Assessment of Streptococcus Mutans Adhesion to the Surface of Biomimetically-Modified Orthodontic Archwires
Bacterial adhesion and biofilm formation on the surfaces of dental and orthodontic biomaterials is primary responsible for oral diseases and biomaterial deterioration. A number of alternatives to reduce bacterial adhesion to biomaterials, including surface modification using a variety of techniques,...
- Autores:
-
Arango Santander, Santiago
González Vélez, Carolina
Aguilar Villada, Anizac Andrea
Cano Melguizo, Alejandro
Castro Florez, Sergio
Sánchez Garzón, Juliana del Pilar
Franco Aguirre, John Querubín
- Tipo de recurso:
- Article of journal
- Fecha de publicación:
- 2020
- Institución:
- Universidad Cooperativa de Colombia
- Repositorio:
- Repositorio UCC
- Idioma:
- OAI Identifier:
- oai:repository.ucc.edu.co:20.500.12494/17067
- Acceso en línea:
- https://hdl.handle.net/20.500.12494/17067
- Palabra clave:
- Adhesión bacteriana
Litografía blanda
Biomimética
Modificación superficial
TG 2020 EOF
Bacterial adhesion
Soft lithography
Biomimetics
Surface modification
- Rights
- openAccess
- License
- Atribución
| Summary: | Bacterial adhesion and biofilm formation on the surfaces of dental and orthodontic biomaterials is primary responsible for oral diseases and biomaterial deterioration. A number of alternatives to reduce bacterial adhesion to biomaterials, including surface modification using a variety of techniques, has been proposed. Even though surface modification has demonstrated a reduction in bacterial adhesion, information on surface modification and biomimetics to reduce bacterial adhesion to a surface is scarce. Therefore, the main objective of this work was to assess bacterial adhesion to orthodontic archwires that were modified following a biomimetic approach. The sample consisted of 0.017 × 0.025, 10 mm-long 316L stainless steel and NiTi orthodontic archwire fragments. For soft lithography, a polydimethylsiloxane (PDMS) stamp was obtained after duplicating the surface of Colocasia esculenta (L) Schott leaves. Topography transfer to the archwires was performed using silica sol. Surface hydrophobicity was assessed by contact angle and surface roughness by atomic force microscopy. Bacterial adhesion was evaluated using Streptococcus mutans. The topography of the Colocasia esculenta (L) Schott leaf was successfully transferred to the surface of the archwires. Contact angle and roughness between modified and unmodified archwire surfaces was statistically significant. A statistically significant reduction in Streptococcus mutans adhesion to modified archwires was also observed. |
|---|