm Andrade, C. de, Mynrine, V., Silva, D. A. da, Mayer, S. L. S., Simetti, R., & Marchiori, F. (2016). Compósito para a construção civil a partir de resíduos industriais. Matéria (Rio de Janeiro), 21(2), 321-329. https://doi.org/10.1590/S1517-707620160002.0031 Aragon, L. (2016). Introducción a la estadística no paramétrica. En Estadística en el área de las Ciencias Sociales y Administrativas (1.a ed., p. 523). Alfaomega. ASTM C150, Standard Specification for Portland Cement. ASTM C114, Standard Test Methods for Chemical Analysis of Hydraulic Cement Beita Sandí, W. (2008). “Caracterización fisicoquímica de las aguas superficiales de la cuenca del río Rincón en la Península de Osa, Puntarenas, Costa Rica”. Recuperado de http://www.kerwa.ucr.ac.cr/handle/10669/334 Calcinor. (2015). Las funciones que realiza la cal en el tratamiento de aguas. Recuperado 16 de mayo de 2019, de https://www.calcinor.com/es/actualidad/2017-03-16/cal-tratamiento de-aguas/ Cavada, C. (2017, junio 1). Contaminación ambiental: ¿Cómo afecta a nuestro sistema respiratorio? Recuperado 4 de abril de 2019, de www.ipsuss.cl website: http://www.ipsuss.cl/ipsuss/site/artic/20170601/pags/20170601165418.html Ceron, O., Millan, S., Espejel, F., Rodriguez, A., & Ramirez, R. (2013). APLICACIÓN DE LODOS DE PLANTAS POTABILIZADORAS PARA ELABORAR MATERIALES DE CONSTRUCCIÓN. Companhia Estadual de Tecnologia de Saneamento Básico e de Controle de Poluiçao das Águas. (2001). Capitulo 8. Tratamiento de agua. En Operación y mantenimiento de plantas de tratamiento de agua (Vol. 1 y 2). lima. DANE. (2018). Estadísticas de cemento gris. Recuperado 3 de abril de 2019, de https://www.dane.gov.co/index.php/estadisticas-por-tema/construccion/estadisticas-de cemento-gris Daza, N., & Medina, A. (2018). ANÁLISIS COMPARATIVO DEL CONTENIDO DE ÓXIDOS PRESENTES EN LAS CENIZAS DE LODOS DE PTAP Y EL CEMENTO PORTLAND TIPO UNO. Universidad de la costa, Barranquilla. Decreto 302 de 2000. Constitución política, Colombia, 25 de febrero de 2000. Decreto 838 de 2005. Disposición final de residuos sólidos, Colombia, 23 de marzo de 2005 DECRETO 1594 DE 1984. Uso del agua y residuos líquidos, Colombia, junio de 1984. Decreto 2104 de 1983, Constitución política, Colombia, 26 de julio de 1983. Decreto 2811 de 1974. Código Nacional de Recursos Naturales Renovables y de Protección al Medio Ambiente, Colombia, 18 de diciembre de 1974. Decreto 4002 de 2004. Revisión de los planes de ordenamiento territorial, Colombia, 30 de noviembre de 2004. Espinoza, L., & Escalante, I. (2008). Comparación de las propiedades del concreto utilizando escoria de alto horno como reemplazo parcial y total del cemento Pórtland ordinario. Nexo Revista Científica, 21(01), 11-18. https://doi.org/10.5377/nexo.v21i01.405 FICEM. (2013). FICEM una mirada al futuro. Federacion interamericana del cemento. Fonseca, L. (2016). Empleo de ceniza volante colombiana como material cementicio suplementario y sus efectos sobre la fijación de cloruros en concretos. Universidad nacional de Colombia, Bogota. Gang, X., & Xianming, S. (2018). Characteristics and applications of fly ash as a sustainable construction material: A state-of-the-art review. Resources, Conservation and Recycling, 136, 95-109. https://doi.org/10.1016/j.resconrec.2018.04.010 Gastaldini, A. L. G., Hengen, M. F., Gastaldini, M. C. C., do Amaral, F. D., Antolini, M. B., & Coletto, T. (2015). The use of water treatment plant sludge ash as a mineral addition. Construction and Building Materials, 94, 513-520. https://doi.org/10.1016/j.conbuildmat.2015.07.038 Gutiérrez Ginés, M. J., & Ranz, I. (2010). Utilización de un equipo portátil de fluorescencia de rayos X para el estudio de metales pesados en suelos: puesta a punto y aplicación a vertederos. Recuperado de https://digital.csic.es/handle/10261/73106 Gutiérrez-Rosero, J. A., Ramírez-Fajardo, Á. I., Rivas, R., Linares, B., & Paredes, D. (2014). Tratamiento de lodos generados en el proceso convencional de potabilización de agua. Revista Ingenierías Universidad de Medellín, 13(25), 13-27 Hagemann, S. E., Gastaldini, A. L. G., Cocco, M., Jahn, S. L., & Terra, L. M. (2019). Synergic effects of the substitution of Portland cement for water treatment plant sludge ash and ground limestone: Technical and economic evaluation. Journal of Cleaner Production, 214, 916-926. https://doi.org/10.1016/j.jclepro.2018.12.324 Hamada, H., Jokhio, G. A., Yahaya, F., Humada, A., & Gul, Y. (2018). The present state of the use of palm oil fuel ash (POFA) in concrete. Construction and Building Materials, 175, 26-40. https://doi.org/10.1016/j.conbuildmat.2018.03.227 Herreros-Chavez, L., Cervera, M. L., & Morales-Rubio, A. (2019). Direct determination by portable ED-XRF of mineral profile in cocoa powder samples. Food Chemistry, 278, 373-379. https://doi.org/10.1016/j.foodchem.2018.11.065 Higuchi, T., Morioka, M., Yoshioka, I., & Yokozeki, K. (2014). Development of a new ecological concrete with CO2 emissions below zero. Construction and Building Materials, 67, 338-343. https://doi.org/10.1016/j.conbuildmat.2014.01.029 IDEAM. (2015, julio 6). Atlas cuenca del rio magdalena version final. Recuperado 3 de abril de 2019, de https://wiki.ead.pucv.cl/Atlas_cuenca_del_rio_magdalena_version_final.pdf Java. (2017). IBM SPSS Statistics Base 22.0 (Versión 22). Recuperado de https://ibm-spss statistics-base.uptodown.com/windows Jiménez, A. (2006). Contraste de Shapiro-Wilk. Recuperado 15 de mayo de 2019, de Xataka Ciencia website: https://www.xatakaciencia.com/matematicas/contraste-de-shapiro-wilk Khodabakhshian, A., Ghalehnovi, M., de Brito, J., & Shamsabadi, E. (2018). Durability performance of structural concrete containing silica fume and marble industry waste powder. Journal of Cleaner Production, 170, 42-60. https://doi.org/10.1016/j.jclepro.2017.09.116 Kosmatka, S., & Wilson, M. (2011). Design and Control of Concrete Mixtures 15th (Fifteenth) Edition (Edición: 15th Edition). Portland Cement Assn. Latorre, A. (2018). La industria del cemento en colombia determinantes y comportamiento de la demanda (1996-2005). Pontificia Universidad Javeriana, Bogota. Ley 9 de 1979. Medidas sanitarias, Colombia, 24 de enero de 1979. Lizarazo Marriaga, J., & Claisse, P. (2011). Influencia de la adición de escoria de alto horno en la penetración de los cloruros en el concreto. Ingeniería e Investigación, 31(2), 38-47. Martirena, F., & Monzo, J. (2018). Vegetable ashes as Supplementary Cementitious Materials. Cement and Concrete Research, 114, 57-64. https://doi.org/10.1016/j.cemconres.2017.08.015 Ministerio de Ambiente, Vivienda y Desarrollo Territorial. (2005). Polí-tica Ambiental Para la Gestión Integral de Residuos o Desechos Peligrosos. Bogota. Molina, N. F., Tarifa, O. I. F., & Mendoza, L. V. (2015). Residuos agroindustriales como adiciones en la elaboración de bloques de concreto no estructural. Ciencia e Ingeniería Neogranadina, 25(2), 2. Montaño, A. M., González, C. P., Castro, D., Gualdron, G., & Atencio, R. (2017). Inclusion of geopolymers derivate from fly ash and pumice in reinforced concrete. Journal of Physics: Conference Series, 935, 012016. https://doi.org/10.1088/1742-6596/935/1/012016 Nowasell, Q. C., & Kevern, J. T. (2015). Using Drinking Water Treatment Waste as Low-Cost Internal Curing Agent for Concrete. ACI Materials Journal, 112(1). Recuperado de https://trid.trb.org/view/1343930 Paris, J. M., Roessler, J. G., Ferraro, C. C., DeFord, H. D., & Townsend, T. G. (2016). A review of waste products utilized as supplements to Portland cement in concrete. Journal of Cleaner Production, 121, 1-18. https://doi.org/10.1016/j.jclepro.2016.02.013 Pedrosa, I., Juarros-Basterretxea, J., Robles-Fernández, A., Basteiro, J., & García-Cueto, E. (2015). Pruebas de bondad de ajuste en distribuciones simétricas, ¿qué estadístico utilizar? Universitas Psychologica, 14(1), 245-254. https://doi.org/10.11144/Javeriana.upsy14-1.pbad Pereira, Y. A., Velasquez, S. R., Valencia, J. J., Ramírez, M. C., & Muñoz, A. P. (2017). Análisis comparativo de la concentración de óxidos presentes en el cemento portland y lodos de plantas de tratamiento de agua potable. Afinidad, 74(577). Recuperado de https://www.raco.cat/index.php/afinidad/article/view/320832 Perez, A. (2018). EVALUACIÓN DE LA INFLUENCIA DEL GRADO DE POLIMERIZACIÓN DEL POLICLORURO DE ALUMINIO COMO COAGULANTE PRIMARIO EN EL TRATAMIENTO DE AGUA. UNIVERSIDAD DE CARABOBO, Valencia. Puertas, F. (1993). Escorias de alto horno: composición y comportamiento hidráulico. Recuperado de https://digital.csic.es/handle/10261/55875 Raffino, M. E. (2018, noviembre 14). Estadística inferencial: Concepto, Usos y Ejemplos. Recuperado 15 de mayo de 2019, de https://concepto.de/estadistica-inferencial/ Rajasekar, A., Arunachalam, K., Kottaisamy, M., & Saraswathy, V. (2018). Durability characteristics of Ultra High Strength Concrete with treated sugarcane bagasse ash. Construction and Building Materials, 171, 350-356. https://doi.org/10.1016/j.conbuildmat.2018.03.140 Ramirez, G. (2003). Manejo de lodos producidos en la planta de tratamiento de agua potable, planta 2, del municipio de Cartago, Valle (Universidad nacional de Colombia). Recuperado de https://core.ac.uk/download/pdf/11051579.pdf Restrepo, J. C., Restrepo, O. J., & Tóbon, J. I. (2014). REDUCCIÓN DE CO2 EN LA INDUSTRIA CEMENTERA POR MEDIO DE PROCESOS DE SÍNTESIS QUÍMICA. Revista Colombiana de Materiales, 0(5), 54-60. Rojas, M. claudia, Garcia, M. E., Vargas, G., & Velilla, M. A. Infraccion ambiental - por descarga de lodos a cuerpos de agua superficial. , (Tribunal administrativo del atlantico 24 de noviembre de 2010). Sanjuan, M., Estevez, E., Argiz, C., & del Barrio, D. (2018). Effect of curing time on granulated blast-furnace slag cement mortars carbonation. Cement and Concrete Composites, 90, 257-265. https://doi.org/10.1016/j.cemconcomp.2018.04.006 SEINTBA S.C. (2010). MANIFESTACION DE IMPACTO AMBIENTAL RESIDUOS PELIGROSOS (p. 117). SERVICIO DE ECOLOGÍA INTEGRAL DEL BAJÍO S.A. DE C.V. Shuqiang, xu, Qinglin, M., & Julin, W. (2018). Combined effect of isobutyltriethoxysilane and silica fume on the performance of natural hydraulic lime-based mortars. Construction and Building Materials, 162, 181-191. https://doi.org/10.1016/j.conbuildmat.2017.09.150 Sollutia.com. (s. f.-a). Cenizas procedentes de la incineración de biomasa \| CEDEX. Recuperado 3 de abril de 2019, de http://www.cedexmateriales.es/catalogo-de-residuos/23/diciembre 2014/ Sollutia.com. (s. f.-b). Humo de sílice \| CEDEX. Recuperado 3 de abril de 2019, de http://www.cedexmateriales.es/catalogo-de-residuos/29/humo-de-silice/ Tobón, J. I., & Gómez, R. K. (2008). DESEMPEÑO DEL CEMENTO PÓRTLAND ADICIONADO CON CALIZAS DE DIFERENTES GRADOS DE PUREZA. DYNA, 75(156), 177-184. Torres, R., & Nicolas, J. (2018). Propuesta metodológica para tratamiento de lodos provenientes de plantas de potabilización en la sabana de Bogotá (estudio de caso Madrid, Cundinamarca). instname:Universidad Libre. Recuperado de http://repository.unilibre.edu.co/handle/10901/11289 Triple A S.A. E.S.P. (s. f.). Etapas de la potabilización del Agua. (http://www.aaa.com.co/acueducto/potabilizacion/). Vargas, J. W. P., Buzón, J. A., Vergara, D. A., & Molina, E. (2011). Reducción de los Residuos Sólidos Orgánicos en Colombia por medio del Compostaje Líquido. Ingeniare, (11), 374. https://doi.org/10.18041/1909-2458/ingeniare.11.643 Vigneshwari, M., Arunachalam, K., & Angayarkanni, A. (2018). Replacement of silica fume with thermally treated rice husk ash in Reactive Powder Concrete. Journal of Cleaner Production, 188, 264-277. https://doi.org/10.1016/j.jclepro.2018.04.008 Vouk, D., Serdar, M., Nakić, D., & Anić-Vučinić, A. (2016). Use of sludge generated at WWTP in the production of cement mortar and concrete. https://doi.org/10.14256/JCE.1374.2015 Walpole, R. E., Myers, R. H., & Myers, S. L. (2012). Probabilidad y estadistica para ingenieria y ciencias (Novena edicion). Mexico: PEARSON EDUCACION. Wons, W., Rzepa, K., Reben, M., Murzyn, P., Sitarz, M., & Olejniczak, Z. (2018). Effect of thermal processing on the structural characteristics of fly ashes. Journal of Molecular Structure, 1165, 299-304. https://doi.org/10.1016/j.molstruc.2018.04.008 Yue, Y., Wang, J., & Bai, Y. (2018). Tracing the status of silica fume in cementitious materials with Raman microscope. Construction and Building Materials, 159, 610-616. https://doi.org/10.1016/j.conbuildmat.2017.11.015 Zhen, C., & Chi, S. (2017). Comparative studies on the effects of sewage sludge ash and fly ash on cement hydration and properties of cement mortars. Construction and Building Materials, 154, 791-803. https://doi.org/10.1016/j.conbuildmat.2017.08.003 Zhen, C., Jiang, S. L., & Chi, S. (2018). Combined use of sewage sludge ash and recycled glass cullet for the production of concrete blocks. Journal of Cleaner Production, 171, 1447 1459. https://doi.org/10.1016/j.jclepro.2017.10.140
dc.rights.spa.fl_str_mv	Attribution-NonCommercial-ShareAlike 4.0 International
dc.rights.uri.spa.fl_str_mv	http://creativecommons.org/licenses/by-nc-sa/4.0/
dc.rights.accessrights.spa.fl_str_mv	info:eu-repo/semantics/openAccess
dc.rights.coar.spa.fl_str_mv	http://purl.org/coar/access_right/c_abf2
rights_invalid_str_mv	Attribution-NonCommercial-ShareAlike 4.0 International http://creativecommons.org/licenses/by-nc-sa/4.0/ http://purl.org/coar/access_right/c_abf2
eu_rights_str_mv	openAccess
dc.publisher.program.spa.fl_str_mv	Ingeniería Civil
institution	Corporación Universidad de la Costa
bitstream.url.fl_str_mv	https://repositorio.cuc.edu.co/bitstreams/16b38abd-6e86-4a9e-8fd7-1f4585d0d422/download https://repositorio.cuc.edu.co/bitstreams/a3a2d6a3-0dc3-41f9-a1c7-4801d6826e62/download https://repositorio.cuc.edu.co/bitstreams/4706d78f-47de-414c-bb68-72591dc46940/download https://repositorio.cuc.edu.co/bitstreams/206a7975-3f20-463b-ac0b-17a3a403052a/download https://repositorio.cuc.edu.co/bitstreams/51b067d2-6a7e-414e-a24a-e8e8b0ecd775/download
bitstream.checksum.fl_str_mv	fd6fb9fe22f36ba567d78ce7d79d33b5 934f4ca17e109e0a05eaeaba504d7ce4 8a4605be74aa9ea9d79846c1fba20a33 fc6825822da9160ff313a78c02d88cb3 a828eb31e7e7a55382f2db995cfa0227
bitstream.checksumAlgorithm.fl_str_mv	MD5 MD5 MD5 MD5 MD5
repository.name.fl_str_mv	Repositorio de la Universidad de la Costa CUC
repository.mail.fl_str_mv	repdigital@cuc.edu.co
_version_	1811760709442207744
spelling	Avila Pereira, Yoleimy Del CarmenDe Paoli, FabricioPacheco Jiménez, DoralisVarela Gómez, Kelly Vanessa2019-05-27T14:33:24Z2019-05-27T14:33:24Z2019-05-17https://hdl.handle.net/11323/4724Corporación Universidad de la CostaREDICUC - Repositorio CUChttps://repositorio.cuc.edu.co/In this research work, the quantities of oxides present in sludge coming from drinking water treatment plant in Barranquilla, Colombia was determined; part of specimen (2.0 kg) was calcined at 800 °C and the other portion was dried during three days with surrounding temperature. The concentration of oxide in sludge calcined and sludge not calcined was get by X-rays fluorescence, the results were validated by ASTM C114, to compare the results with oxides concentration in Portland cement type I. Statistically it was revealed there is a significant ifference in calcium oxide, silicon dioxide, ferric oxides and aluminum oxide concentrations of the sludge and the Portland cement. The sludge coming from drinking water treatment plant have a high cementitious potential when classified as a class F pozzolan with low calcium oxide content, in accordance with ASTM C618. The percentages of magnesium oxide and sulfur rioxide in the sludge don’t exceed the values required by the ASTM C150 standardEn el presente trabajo de investigación, se determinaron las concentraciones de óxidos presentes en el lodo proveniente de la planta de tratamiento de agua potable, ubicada en la ciudad de Barranquilla, Colombia; 2.0 kg de muestra fueron calcinados a 800 °C y la otra parte fue expuesta a temperatura ambiente durante tres días para su secado. Se obtuvieron datos de las concentraciones de óxidos presentes en los lodos calcinados y sin calcinar por medio de ensayo de fluorescencia de rayos X, los valores obtenidos fueron validados mediante la norma ASTM C114, con el fin de comparar las concentraciones de óxidos del cemento Portland tipo I. Estadísticamente se demostró que existe una diferencia significativa en las concentraciones de óxido de calcio, óxido de silicio, óxido de hierro y óxido de aluminio de las muestras de lodos y l cemento. Las muestras de lodos clasificaron como una puzolana de clase F con bajos contenidos de calcio según la norma ASTM C618. Los porcentajes de óxido de magnesio y azufre en los lodos no exceden las cantidades exigidas por la norma ASTM C150.spaAttribution-NonCommercial-ShareAlike 4.0 Internationalhttp://creativecommons.org/licenses/by-nc-sa/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Cenizas de lodoMaterial cementante suplementarioXRFSludge ashSupplementary cementitious materialXRFAnálisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portlandTrabajo de grado - Pregradohttp://purl.org/coar/resource_type/c_7a1fTextinfo:eu-repo/semantics/bachelorThesishttp://purl.org/redcol/resource_type/TPinfo:eu-repo/semantics/acceptedVersionIngeniería CivilACI Committee. (2013). Cementitious Materials for Concrete. ACI Education Bulletin E3-13. ACI Committee E-701. (2013). ACI Education Bulletin E3-13 Cementitious Materials for Concrete. Recuperado 15 de mayo de 2019, de https://docplayer.net/30078272-Aci education-bulletin-e3-13-cementitious-materials-for-concrete.html Ahmad, T., Ahmad, K., & Alam, M. (2016). Characterization of Water Treatment Plant’s Sludge and its Safe Disposal Options. Procedia Environmental Sciences, 35, 950-955. https://doi.org/10.1016/j.proenv.2016.07.088 American Society for Testing and. Materials. (2018). ASTM C618-17a Especificación estándar para Ceniza volante de carbón y puzolana natural cruda o calcinada para su uso en hormigón. Recuperado 15 de mayo de 2019, de https://www.astm.org/Standards/C618 SP.htm Andrade, C. de, Mynrine, V., Silva, D. A. da, Mayer, S. L. S., Simetti, R., & Marchiori, F. (2016). Compósito para a construção civil a partir de resíduos industriais. Matéria (Rio de Janeiro), 21(2), 321-329. https://doi.org/10.1590/S1517-707620160002.0031 Aragon, L. (2016). Introducción a la estadística no paramétrica. En Estadística en el área de las Ciencias Sociales y Administrativas (1.a ed., p. 523). Alfaomega. ASTM C150, Standard Specification for Portland Cement. ASTM C114, Standard Test Methods for Chemical Analysis of Hydraulic Cement Beita Sandí, W. (2008). “Caracterización fisicoquímica de las aguas superficiales de la cuenca del río Rincón en la Península de Osa, Puntarenas, Costa Rica”. Recuperado de http://www.kerwa.ucr.ac.cr/handle/10669/334 Calcinor. (2015). Las funciones que realiza la cal en el tratamiento de aguas. Recuperado 16 de mayo de 2019, de https://www.calcinor.com/es/actualidad/2017-03-16/cal-tratamiento de-aguas/ Cavada, C. (2017, junio 1). Contaminación ambiental: ¿Cómo afecta a nuestro sistema respiratorio? Recuperado 4 de abril de 2019, de www.ipsuss.cl website: http://www.ipsuss.cl/ipsuss/site/artic/20170601/pags/20170601165418.html Ceron, O., Millan, S., Espejel, F., Rodriguez, A., & Ramirez, R. (2013). APLICACIÓN DE LODOS DE PLANTAS POTABILIZADORAS PARA ELABORAR MATERIALES DE CONSTRUCCIÓN. Companhia Estadual de Tecnologia de Saneamento Básico e de Controle de Poluiçao das Águas. (2001). Capitulo 8. Tratamiento de agua. En Operación y mantenimiento de plantas de tratamiento de agua (Vol. 1 y 2). lima. DANE. (2018). Estadísticas de cemento gris. Recuperado 3 de abril de 2019, de https://www.dane.gov.co/index.php/estadisticas-por-tema/construccion/estadisticas-de cemento-gris Daza, N., & Medina, A. (2018). ANÁLISIS COMPARATIVO DEL CONTENIDO DE ÓXIDOS PRESENTES EN LAS CENIZAS DE LODOS DE PTAP Y EL CEMENTO PORTLAND TIPO UNO. Universidad de la costa, Barranquilla. Decreto 302 de 2000. Constitución política, Colombia, 25 de febrero de 2000. Decreto 838 de 2005. Disposición final de residuos sólidos, Colombia, 23 de marzo de 2005 DECRETO 1594 DE 1984. Uso del agua y residuos líquidos, Colombia, junio de 1984. Decreto 2104 de 1983, Constitución política, Colombia, 26 de julio de 1983. Decreto 2811 de 1974. Código Nacional de Recursos Naturales Renovables y de Protección al Medio Ambiente, Colombia, 18 de diciembre de 1974. Decreto 4002 de 2004. Revisión de los planes de ordenamiento territorial, Colombia, 30 de noviembre de 2004. Espinoza, L., & Escalante, I. (2008). Comparación de las propiedades del concreto utilizando escoria de alto horno como reemplazo parcial y total del cemento Pórtland ordinario. Nexo Revista Científica, 21(01), 11-18. https://doi.org/10.5377/nexo.v21i01.405 FICEM. (2013). FICEM una mirada al futuro. Federacion interamericana del cemento. Fonseca, L. (2016). Empleo de ceniza volante colombiana como material cementicio suplementario y sus efectos sobre la fijación de cloruros en concretos. Universidad nacional de Colombia, Bogota. Gang, X., & Xianming, S. (2018). Characteristics and applications of fly ash as a sustainable construction material: A state-of-the-art review. Resources, Conservation and Recycling, 136, 95-109. https://doi.org/10.1016/j.resconrec.2018.04.010 Gastaldini, A. L. G., Hengen, M. F., Gastaldini, M. C. C., do Amaral, F. D., Antolini, M. B., & Coletto, T. (2015). The use of water treatment plant sludge ash as a mineral addition. Construction and Building Materials, 94, 513-520. https://doi.org/10.1016/j.conbuildmat.2015.07.038 Gutiérrez Ginés, M. J., & Ranz, I. (2010). Utilización de un equipo portátil de fluorescencia de rayos X para el estudio de metales pesados en suelos: puesta a punto y aplicación a vertederos. Recuperado de https://digital.csic.es/handle/10261/73106 Gutiérrez-Rosero, J. A., Ramírez-Fajardo, Á. I., Rivas, R., Linares, B., & Paredes, D. (2014). Tratamiento de lodos generados en el proceso convencional de potabilización de agua. Revista Ingenierías Universidad de Medellín, 13(25), 13-27 Hagemann, S. E., Gastaldini, A. L. G., Cocco, M., Jahn, S. L., & Terra, L. M. (2019). Synergic effects of the substitution of Portland cement for water treatment plant sludge ash and ground limestone: Technical and economic evaluation. Journal of Cleaner Production, 214, 916-926. https://doi.org/10.1016/j.jclepro.2018.12.324 Hamada, H., Jokhio, G. A., Yahaya, F., Humada, A., & Gul, Y. (2018). The present state of the use of palm oil fuel ash (POFA) in concrete. Construction and Building Materials, 175, 26-40. https://doi.org/10.1016/j.conbuildmat.2018.03.227 Herreros-Chavez, L., Cervera, M. L., & Morales-Rubio, A. (2019). Direct determination by portable ED-XRF of mineral profile in cocoa powder samples. Food Chemistry, 278, 373-379. https://doi.org/10.1016/j.foodchem.2018.11.065 Higuchi, T., Morioka, M., Yoshioka, I., & Yokozeki, K. (2014). Development of a new ecological concrete with CO2 emissions below zero. Construction and Building Materials, 67, 338-343. https://doi.org/10.1016/j.conbuildmat.2014.01.029 IDEAM. (2015, julio 6). Atlas cuenca del rio magdalena version final. Recuperado 3 de abril de 2019, de https://wiki.ead.pucv.cl/Atlas_cuenca_del_rio_magdalena_version_final.pdf Java. (2017). IBM SPSS Statistics Base 22.0 (Versión 22). Recuperado de https://ibm-spss statistics-base.uptodown.com/windows Jiménez, A. (2006). Contraste de Shapiro-Wilk. Recuperado 15 de mayo de 2019, de Xataka Ciencia website: https://www.xatakaciencia.com/matematicas/contraste-de-shapiro-wilk Khodabakhshian, A., Ghalehnovi, M., de Brito, J., & Shamsabadi, E. (2018). Durability performance of structural concrete containing silica fume and marble industry waste powder. Journal of Cleaner Production, 170, 42-60. https://doi.org/10.1016/j.jclepro.2017.09.116 Kosmatka, S., & Wilson, M. (2011). Design and Control of Concrete Mixtures 15th (Fifteenth) Edition (Edición: 15th Edition). Portland Cement Assn. Latorre, A. (2018). La industria del cemento en colombia determinantes y comportamiento de la demanda (1996-2005). Pontificia Universidad Javeriana, Bogota. Ley 9 de 1979. Medidas sanitarias, Colombia, 24 de enero de 1979. Lizarazo Marriaga, J., & Claisse, P. (2011). Influencia de la adición de escoria de alto horno en la penetración de los cloruros en el concreto. Ingeniería e Investigación, 31(2), 38-47. Martirena, F., & Monzo, J. (2018). Vegetable ashes as Supplementary Cementitious Materials. Cement and Concrete Research, 114, 57-64. https://doi.org/10.1016/j.cemconres.2017.08.015 Ministerio de Ambiente, Vivienda y Desarrollo Territorial. (2005). Polí-tica Ambiental Para la Gestión Integral de Residuos o Desechos Peligrosos. Bogota. Molina, N. F., Tarifa, O. I. F., & Mendoza, L. V. (2015). Residuos agroindustriales como adiciones en la elaboración de bloques de concreto no estructural. Ciencia e Ingeniería Neogranadina, 25(2), 2. Montaño, A. M., González, C. P., Castro, D., Gualdron, G., & Atencio, R. (2017). Inclusion of geopolymers derivate from fly ash and pumice in reinforced concrete. Journal of Physics: Conference Series, 935, 012016. https://doi.org/10.1088/1742-6596/935/1/012016 Nowasell, Q. C., & Kevern, J. T. (2015). Using Drinking Water Treatment Waste as Low-Cost Internal Curing Agent for Concrete. ACI Materials Journal, 112(1). Recuperado de https://trid.trb.org/view/1343930 Paris, J. M., Roessler, J. G., Ferraro, C. C., DeFord, H. D., & Townsend, T. G. (2016). A review of waste products utilized as supplements to Portland cement in concrete. Journal of Cleaner Production, 121, 1-18. https://doi.org/10.1016/j.jclepro.2016.02.013 Pedrosa, I., Juarros-Basterretxea, J., Robles-Fernández, A., Basteiro, J., & García-Cueto, E. (2015). Pruebas de bondad de ajuste en distribuciones simétricas, ¿qué estadístico utilizar? Universitas Psychologica, 14(1), 245-254. https://doi.org/10.11144/Javeriana.upsy14-1.pbad Pereira, Y. A., Velasquez, S. R., Valencia, J. J., Ramírez, M. C., & Muñoz, A. P. (2017). Análisis comparativo de la concentración de óxidos presentes en el cemento portland y lodos de plantas de tratamiento de agua potable. Afinidad, 74(577). Recuperado de https://www.raco.cat/index.php/afinidad/article/view/320832 Perez, A. (2018). EVALUACIÓN DE LA INFLUENCIA DEL GRADO DE POLIMERIZACIÓN DEL POLICLORURO DE ALUMINIO COMO COAGULANTE PRIMARIO EN EL TRATAMIENTO DE AGUA. UNIVERSIDAD DE CARABOBO, Valencia. Puertas, F. (1993). Escorias de alto horno: composición y comportamiento hidráulico. Recuperado de https://digital.csic.es/handle/10261/55875 Raffino, M. E. (2018, noviembre 14). Estadística inferencial: Concepto, Usos y Ejemplos. Recuperado 15 de mayo de 2019, de https://concepto.de/estadistica-inferencial/ Rajasekar, A., Arunachalam, K., Kottaisamy, M., & Saraswathy, V. (2018). Durability characteristics of Ultra High Strength Concrete with treated sugarcane bagasse ash. Construction and Building Materials, 171, 350-356. https://doi.org/10.1016/j.conbuildmat.2018.03.140 Ramirez, G. (2003). Manejo de lodos producidos en la planta de tratamiento de agua potable, planta 2, del municipio de Cartago, Valle (Universidad nacional de Colombia). Recuperado de https://core.ac.uk/download/pdf/11051579.pdf Restrepo, J. C., Restrepo, O. J., & Tóbon, J. I. (2014). REDUCCIÓN DE CO2 EN LA INDUSTRIA CEMENTERA POR MEDIO DE PROCESOS DE SÍNTESIS QUÍMICA. Revista Colombiana de Materiales, 0(5), 54-60. Rojas, M. claudia, Garcia, M. E., Vargas, G., & Velilla, M. A. Infraccion ambiental - por descarga de lodos a cuerpos de agua superficial. , (Tribunal administrativo del atlantico 24 de noviembre de 2010). Sanjuan, M., Estevez, E., Argiz, C., & del Barrio, D. (2018). Effect of curing time on granulated blast-furnace slag cement mortars carbonation. Cement and Concrete Composites, 90, 257-265. https://doi.org/10.1016/j.cemconcomp.2018.04.006 SEINTBA S.C. (2010). MANIFESTACION DE IMPACTO AMBIENTAL RESIDUOS PELIGROSOS (p. 117). SERVICIO DE ECOLOGÍA INTEGRAL DEL BAJÍO S.A. DE C.V. Shuqiang, xu, Qinglin, M., & Julin, W. (2018). Combined effect of isobutyltriethoxysilane and silica fume on the performance of natural hydraulic lime-based mortars. Construction and Building Materials, 162, 181-191. https://doi.org/10.1016/j.conbuildmat.2017.09.150 Sollutia.com. (s. f.-a). Cenizas procedentes de la incineración de biomasa \| CEDEX. Recuperado 3 de abril de 2019, de http://www.cedexmateriales.es/catalogo-de-residuos/23/diciembre 2014/ Sollutia.com. (s. f.-b). Humo de sílice \| CEDEX. Recuperado 3 de abril de 2019, de http://www.cedexmateriales.es/catalogo-de-residuos/29/humo-de-silice/ Tobón, J. I., & Gómez, R. K. (2008). DESEMPEÑO DEL CEMENTO PÓRTLAND ADICIONADO CON CALIZAS DE DIFERENTES GRADOS DE PUREZA. DYNA, 75(156), 177-184. Torres, R., & Nicolas, J. (2018). Propuesta metodológica para tratamiento de lodos provenientes de plantas de potabilización en la sabana de Bogotá (estudio de caso Madrid, Cundinamarca). instname:Universidad Libre. Recuperado de http://repository.unilibre.edu.co/handle/10901/11289 Triple A S.A. E.S.P. (s. f.). Etapas de la potabilización del Agua. (http://www.aaa.com.co/acueducto/potabilizacion/). Vargas, J. W. P., Buzón, J. A., Vergara, D. A., & Molina, E. (2011). Reducción de los Residuos Sólidos Orgánicos en Colombia por medio del Compostaje Líquido. Ingeniare, (11), 374. https://doi.org/10.18041/1909-2458/ingeniare.11.643 Vigneshwari, M., Arunachalam, K., & Angayarkanni, A. (2018). Replacement of silica fume with thermally treated rice husk ash in Reactive Powder Concrete. Journal of Cleaner Production, 188, 264-277. https://doi.org/10.1016/j.jclepro.2018.04.008 Vouk, D., Serdar, M., Nakić, D., & Anić-Vučinić, A. (2016). Use of sludge generated at WWTP in the production of cement mortar and concrete. https://doi.org/10.14256/JCE.1374.2015 Walpole, R. E., Myers, R. H., & Myers, S. L. (2012). Probabilidad y estadistica para ingenieria y ciencias (Novena edicion). Mexico: PEARSON EDUCACION. Wons, W., Rzepa, K., Reben, M., Murzyn, P., Sitarz, M., & Olejniczak, Z. (2018). Effect of thermal processing on the structural characteristics of fly ashes. Journal of Molecular Structure, 1165, 299-304. https://doi.org/10.1016/j.molstruc.2018.04.008 Yue, Y., Wang, J., & Bai, Y. (2018). Tracing the status of silica fume in cementitious materials with Raman microscope. Construction and Building Materials, 159, 610-616. https://doi.org/10.1016/j.conbuildmat.2017.11.015 Zhen, C., & Chi, S. (2017). Comparative studies on the effects of sewage sludge ash and fly ash on cement hydration and properties of cement mortars. Construction and Building Materials, 154, 791-803. https://doi.org/10.1016/j.conbuildmat.2017.08.003 Zhen, C., Jiang, S. L., & Chi, S. (2018). Combined use of sewage sludge ash and recycled glass cullet for the production of concrete blocks. Journal of Cleaner Production, 171, 1447 1459. https://doi.org/10.1016/j.jclepro.2017.10.140PublicationORIGINAL1140892664 - 1124062154.pdf1140892664 - 1124062154.pdfapplication/pdf1791009https://repositorio.cuc.edu.co/bitstreams/16b38abd-6e86-4a9e-8fd7-1f4585d0d422/downloadfd6fb9fe22f36ba567d78ce7d79d33b5MD51CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-81031https://repositorio.cuc.edu.co/bitstreams/a3a2d6a3-0dc3-41f9-a1c7-4801d6826e62/download934f4ca17e109e0a05eaeaba504d7ce4MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-81748https://repositorio.cuc.edu.co/bitstreams/4706d78f-47de-414c-bb68-72591dc46940/download8a4605be74aa9ea9d79846c1fba20a33MD53THUMBNAIL1140892664 - 1124062154.pdf.jpg1140892664 - 1124062154.pdf.jpgimage/jpeg28420https://repositorio.cuc.edu.co/bitstreams/206a7975-3f20-463b-ac0b-17a3a403052a/downloadfc6825822da9160ff313a78c02d88cb3MD55TEXT1140892664 - 1124062154.pdf.txt1140892664 - 1124062154.pdf.txttext/plain115043https://repositorio.cuc.edu.co/bitstreams/51b067d2-6a7e-414e-a24a-e8e8b0ecd775/downloada828eb31e7e7a55382f2db995cfa0227MD5611323/4724oai:repositorio.cuc.edu.co:11323/47242024-09-17 10:44:40.616http://creativecommons.org/licenses/by-nc-sa/4.0/Attribution-NonCommercial-ShareAlike 4.0 Internationalopen.accesshttps://repositorio.cuc.edu.coRepositorio de la Universidad de la Costa CUCrepdigital@cuc.edu.coTk9URTogUExBQ0UgWU9VUiBPV04gTElDRU5TRSBIRVJFClRoaXMgc2FtcGxlIGxpY2Vuc2UgaXMgcHJvdmlkZWQgZm9yIGluZm9ybWF0aW9uYWwgcHVycG9zZXMgb25seS4KCk5PTi1FWENMVVNJVkUgRElTVFJJQlVUSU9OIExJQ0VOU0UKCkJ5IHNpZ25pbmcgYW5kIHN1Ym1pdHRpbmcgdGhpcyBsaWNlbnNlLCB5b3UgKHRoZSBhdXRob3Iocykgb3IgY29weXJpZ2h0Cm93bmVyKSBncmFudHMgdG8gRFNwYWNlIFVuaXZlcnNpdHkgKERTVSkgdGhlIG5vbi1leGNsdXNpdmUgcmlnaHQgdG8gcmVwcm9kdWNlLAp0cmFuc2xhdGUgKGFzIGRlZmluZWQgYmVsb3cpLCBhbmQvb3IgZGlzdHJpYnV0ZSB5b3VyIHN1Ym1pc3Npb24gKGluY2x1ZGluZwp0aGUgYWJzdHJhY3QpIHdvcmxkd2lkZSBpbiBwcmludCBhbmQgZWxlY3Ryb25pYyBmb3JtYXQgYW5kIGluIGFueSBtZWRpdW0sCmluY2x1ZGluZyBidXQgbm90IGxpbWl0ZWQgdG8gYXVkaW8gb3IgdmlkZW8uCgpZb3UgYWdyZWUgdGhhdCBEU1UgbWF5LCB3aXRob3V0IGNoYW5naW5nIHRoZSBjb250ZW50LCB0cmFuc2xhdGUgdGhlCnN1Ym1pc3Npb24gdG8gYW55IG1lZGl1bSBvciBmb3JtYXQgZm9yIHRoZSBwdXJwb3NlIG9mIHByZXNlcnZhdGlvbi4KCllvdSBhbHNvIGFncmVlIHRoYXQgRFNVIG1heSBrZWVwIG1vcmUgdGhhbiBvbmUgY29weSBvZiB0aGlzIHN1Ym1pc3Npb24gZm9yCnB1cnBvc2VzIG9mIHNlY3VyaXR5LCBiYWNrLXVwIGFuZCBwcmVzZXJ2YXRpb24uCgpZb3UgcmVwcmVzZW50IHRoYXQgdGhlIHN1Ym1pc3Npb24gaXMgeW91ciBvcmlnaW5hbCB3b3JrLCBhbmQgdGhhdCB5b3UgaGF2ZQp0aGUgcmlnaHQgdG8gZ3JhbnQgdGhlIHJpZ2h0cyBjb250YWluZWQgaW4gdGhpcyBsaWNlbnNlLiBZb3UgYWxzbyByZXByZXNlbnQKdGhhdCB5b3VyIHN1Ym1pc3Npb24gZG9lcyBub3QsIHRvIHRoZSBiZXN0IG9mIHlvdXIga25vd2xlZGdlLCBpbmZyaW5nZSB1cG9uCmFueW9uZSdzIGNvcHlyaWdodC4KCklmIHRoZSBzdWJtaXNzaW9uIGNvbnRhaW5zIG1hdGVyaWFsIGZvciB3aGljaCB5b3UgZG8gbm90IGhvbGQgY29weXJpZ2h0LAp5b3UgcmVwcmVzZW50IHRoYXQgeW91IGhhdmUgb2J0YWluZWQgdGhlIHVucmVzdHJpY3RlZCBwZXJtaXNzaW9uIG9mIHRoZQpjb3B5cmlnaHQgb3duZXIgdG8gZ3JhbnQgRFNVIHRoZSByaWdodHMgcmVxdWlyZWQgYnkgdGhpcyBsaWNlbnNlLCBhbmQgdGhhdApzdWNoIHRoaXJkLXBhcnR5IG93bmVkIG1hdGVyaWFsIGlzIGNsZWFybHkgaWRlbnRpZmllZCBhbmQgYWNrbm93bGVkZ2VkCndpdGhpbiB0aGUgdGV4dCBvciBjb250ZW50IG9mIHRoZSBzdWJtaXNzaW9uLgoKSUYgVEhFIFNVQk1JU1NJT04gSVMgQkFTRUQgVVBPTiBXT1JLIFRIQVQgSEFTIEJFRU4gU1BPTlNPUkVEIE9SIFNVUFBPUlRFRApCWSBBTiBBR0VOQ1kgT1IgT1JHQU5JWkFUSU9OIE9USEVSIFRIQU4gRFNVLCBZT1UgUkVQUkVTRU5UIFRIQVQgWU9VIEhBVkUKRlVMRklMTEVEIEFOWSBSSUdIVCBPRiBSRVZJRVcgT1IgT1RIRVIgT0JMSUdBVElPTlMgUkVRVUlSRUQgQlkgU1VDSApDT05UUkFDVCBPUiBBR1JFRU1FTlQuCgpEU1Ugd2lsbCBjbGVhcmx5IGlkZW50aWZ5IHlvdXIgbmFtZShzKSBhcyB0aGUgYXV0aG9yKHMpIG9yIG93bmVyKHMpIG9mIHRoZQpzdWJtaXNzaW9uLCBhbmQgd2lsbCBub3QgbWFrZSBhbnkgYWx0ZXJhdGlvbiwgb3RoZXIgdGhhbiBhcyBhbGxvd2VkIGJ5IHRoaXMKbGljZW5zZSwgdG8geW91ciBzdWJtaXNzaW9uLgo=

Análisis estadístico comparativo del contenido de óxidos presentes en lodos sin calcinar, lodos calcinados y cemento portland

Publicaciones similares