Uso de material cerámico como material para curado interno en mezclas de concreto
This study aimed to assess the performance of concrete to variations in the percentages of coarse aggregate and ceramic material for internal curing by assessing the mechanical properties and durability of the mixtures made with this material. The ceramic material used in the different mixture trial...
- Autores:
-
Aldana Barcinilla, Eder Samir
- Tipo de recurso:
- Fecha de publicación:
- 2014
- Institución:
- Escuela Colombiana de Ingeniería Julio Garavito
- Repositorio:
- Repositorio Institucional ECI
- Idioma:
- spa
- OAI Identifier:
- oai:repositorio.escuelaing.edu.co:001/194
- Acceso en línea:
- http://catalogo.escuelaing.edu.co/cgi-bin/koha/opac-detail.pl?biblionumber=17482
https://repositorio.escuelaing.edu.co/handle/001/194
- Palabra clave:
- Material cerámico
Resistencia a la compresión
Propiedades mecánicas
Durabilidad
Permeabilidad al ion cloruro
Curado interno
Ceramic material
Mechanical properties
Compressive strength
Chloride ion permeability
Durability
Internal curing
- Rights
- openAccess
- License
- Derechos Reservados - Escuela Colombiana de Ingeniería Julio Garavito
| id |
ESCUELAIG2_f1c5e90d85e5254ddf458cb7e1ab5ee8 |
|---|---|
| oai_identifier_str |
oai:repositorio.escuelaing.edu.co:001/194 |
| network_acronym_str |
ESCUELAIG2 |
| network_name_str |
Repositorio Institucional ECI |
| repository_id_str |
|
| dc.title.spa.fl_str_mv |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| title |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| spellingShingle |
Uso de material cerámico como material para curado interno en mezclas de concreto Material cerámico Resistencia a la compresión Propiedades mecánicas Durabilidad Permeabilidad al ion cloruro Curado interno Ceramic material Mechanical properties Compressive strength Chloride ion permeability Durability Internal curing |
| title_short |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| title_full |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| title_fullStr |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| title_full_unstemmed |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| title_sort |
Uso de material cerámico como material para curado interno en mezclas de concreto |
| dc.creator.fl_str_mv |
Aldana Barcinilla, Eder Samir |
| dc.contributor.advisor.spa.fl_str_mv |
Torres Castellanos, Nancy, (dir) |
| dc.contributor.author.spa.fl_str_mv |
Aldana Barcinilla, Eder Samir |
| dc.subject.spa.fl_str_mv |
Material cerámico Resistencia a la compresión Propiedades mecánicas Durabilidad Permeabilidad al ion cloruro Curado interno |
| topic |
Material cerámico Resistencia a la compresión Propiedades mecánicas Durabilidad Permeabilidad al ion cloruro Curado interno Ceramic material Mechanical properties Compressive strength Chloride ion permeability Durability Internal curing |
| dc.subject.keywords.spa.fl_str_mv |
Ceramic material Mechanical properties Compressive strength Chloride ion permeability Durability Internal curing |
| description |
This study aimed to assess the performance of concrete to variations in the percentages of coarse aggregate and ceramic material for internal curing by assessing the mechanical properties and durability of the mixtures made with this material. The ceramic material used in the different mixture trials was produced from crushing structural bricks, commonly used in residential construction in the city of Bogota Colombia. Concrete mixtures were evaluated with three different percentages of ceramic material (0%, 20%, and 40%) used in substitution of coarse aggregate and two values of water / cement ratio (0.30 and 0.50). The resistance to compression, elasticity modulus, absorption, permeability, shrinkage, chloride ion permeability and sorptivity were evaluated. Test results showed that as the replacement percentage of ceramic material, for samples with water / cement ratio of 0.30, increases the results of the resistance to compression are higher than the results for the control sample; while for the water / cement ratio of 0.50 resistances lower than those of a concrete with 100% natural aggregate compression were obtained. The modulus of elasticity for all concrete with ceramic replacement were always lower than those obtained for the concrete made with 100% coarse aggregate. Similarly, the properties of durability, measured by permeability tests, absorption, sorptivity and chloride ion permeability, are affected by the increased percentage of ceramic replacement and water / cement ratio. Internal curing is beneficial only to increase the resistance to compression in concrete of low water / cement to reduce drying shrinkage. |
| publishDate |
2014 |
| dc.date.issued.spa.fl_str_mv |
2014 |
| dc.date.accessioned.spa.fl_str_mv |
2015-03-04T19:54:45Z |
| dc.date.available.spa.fl_str_mv |
2015-03-04T19:54:45Z |
| dc.date.accessioned.none.fl_str_mv |
2021-10-01T15:33:42Z |
| dc.date.available.none.fl_str_mv |
2021-10-01T15:33:42Z |
| dc.type.spa.fl_str_mv |
Trabajo de grado - Maestría |
| dc.type.coarversion.fl_str_mv |
http://purl.org/coar/version/c_970fb48d4fbd8a85 |
| dc.type.version.spa.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
| dc.type.content.spa.fl_str_mv |
Text |
| dc.type.driver.spa.fl_str_mv |
info:eu-repo/semantics/masterThesis |
| dc.type.redcol.spa.fl_str_mv |
http://purl.org/redcol/resource_type/TM |
| status_str |
publishedVersion |
| dc.identifier.uri.spa.fl_str_mv |
http://catalogo.escuelaing.edu.co/cgi-bin/koha/opac-detail.pl?biblionumber=17482 |
| dc.identifier.uri.none.fl_str_mv |
https://repositorio.escuelaing.edu.co/handle/001/194 |
| url |
http://catalogo.escuelaing.edu.co/cgi-bin/koha/opac-detail.pl?biblionumber=17482 https://repositorio.escuelaing.edu.co/handle/001/194 |
| dc.language.iso.spa.fl_str_mv |
spa |
| language |
spa |
| dc.rights.spa.fl_str_mv |
Derechos Reservados - Escuela Colombiana de Ingeniería Julio Garavito |
| dc.rights.coar.fl_str_mv |
http://purl.org/coar/access_right/c_abf2 |
| dc.rights.uri.spa.fl_str_mv |
https://creativecommons.org/licenses/by-nc/4.0/ |
| dc.rights.accessrights.spa.fl_str_mv |
info:eu-repo/semantics/openAccess |
| dc.rights.creativecommons.spa.fl_str_mv |
Atribución-NoComercial 4.0 Internacional (CC BY-NC 4.0) |
| rights_invalid_str_mv |
Derechos Reservados - Escuela Colombiana de Ingeniería Julio Garavito https://creativecommons.org/licenses/by-nc/4.0/ Atribución-NoComercial 4.0 Internacional (CC BY-NC 4.0) http://purl.org/coar/access_right/c_abf2 |
| eu_rights_str_mv |
openAccess |
| dc.format.mimetype.spa.fl_str_mv |
application/pdf |
| dc.publisher.spa.fl_str_mv |
Escuela Colombiana de Ingeniería Julio Garavito |
| dc.publisher.program.spa.fl_str_mv |
Maestría en Ingeniería Civil |
| institution |
Escuela Colombiana de Ingeniería Julio Garavito |
| bitstream.url.fl_str_mv |
https://repositorio.escuelaing.edu.co/bitstream/001/194/1/Aldana%20Barcinilla%2c%20Eder%20Samir%20-%202014.pdf https://repositorio.escuelaing.edu.co/bitstream/001/194/2/Art%c3%adculo.pdf https://repositorio.escuelaing.edu.co/bitstream/001/194/3/Anexos.rar https://repositorio.escuelaing.edu.co/bitstream/001/194/4/license.txt https://repositorio.escuelaing.edu.co/bitstream/001/194/5/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593.pdf.txt https://repositorio.escuelaing.edu.co/bitstream/001/194/6/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593-Articulo.pdf.txt https://repositorio.escuelaing.edu.co/bitstream/001/194/13/Aldana%20Barcinilla%2c%20Eder%20Samir%20-%202014.pdf.txt https://repositorio.escuelaing.edu.co/bitstream/001/194/15/Art%c3%adculo.pdf.txt https://repositorio.escuelaing.edu.co/bitstream/001/194/9/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593.pdf.jpg https://repositorio.escuelaing.edu.co/bitstream/001/194/10/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593-Articulo.pdf.jpg https://repositorio.escuelaing.edu.co/bitstream/001/194/14/Aldana%20Barcinilla%2c%20Eder%20Samir%20-%202014.pdf.jpg https://repositorio.escuelaing.edu.co/bitstream/001/194/16/Art%c3%adculo.pdf.jpg |
| bitstream.checksum.fl_str_mv |
837ddfadfc3aa0f60c14073a6f93b103 6f39f3878dda7fc17a5c0ffa07d043a2 fd450d2e56ae88ae6cdced8f398fe197 9480849945fd70c1da11fa639db5a11c 1fedda4c0b6e3ecd595a9340ed31c7fc 84654feb2e5c18e0ea93382f438ef139 5c4cd4e2f32aacc8d035149acb127048 643cf1fa2a4f8e08f3e7fda916db3cb4 b70636db279287aec213ca765941a25e 1b7d8433d781651a6040ac45dd62838a 6981c2355f01efa60d3a0ec2767f34a9 f4b90204c2c31910ae0adeb078f63f6e |
| bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 MD5 MD5 MD5 MD5 MD5 MD5 |
| repository.name.fl_str_mv |
Repositorio Escuela Colombiana de Ingeniería Julio Garavito |
| repository.mail.fl_str_mv |
repositorio.eci@escuelaing.edu.co |
| _version_ |
1814355620631937024 |
| spelling |
Torres Castellanos, Nancy, (dir)2b475ecd9ea004cd3b18c2eaf60c01d1Aldana Barcinilla, Eder Samir62071b32ede5a21ebd2d7116bfbca94a6002015-03-04T19:54:45Z2021-10-01T15:33:42Z2015-03-04T19:54:45Z2021-10-01T15:33:42Z2014http://catalogo.escuelaing.edu.co/cgi-bin/koha/opac-detail.pl?biblionumber=17482https://repositorio.escuelaing.edu.co/handle/001/194This study aimed to assess the performance of concrete to variations in the percentages of coarse aggregate and ceramic material for internal curing by assessing the mechanical properties and durability of the mixtures made with this material. The ceramic material used in the different mixture trials was produced from crushing structural bricks, commonly used in residential construction in the city of Bogota Colombia. Concrete mixtures were evaluated with three different percentages of ceramic material (0%, 20%, and 40%) used in substitution of coarse aggregate and two values of water / cement ratio (0.30 and 0.50). The resistance to compression, elasticity modulus, absorption, permeability, shrinkage, chloride ion permeability and sorptivity were evaluated. Test results showed that as the replacement percentage of ceramic material, for samples with water / cement ratio of 0.30, increases the results of the resistance to compression are higher than the results for the control sample; while for the water / cement ratio of 0.50 resistances lower than those of a concrete with 100% natural aggregate compression were obtained. The modulus of elasticity for all concrete with ceramic replacement were always lower than those obtained for the concrete made with 100% coarse aggregate. Similarly, the properties of durability, measured by permeability tests, absorption, sorptivity and chloride ion permeability, are affected by the increased percentage of ceramic replacement and water / cement ratio. Internal curing is beneficial only to increase the resistance to compression in concrete of low water / cement to reduce drying shrinkage.El presente trabajo de grado tuvo como finalidad evaluar el comportamiento de un concreto al cual se le hizo reemplazo, en ciertos porcentajes, del agregado grueso por material cerámico para obtener curado interno; dicho comportamiento se evaluó mediante la valoración de algunas de las propiedades mecánicas y de durabilidad de las mezclas hechas con este material. El material cerámico usado en las diferentes mezclas de los ensayos fue producido a partir de la trituración de ladrillo tolete estructural, comúnmente usado en la construcción de viviendas en la ciudad de Bogotá. Se evaluó una mezcla de concreto con tres porcentajes diferentes de reemplazo de agregado grueso por material cerámico (0%, 20% y 40%) y dos valores de relación agua/cemento (0.30 y 0.50). Dentro de las propiedades analizadas están la resistencia a la compresión, módulo de elasticidad, absorción, permeabilidad, contracción, permeabilidad al ion cloruro y sortividad. Los resultados de los ensayos mostraron claramente que en la media que se aumenta el porcentaje de reemplazo de material cerámico, para muestras con relación a/c de 0.30, los resultados de la resistencia a la compresión son más altos que para los concretos de la muestra patrón, mientras que para la relación a/c de 0.50, se obtuvieron resistencias a la compresión inferiores a las de un concreto con el 100% del agregado natural. Los módulos de elasticidad para todos los concretos con reemplazo de material cerámico siempre fueron menores a los concretos con el 100% del agregado grueso. Paralelamente, las propiedades de durabilidad, medidas a través de ensayos de permeabilidad, absorción, sortividad y permeabilidad al ion cloruro, se ven afectadas con el aumento del porcentaje de reemplazo de material cerámico y la relación agua/cemento. El curado interno resulta benéfico solamente para aumentar la resistencia a la compresión en concretos de baja relación a/c y para reducir la contracción por secado.MaestríaMagíster en Ingeniería Civilapplication/pdfspaEscuela Colombiana de Ingeniería Julio GaravitoMaestría en Ingeniería CivilDerechos Reservados - Escuela Colombiana de Ingeniería Julio Garavitohttps://creativecommons.org/licenses/by-nc/4.0/info:eu-repo/semantics/openAccessAtribución-NoComercial 4.0 Internacional (CC BY-NC 4.0)http://purl.org/coar/access_right/c_abf2Material cerámicoResistencia a la compresiónPropiedades mecánicasDurabilidadPermeabilidad al ion cloruroCurado internoCeramic materialMechanical propertiesCompressive strengthChloride ion permeabilityDurabilityInternal curingUso de material cerámico como material para curado interno en mezclas de concretoTrabajo de grado - Maestríainfo:eu-repo/semantics/publishedVersionTextinfo:eu-repo/semantics/masterThesishttp://purl.org/redcol/resource_type/TMhttp://purl.org/coar/version/c_970fb48d4fbd8a85ORIGINALAldana Barcinilla, Eder Samir - 2014.pdfPDFapplication/pdf6310796https://repositorio.escuelaing.edu.co/bitstream/001/194/1/Aldana%20Barcinilla%2c%20Eder%20Samir%20-%202014.pdf837ddfadfc3aa0f60c14073a6f93b103MD51open accessArtículo.pdfArticuloapplication/pdf528797https://repositorio.escuelaing.edu.co/bitstream/001/194/2/Art%c3%adculo.pdf6f39f3878dda7fc17a5c0ffa07d043a2MD52open accessAnexos.rarAnexosapplication/octet-stream3083822https://repositorio.escuelaing.edu.co/bitstream/001/194/3/Anexos.rarfd450d2e56ae88ae6cdced8f398fe197MD53open accessLICENSElicense.txttext/plain1762https://repositorio.escuelaing.edu.co/bitstream/001/194/4/license.txt9480849945fd70c1da11fa639db5a11cMD54open accessTEXTCF-Maestria Ingeniería Civil-1102805593.pdf.txtExtracted texttext/plain184407https://repositorio.escuelaing.edu.co/bitstream/001/194/5/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593.pdf.txt1fedda4c0b6e3ecd595a9340ed31c7fcMD55open accessCF-Maestria Ingeniería Civil-1102805593-Articulo.pdf.txtExtracted texttext/plain33045https://repositorio.escuelaing.edu.co/bitstream/001/194/6/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593-Articulo.pdf.txt84654feb2e5c18e0ea93382f438ef139MD56open accessAldana Barcinilla, Eder Samir - 2014.pdf.txtAldana Barcinilla, Eder Samir - 2014.pdf.txtExtracted texttext/plain180969https://repositorio.escuelaing.edu.co/bitstream/001/194/13/Aldana%20Barcinilla%2c%20Eder%20Samir%20-%202014.pdf.txt5c4cd4e2f32aacc8d035149acb127048MD513open accessArtículo.pdf.txtArtículo.pdf.txtExtracted texttext/plain32935https://repositorio.escuelaing.edu.co/bitstream/001/194/15/Art%c3%adculo.pdf.txt643cf1fa2a4f8e08f3e7fda916db3cb4MD515open accessTHUMBNAILCF-Maestria Ingeniería Civil-1102805593.pdf.jpgIM Thumbnailimage/jpeg3644https://repositorio.escuelaing.edu.co/bitstream/001/194/9/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593.pdf.jpgb70636db279287aec213ca765941a25eMD59open accessCF-Maestria Ingeniería Civil-1102805593-Articulo.pdf.jpgIM Thumbnailimage/jpeg4315https://repositorio.escuelaing.edu.co/bitstream/001/194/10/CF-Maestria%20Ingenier%c3%ada%20Civil-1102805593-Articulo.pdf.jpg1b7d8433d781651a6040ac45dd62838aMD510open accessAldana Barcinilla, Eder Samir - 2014.pdf.jpgAldana Barcinilla, Eder Samir - 2014.pdf.jpgGenerated Thumbnailimage/jpeg6984https://repositorio.escuelaing.edu.co/bitstream/001/194/14/Aldana%20Barcinilla%2c%20Eder%20Samir%20-%202014.pdf.jpg6981c2355f01efa60d3a0ec2767f34a9MD514open accessArtículo.pdf.jpgArtículo.pdf.jpgGenerated Thumbnailimage/jpeg15854https://repositorio.escuelaing.edu.co/bitstream/001/194/16/Art%c3%adculo.pdf.jpgf4b90204c2c31910ae0adeb078f63f6eMD516open access001/194oai:repositorio.escuelaing.edu.co:001/1942021-10-01 17:13:22.887open accessRepositorio Escuela Colombiana de Ingeniería Julio Garavitorepositorio.eci@escuelaing.edu.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 |