Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa

This project focuses on developing a new material with thin film technology and with the characteristics of being a ternary compound, with a calcostibite phase and an orthorhombic crystalline structure, such as the CuSbS2 compound, since it has the necessary qualities to function as an active layer....

Full description

Autores:
Tipo de recurso:
Fecha de publicación:
2020
Institución:
Universidad de América
Repositorio:
Lumieres
Idioma:
spa
OAI Identifier:
oai:repository.uamerica.edu.co:20.500.11839/8109
Acceso en línea:
https://hdl.handle.net/20.500.11839/8109
Palabra clave:
Agente complejante
Calcostibita
Electrodeposición simultánea
Película delgada
Complexing agent
Calcostibita
Simultaneous electrodeposition
Thin film
Tesis y disertaciones académicas
Rights
License
Atribución – No comercial
id Lumieres_a30ae35b62b111935de9d255a31030a3
oai_identifier_str oai:repository.uamerica.edu.co:20.500.11839/8109
network_acronym_str Lumieres
network_name_str Lumieres
repository_id_str
dc.title.none.fl_str_mv Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
Synthesis of thin films of the ternary compound CuSbS2 deposited by the electrodeposition technique for use as an active layer
title Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
spellingShingle Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
Agente complejante
Calcostibita
Electrodeposición simultánea
Película delgada
Complexing agent
Calcostibita
Simultaneous electrodeposition
Thin film
Tesis y disertaciones académicas
title_short Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
title_full Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
title_fullStr Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
title_full_unstemmed Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
title_sort Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa
dc.subject.none.fl_str_mv Agente complejante
Calcostibita
Electrodeposición simultánea
Película delgada
Complexing agent
Calcostibita
Simultaneous electrodeposition
Thin film
Tesis y disertaciones académicas
topic Agente complejante
Calcostibita
Electrodeposición simultánea
Película delgada
Complexing agent
Calcostibita
Simultaneous electrodeposition
Thin film
Tesis y disertaciones académicas
description This project focuses on developing a new material with thin film technology and with the characteristics of being a ternary compound, with a calcostibite phase and an orthorhombic crystalline structure, such as the CuSbS2 compound, since it has the necessary qualities to function as an active layer. of a solar cell. For the development of this compound, first a preliminary study of the electrodeposition technique of the Antimony and Copper elements was carried out on each Molybdenum substrates and after having the key parameters, the due simultaneous electrodeposition was carried out, which consists of depositing the antimony and Copper on Molybdenum substrates at the same time. For deposition using this method, parameters such as voltage, temperature of the electrolyte solution, concentration of Antimony and Copper salts, current pulses (PDC), the use of a complexing agent and the deposition time were evaluated. simultaneous.
publishDate 2020
dc.date.none.fl_str_mv 2020-08-18
2021-01-25T23:40:11Z
2021-01-25T23:40:11Z
dc.type.none.fl_str_mv bachelorThesis
dc.type.coar.fl_str_mv http://purl.org/coar/resource_type/c_7a1f
dc.identifier.none.fl_str_mv APA 7th - Celis Páez, M. T. (2020) Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8109
https://hdl.handle.net/20.500.11839/8109
identifier_str_mv APA 7th - Celis Páez, M. T. (2020) Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8109
url https://hdl.handle.net/20.500.11839/8109
dc.language.iso.fl_str_mv spa
language spa
dc.rights.none.fl_str_mv Atribución – No comercial
http://purl.org/coar/access_right/c_abf2
rights_invalid_str_mv Atribución – No comercial
http://purl.org/coar/access_right/c_abf2
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Fundación Universidad de América
publisher.none.fl_str_mv Fundación Universidad de América
institution Universidad de América
repository.name.fl_str_mv
repository.mail.fl_str_mv
_version_ 1841553086305271808
spelling Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activaSynthesis of thin films of the ternary compound CuSbS2 deposited by the electrodeposition technique for use as an active layerAgente complejanteCalcostibitaElectrodeposición simultáneaPelícula delgadaComplexing agentCalcostibitaSimultaneous electrodepositionThin filmTesis y disertaciones académicasThis project focuses on developing a new material with thin film technology and with the characteristics of being a ternary compound, with a calcostibite phase and an orthorhombic crystalline structure, such as the CuSbS2 compound, since it has the necessary qualities to function as an active layer. of a solar cell. For the development of this compound, first a preliminary study of the electrodeposition technique of the Antimony and Copper elements was carried out on each Molybdenum substrates and after having the key parameters, the due simultaneous electrodeposition was carried out, which consists of depositing the antimony and Copper on Molybdenum substrates at the same time. For deposition using this method, parameters such as voltage, temperature of the electrolyte solution, concentration of Antimony and Copper salts, current pulses (PDC), the use of a complexing agent and the deposition time were evaluated. simultaneous.Este proyecto se enfoca en desarrollar un nuevo material con tecnología de película delgada y con las características de ser un compuesto ternario, con fase calcostibita y estructura cristalina ortorrómbica, como lo es el compuesto CuSbS2 ya que este presenta las cualidades necesarias para funcionar como capa activa de una celda solar. Para el desarrollo de este compuesto primero se realizó un estudio preliminar de la técnica de electrodeposición de los elementos Antimonio y Cobre sobre sustratos de Molibdeno cada uno y luego de tener los parámetros claves se realizó la debida electrodeposición simultánea, la cual consiste en depositar el antimonio y Cobre sobre los sustratos de Molibdeno al mismo tiempo. Para la deposición mediante este método se evaluaron parámetros como lo son el voltaje, la temperatura de la solución- electrolito, concentración de las sales de Antimonio y Cobre, pulsos de corriente (PDC), el uso de un agente complejante y el tiempo de deposición simultánea.Fundación Universidad de América2021-01-25T23:40:11Z2021-01-25T23:40:11Z2020-08-18bachelorThesishttp://purl.org/coar/resource_type/c_7a1fapplication/pdfapplication/pdfAPA 7th - Celis Páez, M. T. (2020) Síntesis de películas delgadas del compuesto ternario CuSbS2 depositadas por la técnica de electrodeposición para su uso como capa activa. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8109https://hdl.handle.net/20.500.11839/8109Atribución – No comercialYo (nosotros) en calidad de titular(es) de la obra, autorizo (autorizamos) al Sistema de Bibliotecas de la Fundación Universidad América para que incluya una copia, indexe y divulgue en el Repositorio Digital Institucional – Lumieres, la obra mencionada con el fin de facilitar los procesos de visibilidad e impacto de la misma, conforme a los derechos patrimoniales que me(nos) corresponde(n) y que incluyen: la reproducción, comunicación pública, distribución al público, transformación, en conformidad con la normatividad vigente sobre derechos de autor y derechos conexos (Ley 23 de 1982, Ley 44 de 1993, Decisión Andina 351 de 1993, entre otras). Al respecto como Autor(es) manifestamos conocer que: - La autorización es de carácter no exclusiva y limitada, esto implica que la licencia tiene una vigencia, que no es perpetua y que el autor puede publicar o difundir su obra en cualquier otro medio, así como llevar a cabo cualquier tipo de acción sobre el documento. - La autorización tendrá una vigencia de cinco años a partir del momento de la inclusión de la obra en el repositorio, prorrogable indefinidamente por el tiempo de duración de los derechos patrimoniales del autor y podrá darse por terminada una vez el autor lo manifieste por escrito a la institución, con la salvedad de que la obra es difundida globalmente y cosechada por diferentes buscadores y/o repositorios en Internet, lo que no garantiza que la obra pueda ser retirada de manera inmediata de otros sistemas de información en los que se haya indexado, diferentes al Repositorio Digital Institucional – Lumieres de la Fundación Universidad América. - La autorización de publicación comprende el formato original de la obra y todos los demás que se requiera, para su publicación en el repositorio. Igualmente, la autorización permite a la institución el cambio de soporte de la obra con fines de preservación (impreso, electrónico, digital, Internet, intranet, o cualquier otro formato conocido o por conocer). - La autorización es gratuita y se renuncia a recibir cualquier remuneración por los usos de la obra, de acuerdo con la licencia establecida en esta autorización. - Al firmar esta autorización, se manifiesta que la obra es original y no existe en ella ninguna violación a los derechos de autor de terceros. En caso de que el trabajo haya sido financiado por terceros, el o los autores asumen la responsabilidad del cumplimiento de los acuerdos establecidos sobre los derechos patrimoniales de la obra. - Frente a cualquier reclamación por terceros, el o los autores serán los responsables. En ningún caso la responsabilidad será asumida por la Fundación Universidad de América. - Con la autorización, la Universidad puede difundir la obra en índices, buscadores y otros sistemas de información que favorezcan su visibilidad.http://purl.org/coar/access_right/c_abf2spaCelis Páez, Mónica Tatianaoai:repository.uamerica.edu.co:20.500.11839/81092025-02-01T08:46:21Z

Publicaciones similares